3D Printing Info

Filament comparison

ABS+ vs PA6/66

Compare printing settings, strength, heat resistance, dated prices and sources.

ABS+ / Tough ABS guidePA66 (Nylon 66) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore ABS+ comparisonsMore PA6/66 comparisons
ABS+ vs PA6/66 — documented properties and sources
PropertyABS+ / Tough ABSABSPA66 (Nylon 66)PA
Market snapshot
Listing priceUSD/kg; dated snapshots$26.49/kg median; $15.99–$29.99/kg across 4 dated product listingsNot documented
Identity & Market
Base polymer / chemistryABS reformulated for lower warping and a higher glass transition; Polymaker's ABS Pro and ABS Max reach Tg 114.9 and 126.3 °C against 101 °C for PolyLite ABS[1][2][3]Polyamide 66, condensed from hexamethylenediamine and adipic acid; melts around 40 °C above PA6[4]
Densityg/cm³1.04 (ABS Pro) and 1.06 (ABS Max), ISO 1183[1][2]1.14 (extruded unfilled PA66 stock)[5]
Typical priceUSD/kg1 kg spools cluster near 27[6]Not documented
Price range across brandsUSD/kg16–30 across brands; SUNLU E-ABS 16, Polymaker ABS Pro 25, YXPOLYER ABS Enhanced 28, Polymaker ABS Max 30[6][7][8]Not documented
Market availability1–5Available from several mainstream brands[6]Special order, 1–2 makers worldwide — no unfilled PA66 filament appeared in any catalogue searched, and the 3DXTech nylon range offers PA6, PA12 and a 6/66 copolymer but no straight PA66[9][6]
Spool sizes & diameters1.75 and 2.85 mm; 1 kg spools[6]Not documented
Typical applicationsLarge enclosure and automotive parts where plain ABS warps or softens too early[1][2]Not documented
Printing Parameters
Nozzle temperature°C270–290 (ABS Pro); 270–300 (ABS Max) — 25–35 °C above plain ABS[1][2]Not documented
Bed temperature°C120 (ABS Max)[2]Not documented
Enclosure / chamber requirement1–5Enclosure required (passive)[1][2][10]Enclosure required (passive)[4]
Bed surface & adhesion aidClean the plate and apply glue; Simplify3D also lists Kapton tape and ABS slurry[10][11]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/sUp to 250 mm/s (ABS Pro) and 200 mm/s (ABS Max), equivalent to 20 and 16 on a 0.4 mm nozzle at 0.2 mm layer[1][2][12]Not documented
Warping tendency1–5High — enclosure needed for reliable large parts[10]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[10]Not documented
Stringing / oozing tendency1–5Slight — Polymaker advises 1–2 mm retraction at 20–30 mm/s[13]Not documented
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; the hotter nozzle rules out PTFE-lined hotends[1][2]Advanced — enclosure, hardware upgrades, tuning[4]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely[10]Not documented
Abrasiveness1–5Non-abrasive[10]Not documented
Nozzle clog risk1–5Low — unfilled ABS compound; no special hot-end required and clogging is not among the listed drawbacks[11][14]Very high — frequent jams without careful setup[15][16]
Heat-creep / jam sensitivity1–5Slightly sensitive[11]Not documented
Hotend requirementNo special hot-end required[11]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — 0.51 % maximum water absorption (ABS Pro)[1]Very high (>2 %)[16]
Equilibrium moisture content at ~50 % RH%0.51 maximum water absorption (Polymaker ABS Pro)[1]8.5 at saturation on extruded PA66 stock (ASTM D570) — the highest uptake of any polymer in this dataset[5]
Drying temperature & time70 °C for 6 h (ABS Max)[2]Not documented
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[16]Not documented
Effect of moisture on strengthPolymaker rates ABS moderate-sensitivity and publishes no dry-versus-conditioned figures[16]Measured dry against wet on printed specimens at 6.16 % moisture (Polymaker CoPA): tensile 78.0 → 34.3 MPa, Young's modulus 2703 → 724 MPa, flexural strength 109.8 → 22.6 MPa, while notched Charpy rises 6.9 → 27.7 kJ/m² and elongation 12.7 → 13.2 %[17][15]
Storage requirementSealed with desiccant; Polymaker rates ABS moderate-sensitivity[16]Not documented
Mechanical Properties
Tensile strength (XY)MPa34.9 (ABS Pro) and 35.7 (ABS Max) printed XY, ISO 527[1][2]82.7 at yield and 84.8 at break on extruded PA66 stock (ASTM D638; converted from 12,000 and 12,300 psi) — no printed figure exists because no unfilled PA66 filament was found[5]
Young's modulusMPa2330 (ABS Pro) and 2320 (ABS Max) printed XY, ISO 527[1][2]2413 on extruded PA66 stock (ASTM D638; converted from 350,000 psi)[5]
Elongation at break%6.7 (ABS Max) and 7.3 (ABS Pro) at break, printed XY, ISO 527[1][2]50 at break on extruded PA66 stock (ASTM D638)[5]
Flexural strengthMPa60.1 (ABS Pro) and 63.3 (ABS Max) printed XY, ISO 178[1][2]113.8 on extruded PA66 stock (ASTM D790; converted from 16,500 psi)[5]
Flexural modulusMPa2330 (ABS Pro) and 2500 (ABS Max) printed XY, ISO 178[1][2]3034 on extruded PA66 stock (ASTM D790; converted from 440,000 psi)[5]
Charpy impact, notchedkJ/m²10.5 (ABS Max) and 14.5 (ABS Pro) printed XY, ISO 179, notched[1][2]Not documented
Other impact dataNot documentedIzod 53 J/m on extruded PA66 stock, converted from 1.0 ft-lb/in (ASTM D256)[5]
Layer adhesion / Z tensileMPa21.9 (ABS Pro) and 25.4 (ABS Max) printed Z, ISO 527[1][2]Not documented
Brittleness1–5Tough — absorbs impact, yields before breaking[1][2]Not documented
Hardness (scale-specific)Shore A / Shore D / RockwellNot documentedShore D 86 and Rockwell 85 (108) — the source does not name the scales on extruded PA66 stock (ASTM D2240, D785)[5]
Creep resistance / sustained load1–5Moderate — no creep test found; Tg of 115 °C (ABS Pro) and 126 °C (ABS Max) keeps room-temperature service far below softening[1][2]Not documented
Fatigue / repeated-flex resistance1–5Moderate — no S-N curve found; 6.7–7.3 % elongation and 10.5–14.5 kJ/m² notched Charpy, below unfilled Bambu Lab ABS[1][2][18]Excellent — living hinges viable[4]
Elasticity / flexibility1–5Rigid[1]Semi-flexible[15]
Z strength as % of XY%63 (ABS Pro) and 71 (ABS Max), printed[1][2]Not documented
Wear resistance & frictionNot documentedWear factor 200e-10 in3*min/(ft*lb*h) on extruded PA66 stock (ASTM D3702); Ensinger lists very good slide and wear properties[5]
Thermal Properties
HDT at 0.45 MPa°C106.4 (ABS Pro) and 118.1 (ABS Max), ISO 75 at 0.45 MPa[1][2]232 on extruded PA66 stock (ASTM D648 at 66 psi; converted from 450 °F)[5]
HDT at 1.8 MPa°C101.4 (ABS Pro) and 113.1 (ABS Max), ISO 75 at 1.8 MPa[1][2]90 on extruded PA66 stock (ASTM D648 at 264 psi; converted from 194 °F) — the gap to the 0.45 MPa figure is the widest in the dataset[5]
Glass transition (Tg)°C114.9 (ABS Pro) and 126.3 (ABS Max), DSC[1][2]Not documented
Melting point / Vicat°CAmorphous — no melting point; Vicat 116.1 (ABS Pro) and 127.4 (ABS Max), ISO 306[1][2]255 melting on extruded PA66 stock (ASTM D2133; converted from 491 °F)[5]
Continuous service temperature°CNot documented85 long term and 149 short term on extruded PA66 stock (converted from 185 °F and 300 °F)[5]
Thermal expansion (CTE)µm/m·K86–89 for printed unfilled ABS (fibre Bragg grating, 25–50 °C); no grade-specific measurement published[19]81.0 (extruded PA66 stock, ASTM D696; source states 4.5e-5 in/in/°F)[5]
Flammability / UL 94Not documentedUL 94 V-2 on extruded PA66 stock[5]
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement[13]Not documented
Chemical resistanceGood against weak acids, weak alkalis, oils and grease; dissolved by acetone[3]Not documented
Food contactNot food safe — Polymaker cites potential chemical leaching[13]Not documented
Biodegradability / compostabilityNot biodegradable[13]Not documented
RecyclabilityMechanically recyclable but not accepted in household plastic collection[13]Not documented
Electrical & ESD propertiesNot documentedVolume resistance 1e15 ohm-cm and dielectric constant 4 on extruded PA66 stock (ASTM D257, D150)[5]
Health & Safety
Fume toxicity1–5High — hazardous VOC such as styrene; enclosure and filtration needed[20][10]Moderate — measurable VOCs and UFPs, ventilation advised[20]
VOC emission rateµg/min12–113 styrene, the dominant VOC from every ABS and HIPS combination tested[20]Up to 180 caprolactam, the dominant VOC from nylon; total VOC reached nearly 200 µg/min, the highest of the nine filaments tested[20]
Ultrafine-particle emission rateparticles/min2 × 10¹⁰ to 9 × 10¹⁰ median across all ABS printers, two orders of magnitude above PLA's ≈1 × 10⁸[20]≈2 × 10⁸ median — low for ultrafine particles despite the highest VOC mass of any filament tested[20]
Hazardous species emittedStyrene dominates. Bambu Lab states ABS and ASA release harmful gases such as styrene at printing temperature, which can be toxic and cause dizziness or nausea[20][10]Caprolactam, at up to 180 µg/min from nylon filament — the largest single-VOC emission rate measured in the study[20]
Ventilation / filtration requirement1–5Enclosure with carbon and HEPA filtration — an enclosure alone cut measured UFP by only about 35 %[20][10]Ventilated room or enclosure recommended[20]
Post-Processing
Sanding & machiningSands well and takes filler before painting[13]Not documented
Painting & finishingPaints readily after light abrasion[13]Not documented
Vapour / chemical smoothingAcetone vapour smoothing works[3]Not documented
Support material pairingHIPS breaks away or dissolves in d-limonene; Bambu Lab sells a dedicated Support for ABS[21][10]Not documented
Solvents & Solubility
Soluble inAcetone dissolves it — the basis of ABS slurry; so do MEK, THF, ethyl acetate, chloroform, dichloromethane and toluene.[22][3]Dissolved at 23 °C by formic acid above ~80 %, phenol, m-cresol, 96 % sulphuric acid or hexafluoroisopropanol — laboratory reagents.[23]
Softened or crazed byPetrol and perchloroethylene soften it and benzene attacks it; d-limonene disrupts layer adhesion in some ABS and ASA grades.[22][24]Zinc chloride solutions stress-crack it — 10 % marginal, 37 % not resistant; alcoholic calcium chloride dissolves it.[23]
Solvent welding & smoothing agentAcetone: about 20 min of vapour at 80 °C over 5 mm of liquid. Prusa measured layer adhesion more than doubled.[25]None — nylon's only solvents are formic acid, phenol and HFIP, all of which degrade the part they wet.[23]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Polymaker ABS Pro Technical Data Sheet V1 (2026-05-29) Polymaker · 2026-05 · tds
  2. Polymaker ABS Max Technical Data Sheet V1.1 (2026-06-01) Polymaker · 2026-06 · tds
  3. PolyLite ABS Technical Data Sheet (V5.5 served at this URL) Polymaker · 2024-11 · tds
  4. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  5. TECAMID 66 natural (PA66) — stock shape properties Ensinger · 2026-08 · tds
  6. Polymaker product catalogue Polymaker · 2026-08 · vendor
  7. SUNLU E-ABS (Easy ABS) 3D Printer Filament 1 kg SUNLU · 2026-08 · vendor
  8. YXPOLYER ABS Enhanced product page YXPOLYER · 2026-08 · vendor
  9. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  10. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  11. ABS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  12. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  13. ABS — material basics Polymaker Wiki · 2026-08 · doc
  14. Filament Material Guide Prusa Knowledge Base · 2026-08 · doc
  15. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  16. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  17. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  18. Bambu Filament Technical Data Sheet V3.0 — ABS Bambu Lab · 2026-08 · tds
  19. Characterization of Thermal Expansion Coefficient of 3D Printing Polymeric Materials Using Fiber Bragg Grating Sensors Materials 17(18):4668 · 2024-09 · paper
  20. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  21. HIPS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  22. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  23. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  24. HIPS — Knowledge Base Prusa Research · 2026-08 · doc
  25. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc