3D Printing Info

Filament comparison

LW-PLA vs Breakaway

Compare printing settings, strength, heat resistance, dated prices and sources.

Lightweight / foaming PLA (LW-PLA) guideBreak-away support guide

2 selected · all documented properties

Open these two in the interactive comparisonMore LW-PLA comparisonsMore Breakaway comparisons
LW-PLA vs Breakaway — documented properties and sources
PropertyLightweight / foaming PLA (LW-PLA)PLABreak-away supportSUPPORT
Market snapshot
Listing priceUSD/kg; dated snapshots$47.48/kg median; $37.49–$50.00/kg across 4 dated product listings$42.49/kg median; $26.00–$79.98/kg across 4 dated product listings
Identity & Market
Base polymer / chemistryPLA with a blowing agent. Two distinct types: active-foaming grades that expand at the nozzle (Bambu Lab PLA Aero, colorFabb LW-PLA) and pre-foamed grades that do not (Polymaker PolyLite LW-PLA, PolyWood)[1][2][3][4]Break-away support compounds matched to a specific model material — Polymaker sells separate grades for PLA and for PA12[5][6]
Densityg/cm³Filament 1.21 (Bambu Lab) and 1.24 (colorFabb); pre-foamed filament 0.8 (PolyWood, at 21.5 °C) and 0.9 (Polymaker LW-PLA); foamed prints reach 0.40[1][2][3][4]1.22 (PolySupport for PLA) and 1.29 (PolySupport for PA12), ISO 1183[5][6]
Typical priceUSD/kg1 kg-equivalent spools cluster near 45[7][2][8]1 kg-equivalent spools span 26–80; the middle of the market is about 45[8][9][10]
Price range across brandsUSD/kg37–50 across brands; Polymaker LW-PLA 37, Bambu Lab Aero 45, colorFabb 50, PolyWood 50[8][7][2]26–80 across brands and grades; IEMAI 3D E-REMOVE 26, Polymaker PolySupport for PLA 40 at 750 g, YXPOLYER 45, PolySupport for PA12 80 at 500 g[8][9][10]
Market availability1–5Available from several mainstream brands[7][8][2]Available from several mainstream brands[8][11]
Spool sizes & diameters1.75 and 2.85 mm; 0.6, 0.75, 0.8 and 1 kg spools[8][2]1.75 and 2.85 mm; 0.5 and 0.75 kg spools[8]
Typical applicationsRC aircraft, drone airframes and large props where mass matters more than strength[1][2]Support that peels off by hand, avoiding the moisture handling and dissolution time that soluble supports demand[5]
Printing Parameters
Nozzle temperature°C210–260 (Bambu Lab, foaming); 195–260 (colorFabb, foaming); 190–210 (Polymaker, pre-foamed)[1][2][3]220–230 (PolySupport for PLA)[5]
Bed temperature°C35–45 (Bambu Lab); 50–60 (colorFabb); 25–60 (Polymaker)[1][2][3]25–60 (PolySupport for PLA)[5]
Enclosure / chamber requirement1–5Open frame is fine[3]Open frame is fine[5]
Part cooling fanFan on[1][3]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s3.2–8 at the 40–100 mm/s colorFabb specifies and the 50–100 mm/s Polymaker specifies, on a 0.4 mm nozzle at 0.2 mm layer[3][2][12]4–12 at Polymaker's 50–150 mm/s on a 0.4 mm nozzle at 0.2 mm layer[5]
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; flow has to be cut to match the expansion[2]Easy — minor profile tuning[5]
Extruder requirementBambu Lab PLA Aero is 0.4 mm nozzle only on the store and wiki, while its own TDS lists 0.4, 0.6 and 0.8[1][13]A second extruder or a tool changer[5]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely[3][4]Brass fine indefinitely[5]
Abrasiveness1–5Non-abrasive[3][4]Non-abrasive[5]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles; Bambu Lab warns the foamed extrudate swells and easily clogs the nozzle, and rules out 0.2 mm nozzles[13]Moderate — needs dry filament and a clean nozzle; Polymaker specifies a 55 °C dry for the PLA grade and warns brass nozzle life falls to about 9 h on the PA12 grade[5][6]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — 0.45 % saturated at 25 °C / 55 % RH (Bambu Lab); 0.40 % equilibrium (Polymaker)[1][3]Moderate — 0.64 % equilibrium water absorption (PolySupport for PLA)[5]
Equilibrium moisture content at ~50 % RH%0.45 saturated at 25 °C / 55 % RH (Bambu Lab); 0.40 equilibrium (Polymaker)[1][3]0.64 equilibrium water absorption (Polymaker PolySupport for PLA)[5]
Drying temperature & time55 °C for 6–8 h[1][3]Not documented
Effect of moisture on strengthPolymaker rates PLA low-sensitivity and publishes no dry-versus-conditioned figures for this grade; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[14]Not a structural material; no dry-versus-conditioned data is published[14]
Mechanical Properties
Tensile strength (XY)MPa24 ± 2 (Bambu Lab) and 24.4 (Polymaker) printed XY, ISO 527; colorFabb falls from 43.1 unfoamed to 10.8 at 45 % flow[1][3][2]Not documented
Young's modulusMPa1350 ± 250 (Bambu Lab) and 1689 (Polymaker) printed XY, ISO 527; colorFabb falls from 3334 unfoamed to 864 foamed[1][3][2]Not documented
Elongation at break%2.6 ± 0.7 (Bambu Lab) and 8.8 (Polymaker) printed XY, ISO 527[1][3]Not documented
Flexural strengthMPa45 ± 4 (Bambu Lab) and 50.2 (Polymaker) printed XY, ISO 178[1][3]Not documented
Flexural modulusMPa1690 ± 120 (Bambu Lab) and 1959 (Polymaker) printed XY, ISO 178[1][3]Not documented
Charpy impact, notchedkJ/m²8.2 ± 0.7 printed XY, ISO 179, notched (Bambu Lab); colorFabb 3.67 foamed[1][2]Not documented
Other impact dataCharpy unnotched 28.8 printed XY (Bambu Lab); colorFabb 5.46 foamed[1][2]Not documented
Layer adhesion / Z tensileMPa18 ± 3 printed Z, ISO 527 (Bambu Lab); flexural Z collapses to 17 against 45 in XY[1]Not documented
Brittleness1–5Brittle — snaps with little warning; elongation at break 2.6 % in XY and 1.2 % in Z[1]Not documented
Creep resistance / sustained load1–5Poor — no foamed-grade creep test; plain printed PLA sagged from 12 to 16.2–21.8 mm over 5 days at 1.25 kg, and the foam carries less solid[15][16][17]Not documented
Fatigue / repeated-flex resistance1–5Poor — no grade-specific S-N curve; plain printed PLA ran 38 000–49 000 cycles at 30 % of tensile strength and elongation at break falls to 2.6 % in XY and 1.2 % in Z[18][1]Not documented
Elasticity / flexibility1–5Rigid[1]Not documented
Z strength as % of XY%75 by tensile, 38 by flexural (printed, Bambu Lab)[1]Not documented
Thermal Properties
HDT at 0.45 MPa°C53 (Bambu Lab) and 54 (Polymaker), ISO 75 at 0.45 MPa[1][3]43 (ISO 75, 0.45 MPa, PolySupport for PA12). Polymaker's sheet prints a higher figure at the higher load, which is physically inverted; treat both HDT numbers as approximate[6]
HDT at 1.8 MPa°C48 (Bambu Lab) and 50 (Polymaker), ISO 75 at 1.8 MPa[1][3]53 (ISO 75, 1.8 MPa, PolySupport for PA12) — printed above the 0.45 MPa figure on Polymaker's own sheet, which cannot be right; treat both as approximate[6]
Glass transition (Tg)°C55 (Bambu Lab) and 59 (Polymaker), DSC[1][3]Not documented
Melting point / Vicat°C150 peak melt (Polymaker, DSC); Vicat 60 °C[3]Vicat 171 (PolySupport for PA12, ISO 306)[6]
Annealing responseBambu Lab advises against annealing thin, low-infill Aero prints[1]Not documented
Environment & Chemical
UV resistance1–5Degrades within weeks outdoors[19]Not documented
Electrical & ESD propertiesNot documentedSurface resistance above 10^13 ohm/sq (ASTM D257, THERMAX HTS2 and MTS1)[20][21]
Health & Safety
Fume toxicity1–5Low hazard — minimal VOC and particle emission[22]Low hazard — minimal VOC and particle emission; none of these materials was in the chamber study[22]
Ventilation / filtration requirement1–5None needed in a normal room[22]Open a window / occasional ventilation[22]
Post-Processing
Support material pairingNot documentedThis is the support material. Polymaker publishes an adhesion matrix per model material, from very good to unusable, because break-away supports only work against the polymer they were matched to[5][6]
Dimensional accuracy & detailFoamed surfaces are rough and matte; dimensional accuracy depends on holding the foaming temperature steady[1][2]Not documented
Solvents & Solubility
Soluble inChloroform dissolves the PLA matrix; the foamed wall wicks solvent right through instead of only skinning over.[23]None — break-away support is removed mechanically; 3DXTech lists no water or solvent route for it.[24]
Softened or crazed byAcetone, ethyl acetate and toluene plasticise the matrix but dissolve <1 % even at 65 °C; acetone submersion crazes parts.[23][25]Not documented
Solvent welding & smoothing agentChloroform vapour reaches only the resin skin; no workshop-safe smoothing agent exists for PLA of any kind.[26][25]None — there is no solvent to weld or smooth with.[24]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Bambu Filament Technical Data Sheet V4.0 — PLA Aero Bambu Lab · 2026-08 · tds
  2. LW-PLA technical data sheet colorFabb · 2026-08 · tds
  3. PolyLite LW-PLA Technical Data Sheet (V7.0) Polymaker · 2026-08 · tds
  4. PolyWood Technical Data Sheet Version 4.0 (Nov 2018) Polymaker (copy hosted by 3Dee) · 2018-11 · tds
  5. PolySupport Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  6. PolySupport for PA12 Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  7. PLA Aero — product page Bambu Lab US Store · 2026-08 · vendor
  8. Polymaker product catalogue Polymaker · 2026-08 · vendor
  9. YXPOLYER Breakaway Support Filament 1 kg Black — product page YXPOLYER · 2026-08 · vendor
  10. IEMAI 3D E-REMOVE breakaway support filament — store page IEMAI 3D · 2026-08 · vendor
  11. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  12. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  13. PLA Usage Guide Bambu Lab Wiki · 2026-08 · doc
  14. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  15. BambuLab PLA Basic vs PLA Tough vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  16. Polymaker PLA Pro vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  17. Carbon Fiber PLA vs META-PLA vs PLA+ vs PLA by Sunlu — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  18. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  19. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  20. THERMAX HTS2 Break Away Support Technical Data Sheet v1.0 3DXTech · 2026-08 · tds
  21. THERMAX MTS1 Break Away Support Technical Data Sheet v1.0 3DXTech · 2026-08 · tds
  22. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  23. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  24. THERMAX HTS1 — product page 3DXTech · 2026-08 · vendor
  25. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  26. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper