3D Printing Info

Filament comparison

ABS-GF vs Breakaway

Compare printing settings, strength, heat resistance, dated prices and sources.

Glass-fibre ABS (ABS-GF) guideBreak-away support guide

2 selected · all documented properties

Open these two in the interactive comparisonMore ABS-GF comparisonsMore Breakaway comparisons
ABS-GF vs Breakaway — documented properties and sources
PropertyGlass-fibre ABS (ABS-GF)ABSBreak-away supportSUPPORT
Market snapshot
Listing priceUSD/kg; dated snapshots$34.99/kg median; $24.49–$73.33/kg across 4 dated product listings$42.49/kg median; $26.00–$79.98/kg across 4 dated product listings
Identity & Market
Base polymer / chemistryABS reinforced with chopped glass fibre — 3DXTech's grade is nominally 10 wt%[1][2]Break-away support compounds matched to a specific model material — Polymaker sells separate grades for PLA and for PA12[3][4]
Densityg/cm³1.08 (Bambu Lab) and 1.15 (3DXTech), ISO 1183[2][1]1.22 (PolySupport for PLA) and 1.29 (PolySupport for PA12), ISO 1183[3][4]
Typical priceUSD/kg1 kg-equivalent spools span 24–73; the middle of the market is about 35[5][6][7][8]1 kg-equivalent spools span 26–80; the middle of the market is about 45[9][10][11]
Price range across brandsUSD/kg24–73 across brands; Siraya Tech 24, Bambu Lab 30, SUNLU 40, 3DXTech 73[5][6][7][8]26–80 across brands and grades; IEMAI 3D E-REMOVE 26, Polymaker PolySupport for PLA 40 at 750 g, YXPOLYER 45, PolySupport for PA12 80 at 500 g[9][10][11]
Market availability1–5Available from several mainstream brands[5][6]Available from several mainstream brands[9][6]
Spool sizes & diameters1.75 and 2.85 mm; 750 g and 1 kg spools[6][5]1.75 and 2.85 mm; 0.5 and 0.75 kg spools[9]
Typical applicationsStiff, dimensionally stable enclosure and tooling parts; Bambu Lab notes the fibre blurs layer lines into a matte finish[2]Support that peels off by hand, avoiding the moisture handling and dissolution time that soluble supports demand[3]
Printing Parameters
Nozzle temperature°C240–280 (Bambu Lab)[2]220–230 (PolySupport for PLA)[3]
Bed temperature°C80–100 (Bambu Lab)[2]25–60 (PolySupport for PLA)[3]
Enclosure / chamber requirement1–5Enclosure recommended — Bambu Lab specifies a 45–60 °C chamber[2][12]Open frame is fine[3]
Recommended chamber temperature°C45–60 (Bambu Lab)[2]Not documented
Part cooling fan0–80 % (Bambu Lab)[2]Not documented
Bed surface & adhesion aidClean the plate and apply glue; Simplify3D also lists Kapton tape and ABS slurry[12][13]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s14 at Bambu Lab's 180 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[2][14]4–12 at Polymaker's 50–150 mm/s on a 0.4 mm nozzle at 0.2 mm layer[3]
Warping tendency1–5Moderate — needs adhesion aid or draught shield; Bambu Lab positions the fibre as reducing warping[2]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[12]Not documented
Stringing / oozing tendency1–5Slight — Polymaker advises 1–2 mm retraction at 20–30 mm/s[15]Not documented
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; hardened nozzle mandatory[12]Easy — minor profile tuning[3]
Extruder requirementNot documentedA second extruder or a tool changer[3]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required[12]Brass fine indefinitely[3]
Abrasiveness1–5Highly abrasive — standard GF composite[12]Non-abrasive[3]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech specifies a hardened 0.4 mm minimum nozzle and 0.25 mm layers or higher for the glass-filled grade[16][17]Moderate — needs dry filament and a clean nozzle; Polymaker specifies a 55 °C dry for the PLA grade and warns brass nozzle life falls to about 9 h on the PA12 grade[3][4]
Heat-creep / jam sensitivity1–5Slightly sensitive[13]Not documented
Hotend requirementNo special hot-end required[13]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — 0.53 % saturated at 25 °C / 55 % RH (Bambu Lab)[2]Moderate — 0.64 % equilibrium water absorption (PolySupport for PLA)[3]
Equilibrium moisture content at ~50 % RH%0.53 saturated at 25 °C / 55 % RH (Bambu Lab)[2]0.64 equilibrium water absorption (Polymaker PolySupport for PLA)[3]
Drying temperature & time80 °C for 8 h (Bambu Lab)[2]Not documented
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[18]Not documented
Effect of moisture on strengthPolymaker rates ABS moderate-sensitivity and publishes no dry-versus-conditioned figures; absorbed water flashes to steam in the hotend and shows as bubbling and poor layer adhesion[18]Not a structural material; no dry-versus-conditioned data is published[18]
Storage requirementSealed with desiccant; Polymaker rates ABS moderate-sensitivity[18]Not documented
Mechanical Properties
Tensile strength (XY)MPa36 ± 3 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 68 at break[2][1]Not documented
Young's modulusMPa3160 ± 170 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 4210[2][1]Not documented
Elongation at break%6.3 ± 1.2 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 2 at break[2][1]Not documented
Flexural strengthMPa68 ± 4 printed XY, ISO 178 (Bambu Lab); 3DXTech quotes 70[2][1]Not documented
Flexural modulusMPa2860 ± 130 printed XY, ISO 178 (Bambu Lab); 3DXTech quotes 4420[2][1]Not documented
Charpy impact, notchedkJ/m²4.2 ± 1.1 printed XY, ISO 179, notched (Bambu Lab)[2]Not documented
Other impact dataCharpy unnotched 14.5 ± 1.5 printed XY (Bambu Lab, ISO 179)[2]Not documented
Layer adhesion / Z tensileMPa29 ± 3 printed Z, ISO 527 (Bambu Lab)[2]Not documented
Brittleness1–5Brittle — snaps with little warning; notched Charpy falls from 21.5 to 4.2 kJ/m² against unfilled Bambu Lab ABS[2][19]Not documented
Creep resistance / sustained load1–5Good — no creep test found; chopped glass fibre lifts modulus to 3160 MPa against 2200 for unfilled Bambu Lab ABS[2][19]Not documented
Fatigue / repeated-flex resistance1–5Below average — no S-N curve found; notched Charpy falls to 4.2 kJ/m² against 21.5 for unfilled Bambu Lab ABS[2][19]Not documented
Elasticity / flexibility1–5Rigid[2]Not documented
Z strength as % of XY%81 (Bambu Lab, printed Z against XY tensile)[2]Not documented
Thermal Properties
HDT at 0.45 MPa°C99 (ISO 75, 0.45 MPa, Bambu Lab) against 87 for unfilled Bambu Lab ABS[2][19]43 (ISO 75, 0.45 MPa, PolySupport for PA12). Polymaker's sheet prints a higher figure at the higher load, which is physically inverted; treat both HDT numbers as approximate[4]
HDT at 1.8 MPa°C88 (ISO 75, 1.8 MPa, Bambu Lab) against 84 for unfilled Bambu Lab ABS[2][19]53 (ISO 75, 1.8 MPa, PolySupport for PA12) — printed above the 0.45 MPa figure on Polymaker's own sheet, which cannot be right; treat both as approximate[4]
Melting point / Vicat°CNot documentedVicat 171 (PolySupport for PA12, ISO 306)[4]
Environment & Chemical
Chemical resistanceGood against weak acids, weak alkalis, oils and grease; dissolved by acetone[20]Not documented
Food contactNot food safe — Polymaker cites potential chemical leaching[15]Not documented
Biodegradability / compostabilityNot biodegradable[15]Not documented
RecyclabilityMechanically recyclable but not accepted in household plastic collection[15]Not documented
Electrical & ESD propertiesNot documentedSurface resistance above 10^13 ohm/sq (ASTM D257, THERMAX HTS2 and MTS1)[21][22]
Health & Safety
Fume toxicity1–5High — hazardous VOC such as styrene; enclosure and filtration needed[23][12]Low hazard — minimal VOC and particle emission; none of these materials was in the chamber study[23]
VOC emission rateµg/min12–113 styrene, the dominant VOC from every ABS and HIPS combination tested[23]Not documented
Ultrafine-particle emission rateparticles/min2 × 10¹⁰ to 9 × 10¹⁰ median across all ABS printers, two orders of magnitude above PLA's ≈1 × 10⁸[23]Not documented
Hazardous species emittedStyrene dominates. Bambu Lab states ABS and ASA release harmful gases such as styrene at printing temperature, which can be toxic and cause dizziness or nausea[23][12]Not documented
Ventilation / filtration requirement1–5Enclosure with carbon and HEPA filtration — an enclosure alone cut measured UFP by only about 35 %[23][12]Open a window / occasional ventilation[23]
Dust & fibre handling hazardGlass fibre is bound in the matrix; avoid inhaling sanding dust[1]Not documented
Post-Processing
Sanding & machiningSands well and takes filler before painting[15]Not documented
Painting & finishingPaints readily after light abrasion[15]Not documented
Support material pairingHIPS breaks away or dissolves in d-limonene; Bambu Lab sells a dedicated Support for ABS[24][12]This is the support material. Polymaker publishes an adhesion matrix per model material, from very good to unusable, because break-away supports only work against the polymer they were matched to[3][4]
Dimensional accuracy & detailBambu Lab describes a smooth matte finish with micro-spot gloss that blurs layer lines[2]Not documented
Solvents & Solubility
Soluble inAcetone dissolves the resin and leaves the fibre as sludge; MEK, THF, ethyl acetate and chlorinated solvents do the same.[25][20]None — break-away support is removed mechanically; 3DXTech lists no water or solvent route for it.[26]
Softened or crazed byPetrol and perchloroethylene soften it and benzene attacks it; d-limonene disrupts layer adhesion in some ABS and ASA grades.[25][27]Not documented
Solvent welding & smoothing agentAcetone vapour reaches only the resin fraction, so the fibre is left standing proud of the smoothed surface.[28][20]None — there is no solvent to weld or smooth with.[26]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. FibreX ABS+GF10 Glass Fiber ABS Technical Data Sheet 3DXTech · 2026-08 · tds
  2. Bambu Filament Technical Data Sheet V1.0 — ABS-GF Bambu Lab · 2026-08 · tds
  3. PolySupport Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  4. PolySupport for PA12 Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  5. ABS-GF — product page Bambu Lab US Store · 2026-08 · vendor
  6. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  7. Siraya Tech Fibreheart ABS-GF Filament product page Siraya Tech · 2026-08 · vendor
  8. SUNLU ABS-GF (ABS Glass Fiber) 3D Printer Filament 1 kg SUNLU · 2026-08 · vendor
  9. Polymaker product catalogue Polymaker · 2026-08 · vendor
  10. YXPOLYER Breakaway Support Filament 1 kg Black — product page YXPOLYER · 2026-08 · vendor
  11. IEMAI 3D E-REMOVE breakaway support filament — store page IEMAI 3D · 2026-08 · vendor
  12. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  13. ABS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  14. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  15. ABS — material basics Polymaker Wiki · 2026-08 · doc
  16. FIBREX ABS+GF — product page (print recommendations) 3DXTech · 2026-08 · doc
  17. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  18. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  19. Bambu Filament Technical Data Sheet V3.0 — ABS Bambu Lab · 2026-08 · tds
  20. PolyLite ABS Technical Data Sheet (V5.5 served at this URL) Polymaker · 2024-11 · tds
  21. THERMAX HTS2 Break Away Support Technical Data Sheet v1.0 3DXTech · 2026-08 · tds
  22. THERMAX MTS1 Break Away Support Technical Data Sheet v1.0 3DXTech · 2026-08 · tds
  23. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  24. HIPS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  25. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  26. THERMAX HTS1 — product page 3DXTech · 2026-08 · vendor
  27. HIPS — Knowledge Base Prusa Research · 2026-08 · doc
  28. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc