| Property | Conductive filamentSPECIALTY | PA12 (Nylon 12)PA |
|---|---|---|
| Market snapshot | ||
| Listing priceUSD/kg; dated snapshots | $170.36/kg median; $89.99–$796.00/kg across 4 dated product listings | $64.33/kg median; $36.00–$170.67/kg across 3 dated product listings |
| Identity & Market | ||
| Base polymer / chemistry | A carbon-filled compound conductive by volume rather than merely dissipative; Proto-pasta's is PLA-based, Recreus's and NinjaTek's are TPU, and add:north's Koltron G1 does not state its base polymer[1][2][3][4] | Polyamide 12 — the longest-chain common nylon, with the fewest amide groups per unit mass and so the least moisture uptake[5][6] |
| Densityg/cm³ | Not documented | 1.01 specific gravity (Stratasys FDM Nylon 12, ASTM D792)[7] |
| Typical priceUSD/kg | 1 kg-equivalent spools span 90–181 for the carbon-filled grades; add:north's Koltron G1 sits far above at 796 because it is sold only in 100 and 250 g coils[8][9][10] | 1 kg-equivalent spools span 36–171; the middle of the market is about 64[11][12] |
| Price range across brandsUSD/kg | 90–796 across brands; Proto-pasta conductive PLA 90 at 1 kg, Recreus Conductive Filaflex 160 at 500 g, NinjaTek Eel 181 at 1 kg, add:north Koltron G1 796 at 250 g[8][2][9][10] | 36–171 across brands; IEMAI 3D 36, Fiberlogy 64 at 3DJake, 3DXTech AmideX Nylon 12 171[11][13][12] |
| Market availability1–5 | Niche, a handful of specialist brands[8][2] | Available from several mainstream brands[11][13] |
| Spool sizes & diameters | 1.75 and 2.85 mm; 0.05, 0.1, 0.25, 0.5, 1 and 2 kg spools[8][2][9][10] | 1.75 and 2.85 mm; 750 g and 1 kg spools[13][11] |
| Typical applications | Capacitive touch surfaces, low-current traces, EMI shielding and static-safe fixtures[1] | Dimensionally stable functional parts, ducting and living hinges where PA6 would move too much with humidity[5][14] |
| Printing Parameters | ||
| Nozzle temperature°C | Not documented | 260–290 (Extrudr DURAPRO PA12)[15] |
| Bed temperature°C | Not documented | 110 (Extrudr DURAPRO PA12)[15] |
| Enclosure / chamber requirement1–5 | Open frame is fine[1] | Enclosure required (passive)[5] |
| Part cooling fan | Not documented | Part cooling fan not required (Simplify3D)[16] |
| Bed surface & adhesion aid | Not documented | PEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[16][5] |
| Maximum volumetric flow (mm³/s; see test conditions)mm³/s | Not documented | 12 at Extrudr's 150 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[15][17] |
| Bed-adhesion difficulty1–5 | Not documented | Needs a specific surface plus adhesive[16][5] |
| Stringing / oozing tendency1–5 | Not documented | Moderate — retraction tuning needed[5] |
| Overall printing difficulty1–5 | Intermediate — dry filament and a tuned profile[1] | Advanced — enclosure, hardware upgrades, tuning[5] |
| Hardware Wear & Reliability | ||
| Nozzle hardness required1–4 | Brass acceptable; hardened steel for volume work[1] | Brass fine indefinitely for unfilled grades[5] |
| Abrasiveness1–5 | Moderately abrasive — conductive carbon filler[1] | Non-abrasive when unfilled[5] |
| Nozzle clog risk1–5 | Low — Proto-pasta states the carbon-filled grade prints on standard PLA settings with no special nozzle required[1] | High — jams from moisture, heat creep or particles[14][18] |
| Heat-creep / jam sensitivity1–5 | Not documented | Moderate — good heatbreak cooling needed[16] |
| Hotend requirement | Not documented | May require an all-metal hot end (Simplify3D)[16] |
| Moisture Behaviour | ||
| Moisture absorption (hygroscopicity)1–5 | Not documented | High (0.8–2 %) — Polymaker's PA12-CF10 reaches 1.5 % equilibrium against 3.33 % for its PA6-GF25, and Polymaker developed the PA12 grade specifically for lower moisture sensitivity[6][14] |
| Drying temperature & time | Not documented | 60–80 °C for 8–12 h (Extrudr DURAPRO PA12); 100 °C for 8 h (Polymaker CoPA)[15][19] |
| Symptoms when wet | Not documented | Popping and cracking during extrusion, then hard-to-diagnose defects[14] |
| Effect of moisture on strength | Polymaker rates PLA low-sensitivity and publishes no dry-versus-conditioned figures; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[18] | Polymaker states its PA12 grade changes little between wet and dry, unlike its PA6-based materials; the CoPA dry-to-wet reference shows what the PA6-type response looks like[14][19] |
| Storage requirement | Not documented | Sealed below 20 % RH with desiccant[18] |
| Hydrolysis at melt temperature | Not documented | Polymaker requires a 100 °C dry for 8 h and storage below 20 % RH; no molecular-weight loss figure is published, and the published wet data is conditioning rather than melt hydrolysis[19][20] |
| Mechanical Properties | ||
| Tensile strength (XY)MPa | Not documented | 49.3 at yield and 33.4 at break printed XZ (Stratasys FDM Nylon 12, ASTM D638)[7] |
| Young's modulusMPa | Not documented | 1510 printed XZ and 1250 ZX (Stratasys FDM Nylon 12, ASTM D638)[7] |
| Elongation at break% | Not documented | 30 at break printed XZ against 6.5 in ZX (Stratasys FDM Nylon 12, ASTM D638)[7] |
| Charpy impact, notchedkJ/m² | Not documented | 11 at +23 °C and 6.0 at -30 °C (Extrudr DuraPro PA12, ISO 179/1eA); unnotched does not break[15] |
| Other impact data | Not documented | Izod notched 138 J/m printed XZ against 71.0 J/m in ZX (Stratasys FDM Nylon 12, ASTM D256)[7] |
| Layer adhesion / Z tensileMPa | Not documented | 41.8 at yield and 41.2 at break printed ZX (Stratasys FDM Nylon 12, ASTM D638) — higher than the XZ break figure, because XZ specimens draw and neck first[7] |
| Brittleness1–5 | Brittle — snaps with little warning; carbon-black loading at conductive levels embrittles PLA[1] | Tough — absorbs impact, yields before breaking[5] |
| Creep resistance / sustained load1–5 | Not documented | Moderate — the long-chain polyamides hold load better than PLA but below PC[5] |
| Fatigue / repeated-flex resistance1–5 | Not documented | Excellent — living hinges viable. Stratasys sells FDM Nylon 12 specifically for repetitive-flex parts such as snap-fit clips and press-fit inserts on the strength of its fatigue properties[5][7] |
| Elasticity / flexibility1–5 | Rigid[1] | Semi-flexible[14] |
| Z strength as % of XY% | Not documented | 85 (Stratasys FDM Nylon 12, ZX against XZ tensile yield, ASTM D638) — one of the least anisotropic unfilled filaments measured[7] |
| Thermal Properties | ||
| HDT at 0.45 MPa°C | Not documented | 94.7 printed XY and 91.9 in XZ/ZX (Stratasys FDM Nylon 12, ASTM D648 at 66 psi)[7] |
| HDT at 1.8 MPa°C | Not documented | 84.3 printed XY and 75.3 in XZ/ZX (Stratasys FDM Nylon 12, ASTM D648 at 264 psi)[7] |
| Glass transition (Tg)°C | Not documented | 34.0 (Stratasys FDM Nylon 12, ASTM D7426 inflection point)[7] |
| Melting point / Vicat°C | Not documented | Vicat A 142 (Extrudr DURAPRO PA12, ISO 306)[15] |
| Continuous service temperature°C | Not documented | Bounded by a Vicat softening point of 142 °C (Extrudr DURAPRO PA12); no loaded-bar service figure is published[15] |
| Thermal expansion (CTE)µm/m·K | Not documented | 84-103 printed (Stratasys FDM Nylon 12, ASTM E831: 84.4 in XY and 85.6 in XZ/ZX over -50 to 10 °C, 89.1 over 10-45 °C, 98.2 over 45-70 °C); Extrudr quotes 100 for DURAPRO PA12 (ISO 11359-2)[15][7] |
| Flammability / UL 94 | Not documented | Flammable; no UL 94 rating published for the unfilled grades surveyed[15] |
| Environment & Chemical | ||
| UV resistance1–5 | Not documented | Months outdoors before embrittlement[5] |
| Chemical resistance | Not documented | Withstands oils, fuels and alkalis[5] |
| Water / humidity resistance in service1–5 | Not documented | Good — minor absorption; the least moisture-sensitive of the common nylons[14] |
| Food contact | Not documented | Not food-contact certified as filament[5] |
| Biodegradability / compostability | Not documented | Not biodegradable[5] |
| Recyclability | Not documented | Mechanically recyclable but not accepted in household plastic collection[5] |
| Electrical & ESD properties | Conductive rather than dissipative — Proto-pasta sells the grade as electrically conductive composite PLA[1] | Not documented |
| Health & Safety | ||
| Fume toxicity1–5 | Low hazard — minimal VOC and particle emission; none of these materials was in the chamber study[21] | Moderate — measurable VOCs and UFPs, ventilation advised[21] |
| VOC emission rateµg/min | Not documented | Up to 180 caprolactam, the dominant VOC from nylon; total VOC reached nearly 200 µg/min, the highest of the nine filaments tested[21] |
| Ultrafine-particle emission rateparticles/min | Not documented | ≈2 × 10⁸ median — low for ultrafine particles despite the highest VOC mass of any filament tested[21] |
| Hazardous species emitted | Not documented | Caprolactam, at up to 180 µg/min from nylon filament — the largest single-VOC emission rate measured in the study[21] |
| Ventilation / filtration requirement1–5 | Open a window / occasional ventilation[21] | Ventilated room or enclosure recommended[21] |
| Dust & fibre handling hazard | Conductive carbon filler is bound in the matrix; avoid inhaling sanding dust[1] | Not documented |
| Post-Processing | ||
| Sanding & machining | Not documented | Sands poorly — gums rather than powders[16] |
| Gluing & solvent welding | Not documented | Cyanoacrylate; no common solvent welds polyamide[16] |
| Vapour / chemical smoothing | Not documented | No practical vapour smoothing[16] |
| Support material pairing | Not documented | Polymaker sells a break-away PolySupport matched to PA12[16] |
| Dimensional accuracy & detail | Not documented | Holds dimensions better than PA6 after conditioning — Polymaker singles its PA12 grade out on exactly this point[14] |
| Solvents & Solubility | ||
| Soluble in | Chloroform dissolves PLA-based grades, leaving the carbon black; TPU-based grades need DMF, NMP or THF. Laboratory reagents.[22][23] | Dissolved at 23 °C by formic acid, phenol, m-cresol, 96 % sulphuric acid or hexafluoroisopropanol — all laboratory reagents.[24][25] |
| Softened or crazed by | Acetone and ethyl acetate plasticise a PLA-based grade; a TPU-based grade swells in toluene, esters and alcohols.[22][23] | Not resistant to 10 % formic acid, phenol, chloroform or dichloromethane (Ensinger); zinc chloride stress-cracks nylon.[25][24] |
| Solvent welding & smoothing agent | None — neither PLA nor TPU has a workshop-safe welding or smoothing solvent.[22][23] | None — nylon's only solvents are formic acid, phenol and HFIP, all of which degrade the part they wet.[24] |
Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.
Sources for this comparison
- Electrically Conductive Composite PLA — product page and technical data Proto-pasta · 2026-08 · tds
- Recreus product catalogue Recreus · 2026-08 · vendor
- Eel 3D Printing Filament Technical Specifications NinjaTek · 2026-08 · tds
- Koltron G1 Technical Data Sheet add:north · 2026-08 · tds
- PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
- Fiberon PA612-CF15 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
- FDM Nylon 12 — Material Data Sheet Stratasys · 2021-09 · tds
- Proto-pasta product catalogue Proto-pasta · 2026-08 · vendor
- Eel product page — durometer, print guidelines and price NinjaTek · 2026-08 · vendor
- add:north Koltron G1 product page add:north · 2026-08 · vendor
- Nylon PA12 — product listing 3DJake International · 2026-08 · vendor
- IEMAI 3D PA12 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
- 3DXTech product catalogue 3DXTech · 2026-08 · vendor
- Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
- Extrudr Product Catalogue (DURAPRO PA12 data block) Extrudr · 2025-03 · tds
- Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
- Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
- Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
- PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
- PolyMide CoPA — Technical Data Sheet page Polymaker Wiki · 2026-08 · tds
- Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
- Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
- Elastollan — Chemical properties: swelling and chemical resistance BASF · 2026-08 · tds
- Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
- Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds