3D Printing Info

Filament comparison

ABS-GF vs PP

Compare printing settings, strength, heat resistance, dated prices and sources.

Glass-fibre ABS (ABS-GF) guidePolypropylene (PP) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore ABS-GF comparisonsMore PP comparisons
ABS-GF vs PP — documented properties and sources
PropertyGlass-fibre ABS (ABS-GF)ABSPolypropylene (PP)POLYOLEFIN
Market snapshot
Listing priceUSD/kg; dated snapshots$34.99/kg median; $24.49–$73.33/kg across 4 dated product listings$46.56/kg median; $31.99–$53.00/kg across 4 dated product listings
Identity & Market
Base polymer / chemistryABS reinforced with chopped glass fibre — 3DXTech's grade is nominally 10 wt%[1][2]Polypropylene — a semi-crystalline polyolefin with no polar groups, so it neither absorbs water nor bonds to most bed surfaces[3][4]
Densityg/cm³1.08 (Bambu Lab) and 1.15 (3DXTech), ISO 1183[2][1]0.91 (Prusa PP composite, ISO 1183) — the lightest common filament[5]
Typical priceUSD/kg1 kg-equivalent spools span 24–73; the middle of the market is about 35[6][7][8][9]1 kg-equivalent spools span 27–53; the middle of the market is about 44[10][11][12][13]
Price range across brandsUSD/kg24–73 across brands; Siraya Tech 24, Bambu Lab 30, SUNLU 40, 3DXTech 73[6][7][8][9]27–53 across brands; Reli3D 32 on Amazon, SUNLU 44 at 0.8 kg, Fiberlogy 49 at 750 g, IEMAI 3D 53, and the 3DJake PP listing spans 27–49[10][14][11][12][13]
Market availability1–5Available from several mainstream brands[6][7]Available from several mainstream brands[14][11][10]
Spool sizes & diameters1.75 and 2.85 mm; 750 g and 1 kg spools[7][6]1.75 and 2.85 mm; 0.75 kg spools are common[11]
Typical applicationsStiff, dimensionally stable enclosure and tooling parts; Bambu Lab notes the fibre blurs layer lines into a matte finish[2]Living hinges, chemical-resistant containers, automotive clips and packaging prototypes[3]
Printing Parameters
Nozzle temperature°C240–280 (Bambu Lab)[2]210–230 (Braskem-type PE/PP window); Formfutura's Centaur PP melts at 205 ± 15 °C[3]
Bed temperature°C80–100 (Bambu Lab)[2]Not documented
Enclosure / chamber requirement1–5Enclosure recommended — Bambu Lab specifies a 45–60 °C chamber[2][15]Enclosure recommended — Simplify3D lists an enclosure as a hardware requirement and Polymaker advises one below 70 °C ambient to stop warping and cracking[16][4]
Recommended chamber temperature°C45–60 (Bambu Lab)[2]Not documented
Part cooling fan0–80 % (Bambu Lab)[2]Part cooling fan required (Simplify3D)[16]
Bed surface & adhesion aidClean the plate and apply glue; Simplify3D also lists Kapton tape and ABS slurry[15][17]Packing tape, a polypropylene sheet, or a PP-specific adhesive such as Magigoo PP — ordinary PLA and ABS adhesives do not hold it[16][4]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s14 at Bambu Lab's 180 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[2][18]Not documented
Warping tendency1–5Moderate — needs adhesion aid or draught shield; Bambu Lab positions the fibre as reducing warping[2]High — enclosure needed for reliable large parts; PP's crystallinity drives shrinkage and Prusa recommends a brim on its PP grades[5][19]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[15]Very difficult — special plates or slurry required. PP bonds to almost nothing; a polypropylene-specific tape or adhesive is the normal answer[5][4]
Stringing / oozing tendency1–5Slight — Polymaker advises 1–2 mm retraction at 20–30 mm/s[20]Slight — Polymaker advises 1–2 mm retraction at 20–30 mm/s[4]
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; hardened nozzle mandatory[15]Advanced — enclosure, hardware upgrades, tuning; bed adhesion is the whole problem[4][5]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required[15]Brass fine indefinitely for unfilled grades — Simplify3D states no special hotend is required[16]
Abrasiveness1–5Highly abrasive — standard GF composite[15]Non-abrasive when unfilled[16]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech specifies a hardened 0.4 mm minimum nozzle and 0.25 mm layers or higher for the glass-filled grade[21][22]Low — Simplify3D lists no special hotend requirement for PP and clogging is not among its listed drawbacks[23][16]
Heat-creep / jam sensitivity1–5Slightly sensitive[17]Slightly sensitive[16]
Hotend requirementNo special hot-end required[17]No special hot-end required (Simplify3D)[16]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — 0.53 % saturated at 25 °C / 55 % RH (Bambu Lab)[2]Negligible (<0.1 % EMC) — Prusa measures 0.03 % in 24 h and 0.04 % in 7 days on its PP composite, the lowest figures it publishes for any filament[5]
Equilibrium moisture content at ~50 % RH%0.53 saturated at 25 °C / 55 % RH (Bambu Lab)[2]0.03 after 24 h and 0.04 after 7 days at 24 °C / 22 % RH (Prusa Polymers, measured on its PP composite)[5]
Drying temperature & time80 °C for 8 h (Bambu Lab)[2]No drying step is published for PP; uptake is below the level that affects printing[5]
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[23]Bubbling and popping at the nozzle; Polymaker still advises a 70 °C dry for 4–6 h despite the low uptake[4]
Effect of moisture on strengthPolymaker rates ABS moderate-sensitivity and publishes no dry-versus-conditioned figures; absorbed water flashes to steam in the hotend and shows as bubbling and poor layer adhesion[23]Not applicable in practice — with equilibrium uptake at 0.04 %, there is no moisture-driven strength loss to measure. Polymaker's sensitivity tiers put polyolefins below even PLA[5][23]
Storage requirementSealed with desiccant; Polymaker rates ABS moderate-sensitivity[23]No special storage needed[5]
Mechanical Properties
Tensile strength (XY)MPa36 ± 3 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 68 at break[2][1]12 at yield (Formfutura Centaur PP, ASTM D638)[3]
Young's modulusMPa3160 ± 170 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 4210[2][1]724 on extruded PP stock (ASTM D638; converted from 105,000 psi)[24]
Elongation at break%6.3 ± 1.2 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 2 at break[2][1]Above 600 at break (Formfutura Centaur PP, ASTM D638)[3]
Flexural strengthMPa68 ± 4 printed XY, ISO 178 (Bambu Lab); 3DXTech quotes 70[2][1]31.0 on extruded PP stock (ASTM D790; converted from 4500 psi)[24]
Flexural modulusMPa2860 ± 130 printed XY, ISO 178 (Bambu Lab); 3DXTech quotes 4420[2][1]402 flexural modulus (Formfutura Centaur PP, ASTM D790) — an order of magnitude below any rigid filament[3]
Charpy impact, notchedkJ/m²4.2 ± 1.1 printed XY, ISO 179, notched (Bambu Lab)[2]Not documented
Other impact dataCharpy unnotched 14.5 ± 1.5 printed XY (Bambu Lab, ISO 179)[2]Izod notched 112 J/m on extruded PP stock, converted from 2.1 ft-lb/in (ASTM D256)[24]
Layer adhesion / Z tensileMPa29 ± 3 printed Z, ISO 527 (Bambu Lab)[2]Not documented
Brittleness1–5Brittle — snaps with little warning; notched Charpy falls from 21.5 to 4.2 kJ/m² against unfilled Bambu Lab ABS[2][25]Very ductile — bends far before failing[3]
Hardness (scale-specific)Shore A / Shore D / RockwellNot documentedRockwell R102 (and M95) on extruded PP stock (ASTM D785)[24]
Creep resistance / sustained load1–5Good — no creep test found; chopped glass fibre lifts modulus to 3160 MPa against 2200 for unfilled Bambu Lab ABS[2][25]Below average[3]
Fatigue / repeated-flex resistance1–5Below average — no S-N curve found; notched Charpy falls to 4.2 kJ/m² against 21.5 for unfilled Bambu Lab ABS[2][25]Excellent — living hinges viable, the classic polypropylene application[3]
Elasticity / flexibility1–5Rigid[2]Semi-flexible[3]
Z strength as % of XY%81 (Bambu Lab, printed Z against XY tensile)[2]Not documented
Thermal Properties
HDT at 0.45 MPa°C99 (ISO 75, 0.45 MPa, Bambu Lab) against 87 for unfilled Bambu Lab ABS[2][25]74 on extruded PP stock (ASTM D648 at 66 psi; converted from 165 °F)[24]
HDT at 1.8 MPa°C88 (ISO 75, 1.8 MPa, Bambu Lab) against 84 for unfilled Bambu Lab ABS[2][25]Not documented
Melting point / Vicat°CNot documented205 ± 15 melting (Formfutura Centaur PP)[3]
Continuous service temperature°CNot documentedBounded by a melting point of 205 ± 15 °C and by the 158 °C heat deflection of the carbon-filled grade; no loaded-bar service figure is published for unfilled PP[3][5]
Flammability / UL 94Not documentedFlammable; no UL 94 rating published for the grades surveyed[5]
Environment & Chemical
UV resistance1–5Not documentedMonths outdoors before embrittlement — unstabilised polypropylene chalks under UV[4]
Chemical resistanceGood against weak acids, weak alkalis, oils and grease; dissolved by acetone[26]Excellent against acids, alkalis and most solvents — the usual reason to choose PP[4]
Water / humidity resistance in service1–5Not documentedExcellent — essentially unaffected[5]
Food contactNot food safe — Polymaker cites potential chemical leaching[20]Polypropylene is a common food-packaging polymer, but no filament here carries a food-contact certification[4]
Biodegradability / compostabilityNot biodegradable[20]Not biodegradable[4]
RecyclabilityMechanically recyclable but not accepted in household plastic collection[20]Mechanically recyclable as resin code 5, but printed waste is not accepted in household collection[4]
Health & Safety
Fume toxicity1–5High — hazardous VOC such as styrene; enclosure and filtration needed[27][15]Low hazard — minimal VOC and particle emission. Inferred: no polyolefin was among the nine filaments in the Azimi chamber study, so this is a family-level judgement rather than a measurement[27]
VOC emission rateµg/min12–113 styrene, the dominant VOC from every ABS and HIPS combination tested[27]Not documented
Ultrafine-particle emission rateparticles/min2 × 10¹⁰ to 9 × 10¹⁰ median across all ABS printers, two orders of magnitude above PLA's ≈1 × 10⁸[27]Not documented
Hazardous species emittedStyrene dominates. Bambu Lab states ABS and ASA release harmful gases such as styrene at printing temperature, which can be toxic and cause dizziness or nausea[27][15]Not documented
Ventilation / filtration requirement1–5Enclosure with carbon and HEPA filtration — an enclosure alone cut measured UFP by only about 35 %[27][15]Open a window / occasional ventilation. Inferred — no polyolefin was measured in the chamber study[27]
Dust & fibre handling hazardGlass fibre is bound in the matrix; avoid inhaling sanding dust[1]Not documented
Post-Processing
Sanding & machiningSands well and takes filler before painting[20]Sands poorly — the waxy surface loads abrasive paper[16]
Painting & finishingPaints readily after light abrasion[20]Paint and adhesives do not key to untreated PP; flame or plasma treatment is normally needed first[4]
Gluing & solvent weldingNot documentedNothing common bonds untreated PP; flame or plasma treatment is needed before adhesives key[4]
Vapour / chemical smoothingNot documentedNo practical vapour smoothing[16]
Support material pairingHIPS breaks away or dissolves in d-limonene; Bambu Lab sells a dedicated Support for ABS[28][15]Prints its own supports; no soluble support is rated for PP[16]
Dimensional accuracy & detailBambu Lab describes a smooth matte finish with micro-spot gloss that blurs layer lines[2]Shrinkage and warping dominate; the low modulus means parts flex rather than hold tolerance[5]
Solvents & Solubility
Soluble inAcetone dissolves the resin and leaves the fibre as sludge; MEK, THF, ethyl acetate and chlorinated solvents do the same.[29][26]None at room temperature; chloroform dissolves it at 60 °C and xylene at about 118 °C — the xylene-solubles route.[30][31]
Softened or crazed byPetrol and perchloroethylene soften it and benzene attacks it; d-limonene disrupts layer adhesion in some ABS and ASA grades.[29][32]Xylene, decalin, CCl4 and chlorobenzene are heavily absorbed at 20 °C; oleum, chlorosulphonic acid and bromine destroy it.[30]
Solvent welding & smoothing agentAcetone vapour reaches only the resin fraction, so the fibre is left standing proud of the smoothed surface.[33][26]None — nothing softens PP at room temperature, so joints have to be welded thermally rather than chemically.[30]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. FibreX ABS+GF10 Glass Fiber ABS Technical Data Sheet 3DXTech · 2026-08 · tds
  2. Bambu Filament Technical Data Sheet V1.0 — ABS-GF Bambu Lab · 2026-08 · tds
  3. Centaur PP Technical Data Sheet Formfutura · 2026-08 · tds
  4. PP — material basics Polymaker Wiki · 2026-08 · doc
  5. Prusament PP Carbon Fiber Technical Datasheet v1.0 Prusa Polymers · 2024-11 · tds
  6. ABS-GF — product page Bambu Lab US Store · 2026-08 · vendor
  7. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  8. Siraya Tech Fibreheart ABS-GF Filament product page Siraya Tech · 2026-08 · vendor
  9. SUNLU ABS-GF (ABS Glass Fiber) 3D Printer Filament 1 kg SUNLU · 2026-08 · vendor
  10. SUNLU product catalogue SUNLU · 2026-08 · vendor
  11. Fiberlogy PP Natural — product page 3DJake International · 2026-08 · vendor
  12. Reli3D Low Warp PP Filament 1.75 mm 1 kg Black — Amazon listing Amazon.com · 2026-08 · vendor
  13. IEMAI 3D PP 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  14. PP filament listing 3DJake International · 2026-08 · vendor
  15. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  16. Polypropylene — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  17. ABS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  18. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  19. Prusament PP Glass Fiber Technical Datasheet v1.0 Prusa Polymers · 2024-11 · tds
  20. ABS — material basics Polymaker Wiki · 2026-08 · doc
  21. FIBREX ABS+GF — product page (print recommendations) 3DXTech · 2026-08 · doc
  22. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  23. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  24. TECAFINE PP natural — stock shape properties Ensinger · 2026-08 · tds
  25. Bambu Filament Technical Data Sheet V3.0 — ABS Bambu Lab · 2026-08 · tds
  26. PolyLite ABS Technical Data Sheet (V5.5 served at this URL) Polymaker · 2024-11 · tds
  27. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  28. HIPS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  29. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  30. Pro-fax and Moplen polypropylene — Chemical Resistance Guide (20, 60 and 100 °C) LyondellBasell · 2026-08 · tds
  31. US 5,278,282 Polymer recycling by selective dissolution — xylene dissolution temperatures Nauman & Lynch, Rensselaer Polytechnic Institute · 1994-01 · paper
  32. HIPS — Knowledge Base Prusa Research · 2026-08 · doc
  33. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc