3D Printing Info

Filament comparison

ASA vs PA aramid

Compare printing settings, strength, heat resistance, dated prices and sources.

ASA guideAramid-fibre nylon guide

2 selected · all documented properties

Open these two in the interactive comparisonMore ASA comparisonsMore PA aramid comparisons
ASA vs PA aramid — documented properties and sources
PropertyASAASAAramid-fibre nylonPA
Market snapshot
Listing priceUSD/kg; dated snapshots$28.98/kg median; $17.99–$50.00/kg across 14 dated product listingsNot documented
Identity & Market
Base polymer / chemistryAcrylonitrile styrene acrylate — ABS with the butadiene rubber phase replaced by an acrylate rubber that has no UV-vulnerable double bonds[1][2]Aramid-fibre reinforced polyamide[3]
Densityg/cm³1.05 (Bambu Lab) to 1.13 (PolyLite ASA), ISO 1183; Prusament 1.07[4][5][2]Not documented
Typical priceUSD/kg1 kg spools cluster near 30[6][7][8]Not documented
Price range across brandsUSD/kg18–50 across brands; IEMAI 18, SUNLU 18, Ambrosia 23, Polymaker 26, Bambu Lab 30, YXPOLYER 30, Prusament 41, 3DXTech 50[9][7][6][10][8][11][12][13][14]Not documented
Market availability1–5Stocked by most mainstream brands[6][7][11][8]Special order, 1–2 makers worldwide — no aramid-filled nylon filament was found in any catalogue searched; the aramid filaments that do exist in the retail market use an ASA matrix[7][11]
Spool sizes & diameters1.75 and 2.85 mm; 0.8, 1, 4 and 10 kg spools[11][8][6]Not documented
Typical applicationsOutdoor fittings, signage, automotive exterior trim and anything that has to hold colour and strength in sunlight[15][1]Not documented
Diameter tolerance± mm±0.04 (Prusament)[2]Not documented
Printing Parameters
Nozzle temperature°C230–270 across brands; Prusament 260 ± 10, Bambu Lab 240–270, PolyLite 230–260[4][5][2]Not documented
Bed temperature°C75–110; Prusament 110 ± 5, Bambu Lab 80–100, PolyLite 75–95[4][5][2]Not documented
Enclosure / chamber requirement1–5Enclosure recommended — Polymaker calls a chamber needed at ambient temperature, Bambu Lab requires an enclosed printer and rules out its P1P and A-series machines[5][16]Enclosure required (passive) — as for every nylon[3]
Recommended chamber temperature°C45–60 (Bambu Lab)[4]Not documented
Part cooling fanLow — Prusament 30 % within a 0–50 % range, Bambu Lab 0–80 %, PolyLite off[2][4][5]Not documented
Bed surface & adhesion aidSatin, smooth PEI or powder-coated sheet with a glue stick; Prusa advises a 3 mm or taller brim on large parts[2][16]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s10–16 (PrusaSlicer guidance for ABS/ASA)[17]Not documented
Warping tendency1–5High — enclosure needed for reliable large parts; Prusa recommends a tall brim and Bambu Lab attributes cracking to cooling stress exceeding interlayer adhesion[2][16]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[2][16]Not documented
Stringing / oozing tendency1–5Slight[5]Not documented
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile[16][2]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely[16]Hardened steel required — no aramid-filled nylon datasheet was obtainable; Polymaker measures about 9 h of brass nozzle life on its fibre-filled nylons[18]
Abrasiveness1–5Non-abrasive[16]Highly abrasive — fibre-reinforced nylon composite[18]
Nozzle clog risk1–5Low — no special hot-end required and clogging is not among the listed drawbacks; Prusa lists no drybox and no hardened nozzle[19][20]High — jams from moisture, heat creep or particles; nylon already needs a drybox and Prusa names kevlar among the fibres that raise nozzle-clogging risk[21]
Heat-creep / jam sensitivity1–5Slightly sensitive[19]Not documented
Hotend requirementNo special hot-end required[19]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — 0.45 % saturated at 25 °C / 55 % RH (Bambu Lab) and 0.40 % equilibrium (Polymaker); Prusa measures only 0.17 % after 7 days at 22 % RH[4][5][2]Very high (>2 %) — the polyamide matrix governs uptake[22]
Equilibrium moisture content at ~50 % RH%0.45 saturated at 25 °C / 55 % RH (Bambu Lab); 0.40 equilibrium (Polymaker); 0.17 after 7 days at 24 °C / 22 % RH (Prusa)[4][5][2]Not documented
Drying temperature & time80 °C for 8 h (Bambu Lab); 70 °C for 7 h (Polymaker)[4][5]Not documented
Symptoms when wetBubbling and popping at the nozzle, stringing, rough surface and weak layers[22]Not documented
Effect of moisture on strengthNo dry-versus-conditioned figures are published for ASA; Polymaker groups the styrenics as moderate-sensitivity and the loss shows as poor layer adhesion rather than a stated strength delta[22]Polymaker's printed dry-versus-wet blocks for its CoPA nylon show what conditioning does to the family: tensile 78.0 → 34.3 MPa and modulus 2703 → 724 MPa, with notched Charpy rising 6.9 → 27.7 kJ/m². Fibre reinforcement reduces but does not remove the effect[23][24]
Storage requirementSealed with desiccant; Polymaker rates the styrenics moderate-sensitivity[22]Not documented
Mechanical Properties
Tensile strength (XY)MPa37 ± 3 (Bambu Lab) to 43.8 (PolyLite) printed XY, ISO 527; Prusament 42 ± 1 at yield; Formfutura quotes 47.5 at yield[4][5][2][25]Not documented
Young's modulusMPa2379 (PolyLite) to 2450 (Bambu Lab) printed XY, ISO 527; Prusament 1600, Formfutura 2020[4][5][2][25]Not documented
Elongation at break%6.7 (PolyLite) to 9.2 (Bambu Lab) at break, printed XY, ISO 527; Formfutura quotes 15 at break, Prusament 3.4 at yield[4][5][25][2]Not documented
Flexural strengthMPa64 ± 1 printed horizontal (Prusament, ISO 178); Bambu Lab 65 ± 5, PolyLite 73.4[2][4][5]Not documented
Flexural modulusMPa1920 ± 130 (Bambu Lab) to 3206 (PolyLite) printed XY, ISO 178; Prusament 2000[4][5][2]Not documented
Charpy impact, notchedkJ/m²10.3 (PolyLite) to 19.6 (Bambu Lab) printed XY, ISO 179, notched; Prusament 12 ± 1, Formfutura 18[5][4][2][25]Not documented
Other impact dataCharpy unnotched 25 ± 3 printed horizontal and 38 ± 11 printed vertical (Prusament, ISO 179-1); Bambu Lab 41.0 ± 2.3 printed XY[2][4]Not documented
Layer adhesion / Z tensileMPa11 ± 1 (Prusa interlayer adhesion test); 31 ± 4 (Bambu Lab) and 32 (PolyLite) printed Z tensile, ISO 527[2][4][5]Not documented
Brittleness1–5Tough — absorbs impact, yields before breaking[4][2]Not documented
Hardness (scale-specific)Shore A / Shore D / Rockwell78 Shore D (Prusa Polymers method)[2]Not documented
Creep resistance / sustained load1–5Moderate — no printed-ASA creep test found; Tg of 98 °C keeps room-temperature service far below softening, unlike PLA[5][2]Not documented
Fatigue / repeated-flex resistance1–5Moderate — fatigue limit at 25 % of tensile strength (8 MPa) on printed specimens, the best of the four polymers in that study[26]Not documented
Elasticity / flexibility1–5Rigid[4]Not documented
Z strength as % of XY%84 (Bambu Lab, printed Z against XY tensile); 73 for PolyLite ASA[4][5]Not documented
Thermal Properties
HDT at 0.45 MPa°C93 (Prusament) to 103 (PolyLite), ISO 75 at 0.45 MPa; Bambu Lab 100[2][5][4]Not documented
HDT at 1.8 MPa°C86 (Prusament) to 100 (PolyLite), ISO 75 at 1.8 MPa; Bambu Lab 92[2][5][4]Not documented
Glass transition (Tg)°C98 (PolyLite, DSC)[5]Not documented
Melting point / Vicat°CAmorphous — no melting point; Vicat 105 (PolyLite, ISO 306)[5]Not documented
Continuous service temperature°C93 — Prusa publishes this as the temperature resistance of Prusament ASA[27]Not documented
Thermal expansion (CTE)µm/m·K69 ± 17 in XY and 115 ± 24 in the build direction (printed, TMA, 40–70 °C)[28]Not documented
Flammability / UL 94Flammable; no UL 94 rating published for standard ASA[4]Not documented
Environment & Chemical
UV resistance1–5Excellent — designed for permanent outdoor use. After 1000 h of QUV exposure to ASTM G154 Stratasys measured yield strength falling only from 30.5 to 30.3 MPa and stress at break by 3.0 %[15]Not documented
Outdoor durability1000 h QUV per ASTM G154, cycling 8 h at 60 °C and 4 h at 50 °C with condensation: yield 30.5 → 30.3 MPa, stress at break 30.5 → 29.5 MPa, elongation 2.8 → 2.3 %, modulus 1.82 → 1.95 GPa[15]Not documented
Chemical resistanceGood against weak acids, weak alkalis, oils and grease; dissolved by acetone[5]Not documented
Water / humidity resistance in service1–5Good — minor absorption[4]Not documented
Food contactNot food safe[1]Not documented
Biodegradability / compostabilityNot biodegradable[1]Not documented
RecyclabilityNot accepted in household plastic collection[1]Not documented
Health & Safety
Fume toxicity1–5High — hazardous VOC such as styrene; enclosure and filtration needed[29][16]Moderate — measurable VOCs and UFPs, ventilation advised[29]
VOC emission rateµg/min12–113 styrene, the range measured across the styrenic filaments tested; ASA itself was not among them[29]Up to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[29]
Ultrafine-particle emission rateparticles/min2 × 10¹⁰ to 9 × 10¹⁰ median for ABS, the closest styrenic tested; ASA itself was not measured[29]≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[29]
Hazardous species emittedStyrene. Bambu Lab states ABS and ASA release harmful gases such as styrene at printing temperature, which can be toxic and cause dizziness or nausea. Azimi et al. measured styrene from every styrenic filament tested but did not test ASA itself[16][29]Caprolactam, at up to 180 µg/min from nylon filament[29]
Ventilation / filtration requirement1–5Enclosure with carbon and HEPA filtration[29][16]Ventilated room or enclosure recommended[29]
Post-Processing
Sanding & machiningSands well and takes filler before painting[1]Not documented
Gluing & solvent weldingSolvent-welds with acetone[5]Not documented
Vapour / chemical smoothingAcetone vapour smoothing works — ASA dissolves in acetone[5]Not documented
Support material pairingHIPS breaks away or dissolves in d-limonene; Bambu Lab sells a dedicated Support for ABS that also serves ASA[16]Not documented
Dimensional accuracy & detailWarping and cooling-stress cracking are the accuracy limits; Stratasys notes the matte finish as a deliberate aesthetic advantage[16][15]Not documented
Solvents & Solubility
Soluble inAcetone dissolves it (Polymaker); MEK, THF, ethyl acetate and the chlorinated solvents dissolve the styrenic backbone.[30][5]Formic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[31]
Softened or crazed byLimonene attacks some grades — Prusa reports Prusament ASA Orange flaking apart as layer adhesion fails.[32]Zinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[31]
Solvent welding & smoothing agentAcetone vapour, ~20 min at 80 °C over 5 mm of liquid (15–40 min across brands); layer adhesion up, tensile slightly down.[33]None — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[31]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. ASA — material basics Polymaker Wiki · 2026-08 · doc
  2. Prusament ASA Technical Datasheet v1.1 Prusa Polymers · 2024-05 · tds
  3. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  4. Bambu Filament Technical Data Sheet V3.0 — ASA Bambu Lab · 2026-08 · tds
  5. PolyLite ASA Technical Data Sheet Polymaker · 2024-11 · tds
  6. ASA — product page Bambu Lab US Store · 2026-08 · vendor
  7. Polymaker product catalogue Polymaker · 2026-08 · vendor
  8. Printed Solid product catalogue Printed Solid · 2026-08 · vendor
  9. Filastruder product catalogue Filastruder · 2026-08 · vendor
  10. ZYLtech ASA-GF Glass Fiber filament — product page ZYLtech · 2026-08 · vendor
  11. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  12. IEMAI ASA 3D Printing Filament product page IEMAI 3D · 2026-08 · vendor
  13. SUNLU ASA 3D Printer Filament 1 kg SUNLU · 2026-08 · vendor
  14. YXPOLYER ASA Purple product page YXPOLYER · 2026-08 · vendor
  15. ASA — FDM Material Data Sheet (includes 1000 h QUV exposure results) Stratasys · 2026-08 · tds
  16. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  17. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  18. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  19. ASA — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  20. Filament Material Guide Prusa Knowledge Base · 2026-08 · doc
  21. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  22. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  23. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  24. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  25. ApolloX Technical Data Sheet Formfutura · 2026-08 · tds
  26. Mechanical, Fatigue, and Thermal Characterization of ASA, Nylon 12, PC and PC-ABS Manufactured by Fused Filament Fabrication (FFF) Polymers 18(2):302 · 2026-01 · paper
  27. Prusament ASA — material page Prusa Polymers · 2026-08 · doc
  28. Basalt Fiber Composites with Reduced Thermal Expansion for Additive Manufacturing Polymers 14(15):3216 · 2022-08 · paper
  29. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  30. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  31. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  32. HIPS — Knowledge Base Prusa Research · 2026-08 · doc
  33. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc