3D Printing Info

Filament comparison

LW-PLA vs PP-GF

Compare printing settings, strength, heat resistance, dated prices and sources.

Lightweight / foaming PLA (LW-PLA) guideGlass-fibre PP (PP-GF) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore LW-PLA comparisonsMore PP-GF comparisons
LW-PLA vs PP-GF — documented properties and sources
PropertyLightweight / foaming PLA (LW-PLA)PLAGlass-fibre PP (PP-GF)POLYOLEFIN
Market snapshot
Listing priceUSD/kg; dated snapshots$47.48/kg median; $37.49–$50.00/kg across 4 dated product listings$49.09/kg median; $46.27–$86.01/kg across 3 dated product listings
Identity & Market
Base polymer / chemistryPLA with a blowing agent. Two distinct types: active-foaming grades that expand at the nozzle (Bambu Lab PLA Aero, colorFabb LW-PLA) and pre-foamed grades that do not (Polymaker PolyLite LW-PLA, PolyWood)[1][2][3][4]Polypropylene reinforced with chopped glass fibre[5][6]
Densityg/cm³Filament 1.21 (Bambu Lab) and 1.24 (colorFabb); pre-foamed filament 0.8 (PolyWood, at 21.5 °C) and 0.9 (Polymaker LW-PLA); foamed prints reach 0.40[1][2][3][4]1.12 (Prusament PP Glass Fiber, ISO 1183) — the glass lifts it above water[5]
Typical priceUSD/kg1 kg-equivalent spools cluster near 45[7][2][8]1 kg-equivalent spools cluster near 49[9][10][11]
Price range across brandsUSD/kg37–50 across brands; Polymaker LW-PLA 37, Bambu Lab Aero 45, colorFabb 50, PolyWood 50[8][7][2]46-86 across brands; BCN3D PP GF30 46 at 700 g, BASF Ultrafuse PP GF30 49 at 2.2 kg, Prusament PP Glass Fiber 86 at 850 g[9][10][11]
Market availability1–5Available from several mainstream brands[7][8][2]Available from several mainstream brands[9][10][11]
Spool sizes & diameters1.75 and 2.85 mm; 0.6, 0.75, 0.8 and 1 kg spools[8][2]1.75 and 2.85 mm; 700 g, 850 g and 2.2 kg spools[9][10][11]
Typical applicationsRC aircraft, drone airframes and large props where mass matters more than strength[1][2]Stiff, chemically resistant parts where PP-CF's cost or conductivity is unwanted[6]
Diameter tolerance± mmNot documented±0.04 (Prusament)[5]
Printing Parameters
Nozzle temperature°C210–260 (Bambu Lab, foaming); 195–260 (colorFabb, foaming); 190–210 (Polymaker, pre-foamed)[1][2][3]245 ± 10 (Prusament) — 25 °C below the carbon-fibre grade[5][12]
Bed temperature°C35–45 (Bambu Lab); 50–60 (colorFabb); 25–60 (Polymaker)[1][2][3]95 ± 10 (Prusament)[5]
Enclosure / chamber requirement1–5Open frame is fine[3]Enclosure recommended — Simplify3D lists an enclosure as a hardware requirement and Polymaker advises one below 70 °C ambient to stop warping and cracking[13][14]
Part cooling fanFan on[1][3]Off — Prusa runs 0 % except 100 % on bridges[5]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s3.2–8 at the 40–100 mm/s colorFabb specifies and the 50–100 mm/s Polymaker specifies, on a 0.4 mm nozzle at 0.2 mm layer[3][2][15]4 at Prusa's 50 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[5][15]
Warping tendency1–5Not documentedHigh — enclosure needed for reliable large parts; Prusa recommends a brim[5]
Bed-adhesion difficulty1–5Not documentedVery difficult — special plates or slurry required[5]
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; flow has to be cut to match the expansion[2]Advanced — enclosure, hardware upgrades, tuning; hardened nozzle mandatory[5]
Extruder requirementBambu Lab PLA Aero is 0.4 mm nozzle only on the store and wiki, while its own TDS lists 0.4, 0.6 and 0.8[1][16]Prusa states a hardened nozzle is necessary and recommends a brim[5]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely[3][4]Hardened steel required[5]
Abrasiveness1–5Non-abrasive[3][4]Highly abrasive — standard GF composite[5]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles; Bambu Lab warns the foamed extrudate swells and easily clogs the nozzle, and rules out 0.2 mm nozzles[16]Moderate — needs dry filament and a clean nozzle; Prusa lists higher risk of nozzle clogging for glass-filled composites[17]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — 0.45 % saturated at 25 °C / 55 % RH (Bambu Lab); 0.40 % equilibrium (Polymaker)[1][3]Low (0.1–0.3 %) — 0.11 % at both 24 h and 7 days, higher than the carbon-fibre grade's 0.04 % but still very low[5][12]
Equilibrium moisture content at ~50 % RH%0.45 saturated at 25 °C / 55 % RH (Bambu Lab); 0.40 equilibrium (Polymaker)[1][3]0.11 after 24 h and 0.11 after 7 days at 24 °C / 22 % RH (Prusa Polymers)[5]
Drying temperature & time55 °C for 6–8 h[1][3]Not documented
Effect of moisture on strengthPolymaker rates PLA low-sensitivity and publishes no dry-versus-conditioned figures for this grade; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[18]Not applicable in practice at 0.11 % equilibrium uptake[5]
Storage requirementNot documentedNo special storage needed[5]
Mechanical Properties
Tensile strength (XY)MPa24 ± 2 (Bambu Lab) and 24.4 (Polymaker) printed XY, ISO 527; colorFabb falls from 43.1 unfoamed to 10.8 at 45 % flow[1][3][2]46.6 ± 1.3 filament tensile yield (Prusament, ISO 527) — more than double the carbon-fibre grade's 21[5][12]
Young's modulusMPa1350 ± 250 (Bambu Lab) and 1689 (Polymaker) printed XY, ISO 527; colorFabb falls from 3334 unfoamed to 864 foamed[1][3][2]Not documented
Elongation at break%2.6 ± 0.7 (Bambu Lab) and 8.8 (Polymaker) printed XY, ISO 527[1][3]Not documented
Flexural strengthMPa45 ± 4 (Bambu Lab) and 50.2 (Polymaker) printed XY, ISO 178[1][3]Not documented
Flexural modulusMPa1690 ± 120 (Bambu Lab) and 1959 (Polymaker) printed XY, ISO 178[1][3]Not documented
Charpy impact, notchedkJ/m²8.2 ± 0.7 printed XY, ISO 179, notched (Bambu Lab); colorFabb 3.67 foamed[1][2]7.9 ± 0.4 printed horizontal and 9.9 ± 0.8 printed vertical XZ (ISO 179-1, notched)[5]
Other impact dataCharpy unnotched 28.8 printed XY (Bambu Lab); colorFabb 5.46 foamed[1][2]Not documented
Layer adhesion / Z tensileMPa18 ± 3 printed Z, ISO 527 (Bambu Lab); flexural Z collapses to 17 against 45 in XY[1]Not documented
Brittleness1–5Brittle — snaps with little warning; elongation at break 2.6 % in XY and 1.2 % in Z[1]Moderate[5]
Hardness (scale-specific)Shore A / Shore D / RockwellNot documentedRockwell R102 (and M95) on extruded unfilled PP stock (ASTM D785); no figure is published for a glass-fibre PP filament[19]
Creep resistance / sustained load1–5Poor — no foamed-grade creep test; plain printed PLA sagged from 12 to 16.2–21.8 mm over 5 days at 1.25 kg, and the foam carries less solid[20][21][22]Not documented
Fatigue / repeated-flex resistance1–5Poor — no grade-specific S-N curve; plain printed PLA ran 38 000–49 000 cycles at 30 % of tensile strength and elongation at break falls to 2.6 % in XY and 1.2 % in Z[23][1]Not documented
Elasticity / flexibility1–5Rigid[1]Rigid[5]
Z strength as % of XY%75 by tensile, 38 by flexural (printed, Bambu Lab)[1]Not documented
Thermal Properties
HDT at 0.45 MPa°C53 (Bambu Lab) and 54 (Polymaker), ISO 75 at 0.45 MPa[1][3]138.3 (ISO 75, 0.45 MPa)[5]
HDT at 1.8 MPa°C48 (Bambu Lab) and 50 (Polymaker), ISO 75 at 1.8 MPa[1][3]112.6 (ISO 75, 1.8 MPa)[5]
Glass transition (Tg)°C55 (Bambu Lab) and 59 (Polymaker), DSC[1][3]Not documented
Melting point / Vicat°C150 peak melt (Polymaker, DSC); Vicat 60 °C[3]Not documented
Annealing responseBambu Lab advises against annealing thin, low-infill Aero prints[1]Not documented
Environment & Chemical
UV resistance1–5Degrades within weeks outdoors[24]Not documented
Chemical resistanceNot documentedExcellent against acids, alkalis and most solvents[14]
Water / humidity resistance in service1–5Not documentedExcellent — essentially unaffected[5]
Health & Safety
Fume toxicity1–5Low hazard — minimal VOC and particle emission[25]Low hazard — minimal VOC and particle emission. Inferred: no polyolefin was among the nine filaments in the Azimi chamber study, so this is a family-level judgement rather than a measurement[25]
Ventilation / filtration requirement1–5None needed in a normal room[25]Open a window / occasional ventilation. Inferred — no polyolefin was measured in the chamber study[25]
Dust & fibre handling hazardNot documentedGlass fibre is bound in the matrix; avoid inhaling sanding dust[5]
Post-Processing
Dimensional accuracy & detailFoamed surfaces are rough and matte; dimensional accuracy depends on holding the foaming temperature steady[1][2]Not documented
Solvents & Solubility
Soluble inChloroform dissolves the PLA matrix; the foamed wall wicks solvent right through instead of only skinning over.[26]None at room temperature; chloroform dissolves the matrix at 60 °C and xylene at about 118 °C, leaving the fibre.[27][28]
Softened or crazed byAcetone, ethyl acetate and toluene plasticise the matrix but dissolve <1 % even at 65 °C; acetone submersion crazes parts.[26][29]Xylene, decalin, CCl4 and chlorobenzene are heavily absorbed at 20 °C; oleum, chlorosulphonic acid and bromine destroy it.[27]
Solvent welding & smoothing agentChloroform vapour reaches only the resin skin; no workshop-safe smoothing agent exists for PLA of any kind.[30][29]None — nothing softens PP at room temperature, so joints have to be welded thermally rather than chemically.[27]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Bambu Filament Technical Data Sheet V4.0 — PLA Aero Bambu Lab · 2026-08 · tds
  2. LW-PLA technical data sheet colorFabb · 2026-08 · tds
  3. PolyLite LW-PLA Technical Data Sheet (V7.0) Polymaker · 2026-08 · tds
  4. PolyWood Technical Data Sheet Version 4.0 (Nov 2018) Polymaker (copy hosted by 3Dee) · 2018-11 · tds
  5. Prusament PP Glass Fiber Technical Datasheet v1.0 Prusa Polymers · 2024-11 · tds
  6. Prusament PP Glass Fiber — material page Prusa Polymers · 2026-08 · doc
  7. PLA Aero — product page Bambu Lab US Store · 2026-08 · vendor
  8. Polymaker product catalogue Polymaker · 2026-08 · vendor
  9. BASF Ultrafuse PP GF30 Black 2.85 mm 2.200 g igo3d · 2026-08 · vendor
  10. BCN3D PP GF30 Black 2.85 mm 700 g igo3d · 2026-08 · vendor
  11. Prusa Prusament PP Glass Fiber Natural (NFC), 1.75 mm / 850 g 3DJAKE · 2026-08 · vendor
  12. Prusament PP Carbon Fiber Technical Datasheet v1.0 Prusa Polymers · 2024-11 · tds
  13. Polypropylene — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  14. PP — material basics Polymaker Wiki · 2026-08 · doc
  15. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  16. PLA Usage Guide Bambu Lab Wiki · 2026-08 · doc
  17. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  18. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  19. TECAFINE PP natural — stock shape properties Ensinger · 2026-08 · tds
  20. BambuLab PLA Basic vs PLA Tough vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  21. Polymaker PLA Pro vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  22. Carbon Fiber PLA vs META-PLA vs PLA+ vs PLA by Sunlu — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  23. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  24. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  25. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  26. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  27. Pro-fax and Moplen polypropylene — Chemical Resistance Guide (20, 60 and 100 °C) LyondellBasell · 2026-08 · tds
  28. US 5,278,282 Polymer recycling by selective dissolution — xylene dissolution temperatures Nauman & Lynch, Rensselaer Polytechnic Institute · 1994-01 · paper
  29. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  30. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper