3D Printing Info

Filament comparison

ABS+ vs PCTG

Compare printing settings, strength, heat resistance, dated prices and sources.

ABS+ / Tough ABS guidePCTG guide

2 selected · all documented properties

Open these two in the interactive comparisonMore ABS+ comparisonsMore PCTG comparisons
ABS+ vs PCTG — documented properties and sources
PropertyABS+ / Tough ABSABSPCTGPETG
Market snapshot
Listing priceUSD/kg; dated snapshots$26.49/kg median; $15.99–$29.99/kg across 4 dated product listings$34.99/kg median; $14.00–$50.67/kg across 5 dated product listings
Identity & Market
Base polymer / chemistryABS reformulated for lower warping and a higher glass transition; Polymaker's ABS Pro and ABS Max reach Tg 114.9 and 126.3 °C against 101 °C for PolyLite ABS[1][2][3]Poly(cyclohexylenedimethylene terephthalate) glycol — a copolyester with a higher cyclohexanedimethanol content than PETG[4][5]
Densityg/cm³1.04 (ABS Pro) and 1.06 (ABS Max), ISO 1183[1][2]1.23 (Extrudr, ASTM D792; 3DXTech, ISO 1183)[5][6]
Typical priceUSD/kg1 kg spools cluster near 27[7]1 kg spools cluster near 34[8][6][9]
Price range across brandsUSD/kg16–30 across brands; SUNLU E-ABS 16, Polymaker ABS Pro 25, YXPOLYER ABS Enhanced 28, Polymaker ABS Max 30[7][10][11]14–51 across brands; CHCKX 14 in a 10-roll bundle, Push Plastic 30, Proto-pasta 35 at 1 kg, 3DXTech 51[8][6][12]
Market availability1–5Available from several mainstream brands[7]Available from several mainstream brands[8][6][9][13]
Spool sizes & diameters1.75 and 2.85 mm; 1 kg spools[7]1.75 and 2.85 mm; 0.5, 0.75, 1, 3 and 5 kg spools[8][9][6]
Typical applicationsLarge enclosure and automotive parts where plain ABS warps or softens too early[1][2]Transparent covers, guards and impact-loaded parts where PETG cracks[4][5]
Printing Parameters
Nozzle temperature°C270–290 (ABS Pro); 270–300 (ABS Max) — 25–35 °C above plain ABS[1][2]250–270 (Spectrum, Extrudr)[4][5]
Bed temperature°C120 (ABS Max)[2]60–100 (Spectrum)[4]
Enclosure / chamber requirement1–5Enclosure required (passive)[1][2][14]Open frame is fine — Spectrum and Extrudr both say a closed chamber is not necessary, Extrudr adds it helps on larger parts[4][5]
Part cooling fanNot documentedUp to 100 % (Spectrum); 20–50 % (Extrudr)[4][5]
Bed surface & adhesion aidClean the plate and apply glue; Simplify3D also lists Kapton tape and ABS slurry[14][15]Textured PEI, satin or powder-coated sheets; on smooth PEI a glue stick acts as a release agent[16][17]
Maximum volumetric flow (mm³/s; see test conditions)mm³/sUp to 250 mm/s (ABS Pro) and 200 mm/s (ABS Max), equivalent to 20 and 16 on a 0.4 mm nozzle at 0.2 mm layer[1][2][18]1.6–16 at the 20–200 mm/s Extrudr rates the material for, on a 0.4 mm nozzle at 0.2 mm layer[5][18]
Warping tendency1–5High — enclosure needed for reliable large parts[14]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[14]Needs the right surface or a thin adhesive — the problem is releasing the part, not sticking it[16][17]
Stringing / oozing tendency1–5Slight — Polymaker advises 1–2 mm retraction at 20–30 mm/s[19]Moderate — retraction tuning needed; Polymaker names stringing as PETG's common quirk[17]
Shrinkage%Not documented0.2–0.5 (Extrudr, ASTM D955)[5]
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; the hotter nozzle rules out PTFE-lined hotends[1][2]Easy — minor profile tuning[4][5]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely[14]Brass fine indefinitely — Extrudr explicitly states no hardened nozzle is needed[5]
Abrasiveness1–5Non-abrasive[14]Non-abrasive[5]
Nozzle clog risk1–5Low — unfilled ABS compound; no special hot-end required and clogging is not among the listed drawbacks[15][20]Low — 3DXTech lists no special nozzle concerns and no minimum layer height for PCTG, only a 65 °C pre-dry[21]
Heat-creep / jam sensitivity1–5Slightly sensitive[15]Slightly sensitive[22]
Hotend requirementNo special hot-end required[15]No special hot-end required[22]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — 0.51 % maximum water absorption (ABS Pro)[1]Moderate (0.3–0.8 %) — the copolyester matrix reaches 0.40 % saturated at 25 °C / 55 % RH and 3DXTech specifies a 65 °C, 4 h pre-dry[16][21]
Equilibrium moisture content at ~50 % RH%0.51 maximum water absorption (Polymaker ABS Pro)[1]Not documented
Drying temperature & time70 °C for 6 h (ABS Max)[2]Not documented
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[23]Bubbling and popping at the nozzle, stringing and a rough surface[23]
Effect of moisture on strengthPolymaker rates ABS moderate-sensitivity and publishes no dry-versus-conditioned figures[23]Polymaker groups PETG with nylon, PVA and TPU as highly hygroscopic; no dry-versus-conditioned strength figures are published for this grade and the loss shows as bubbling and poor layer adhesion[23]
Storage requirementSealed with desiccant; Polymaker rates ABS moderate-sensitivity[23]Sealed with desiccant; Polymaker groups PETG with the highly hygroscopic materials[23][17]
Mechanical Properties
Tensile strength (XY)MPa34.9 (ABS Pro) and 35.7 (ABS Max) printed XY, ISO 527[1][2]43–44 at yield and 45–46 at break (ISO 527, injection-moulded resin data from Spectrum and Extrudr); 48 on My Tech Fun printed bars[4][5][24]
Young's modulusMPa2330 (ABS Pro) and 2320 (ABS Max) printed XY, ISO 527[1][2]Not documented
Elongation at break%6.7 (ABS Max) and 7.3 (ABS Pro) at break, printed XY, ISO 527[1][2]215–220 at break on moulded specimens (ISO 527); 4.3–4.4 at yield[4][5]
Flexural strengthMPa60.1 (ABS Pro) and 63.3 (ABS Max) printed XY, ISO 178[1][2]Not documented
Flexural modulusMPa2330 (ABS Pro) and 2500 (ABS Max) printed XY, ISO 178[1][2]Not documented
Charpy impact, notchedkJ/m²10.5 (ABS Max) and 14.5 (ABS Pro) printed XY, ISO 179, notched[1][2]93–94 notched Izod at 23 °C on moulded specimens (ISO 180); 3DXTech quotes 8 by ISO 180/A[4][5][6]
Other impact dataNot documentedIzod 4.14 kJ/m² on My Tech Fun printed bars, against 3.37 for PETG on the same rig[24]
Layer adhesion / Z tensileMPa21.9 (ABS Pro) and 25.4 (ABS Max) printed Z, ISO 527[1][2]21.6 on My Tech Fun 4×4 mm printed bars, against 32.9 for PETG[24]
Brittleness1–5Tough — absorbs impact, yields before breaking[1][2]Tough — absorbs impact, yields before breaking[4][5]
Hardness (scale-specific)Shore A / Shore D / RockwellNot documented69 Shore D measured by My Tech Fun, against 72 for PETG[24]
Creep resistance / sustained load1–5Moderate — no creep test found; Tg of 115 °C (ABS Pro) and 126 °C (ABS Max) keeps room-temperature service far below softening[1][2]Below average — a 12 mm bar sagged to 19.4 mm over 5 days at 1.25 kg, slightly worse than PETG's 18.2[24]
Fatigue / repeated-flex resistance1–5Moderate — no S-N curve found; 6.7–7.3 % elongation and 10.5–14.5 kJ/m² notched Charpy, below unfilled Bambu Lab ABS[1][2][25]Good — 215 % elongation at break and 94 kJ/m² notched Izod on moulded specimens (Extrudr, Spectrum)[4][5]
Elasticity / flexibility1–5Rigid[1]Slightly flexible in thin sections[24]
Z strength as % of XY%63 (ABS Pro) and 71 (ABS Max), printed[1][2]Not documented
Thermal Properties
HDT at 0.45 MPa°C106.4 (ABS Pro) and 118.1 (ABS Max), ISO 75 at 0.45 MPa[1][2]Not documented
HDT at 1.8 MPa°C101.4 (ABS Pro) and 113.1 (ABS Max), ISO 75 at 1.8 MPa[1][2]Not documented
Glass transition (Tg)°C114.9 (ABS Pro) and 126.3 (ABS Max), DSC[1][2]78 (3DXTech, DSC)[6]
Melting point / Vicat°CAmorphous — no melting point; Vicat 116.1 (ABS Pro) and 127.4 (ABS Max), ISO 306[1][2]Amorphous — no melting point; Vicat 88 (Spectrum, Extrudr)[4][5]
Continuous service temperature°CNot documented68 — loaded bars begin to move at this temperature, against 65 for PETG[24]
Thermal expansion (CTE)µm/m·K86–89 for printed unfilled ABS (fibre Bragg grating, 25–50 °C); no grade-specific measurement published[26]Not documented
Flammability / UL 94Not documentedFlammable; no UL 94 rating published for standard grades[27]
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement[19]Not documented
Chemical resistanceGood against weak acids, weak alkalis, oils and grease; dissolved by acetone[3]Withstands acids, alkalis, oils and UV exposure[17]
Water / humidity resistance in service1–5Not documentedGood — minor absorption; Spectrum describes the polymer as hydrophobic[4]
Food contactNot food safe — Polymaker cites potential chemical leaching[19]Not certified for food contact as filament[17]
Biodegradability / compostabilityNot biodegradable[19]Not biodegradable[17]
RecyclabilityMechanically recyclable but not accepted in household plastic collection[19]Not accepted in household plastic collection[17]
Electrical & ESD propertiesNot documentedSurface resistance above 10¹³ ohm/sq — insulating (3DXTech, ASTM D257)[6]
Health & Safety
Fume toxicity1–5High — hazardous VOC such as styrene; enclosure and filtration needed[28][14]Moderate — measurable VOCs and UFPs, ventilation advised[28]
VOC emission rateµg/min12–113 styrene, the dominant VOC from every ABS and HIPS combination tested[28]Not documented
Ultrafine-particle emission rateparticles/min2 × 10¹⁰ to 9 × 10¹⁰ median across all ABS printers, two orders of magnitude above PLA's ≈1 × 10⁸[28]Not documented
Hazardous species emittedStyrene dominates. Bambu Lab states ABS and ASA release harmful gases such as styrene at printing temperature, which can be toxic and cause dizziness or nausea[28][14]Not documented
Ventilation / filtration requirement1–5Enclosure with carbon and HEPA filtration — an enclosure alone cut measured UFP by only about 35 %[28][14]Open a window / occasional ventilation[28]
Post-Processing
Sanding & machiningSands well and takes filler before painting[19]Sands poorly — the material is tough and gums rather than powders[22]
Painting & finishingPaints readily after light abrasion[19]Not documented
Gluing & solvent weldingNot documentedCyanoacrylate; no common solvent welds PETG cleanly[22]
Vapour / chemical smoothingAcetone vapour smoothing works[3]No practical vapour smoothing[22]
Support material pairingHIPS breaks away or dissolves in d-limonene; Bambu Lab sells a dedicated Support for ABS[29][14]Prints its own supports; Polymaker rates PolyDissolve S1 for PETG[22]
Dimensional accuracy & detailNot documentedOptical clarity is the selling point; Extrudr recommends a layer height at most 50 % of nozzle diameter[5]
Solvents & Solubility
Soluble inAcetone dissolves it — the basis of ABS slurry; so do MEK, THF, ethyl acetate, chloroform, dichloromethane and toluene.[30][3]No common workshop solvent; Eastman's CHDM copolyester data shows 1,2-dichloroethane destroying it within a week.[31]
Softened or crazed byPetrol and perchloroethylene soften it and benzene attacks it; d-limonene disrupts layer adhesion in some ABS and ASA grades.[30][32]Acetone, ethyl acetate, toluene and DMF swell and soften the copolyester; methanol crazes it (Eastman, 1 y at 23 °C).[31]
Solvent welding & smoothing agentAcetone: about 20 min of vapour at 80 °C over 5 mm of liquid. Prusa measured layer adhesion more than doubled.[33]Dichloromethane brushed on is the only agent that smooths PETG — a controlled carcinogen, not workshop stock.[33]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Polymaker ABS Pro Technical Data Sheet V1 (2026-05-29) Polymaker · 2026-05 · tds
  2. Polymaker ABS Max Technical Data Sheet V1.1 (2026-06-01) Polymaker · 2026-06 · tds
  3. PolyLite ABS Technical Data Sheet (V5.5 served at this URL) Polymaker · 2024-11 · tds
  4. Spectrum Premium PCTG Technical Data Sheet Spectrum Filaments · 2026-08 · tds
  5. Extrudr PCTG technical data Extrudr · 2026-08 · tds
  6. MAX-G PCTG Technical Data Sheet 3DXTech · 2026-08 · tds
  7. Polymaker product catalogue Polymaker · 2026-08 · vendor
  8. Push Plastic product catalogue Push Plastic · 2026-08 · vendor
  9. Proto-pasta product catalogue Proto-pasta · 2026-08 · vendor
  10. SUNLU E-ABS (Easy ABS) 3D Printer Filament 1 kg SUNLU · 2026-08 · vendor
  11. YXPOLYER ABS Enhanced product page YXPOLYER · 2026-08 · vendor
  12. CHCKX 10KG Multicolor PCTG Filament bundle CHCKX (Amazon US) · 2026-08 · vendor
  13. Atomic Filament product catalogue Atomic Filament · 2026-08 · vendor
  14. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  15. ABS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  16. Prusament PETG Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  17. PETG — material basics Polymaker Wiki · 2026-08 · doc
  18. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  19. ABS — material basics Polymaker Wiki · 2026-08 · doc
  20. Filament Material Guide Prusa Knowledge Base · 2026-08 · doc
  21. MAX-G PCTG — product page (print recommendations) 3DXTech · 2026-08 · doc
  22. PET and PETG — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  23. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  24. PCTG vs PETG comparison — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  25. Bambu Filament Technical Data Sheet V3.0 — ABS Bambu Lab · 2026-08 · tds
  26. Characterization of Thermal Expansion Coefficient of 3D Printing Polymeric Materials Using Fiber Bragg Grating Sensors Materials 17(18):4668 · 2024-09 · paper
  27. Prusament PETG V0 Technical Datasheet Prusa Polymers · 2026-08 · tds
  28. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  29. HIPS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  30. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  31. Eastman Spectar copolyester — Chemical resistance (unstressed bars, 1 year at 23 °C) Eastman Chemical Company · 2026-08 · tds
  32. HIPS — Knowledge Base Prusa Research · 2026-08 · doc
  33. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc