3D Printing Info

Filament comparison

ABS-CF vs PA12-CF

Compare printing settings, strength, heat resistance, dated prices and sources.

Carbon-fibre ABS (ABS-CF) guideCarbon-fibre PA12 (PA12-CF) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore ABS-CF comparisonsMore PA12-CF comparisons
ABS-CF vs PA12-CF — documented properties and sources
PropertyCarbon-fibre ABS (ABS-CF)ABSCarbon-fibre PA12 (PA12-CF)PA
Market snapshot
Listing priceUSD/kg; dated snapshots$35.99/kg median; $22.00–$125.00/kg across 7 dated product listings$109.98/kg median; $52.00–$180.00/kg across 4 dated product listings
Identity & Market
Base polymer / chemistryABS reinforced with chopped carbon fibre[1]PA12 reinforced with chopped carbon fibre — Polymaker's grade is 10 wt%[2][3]
Densityg/cm³1.11 (ISO 1183)[1]1.06 (Polymaker Fiberon) and 1.16 (3DXTech), ISO 1183[2][3]
Typical priceUSD/kg1 kg-equivalent spools span 22–125; the middle of the market is about 36[4][5][6][7][8]1 kg-equivalent spools span 52–180; the middle of the market is about 110[9][4][10]
Price range across brandsUSD/kg22–125 across brands; IEMAI 22, Siraya Tech 28 and 36 for the core-shell grade, YXPOLYER 35, Push Plastic 50 at 2 kg, 3DXTech 64 at 750 g; Stratasys-compatible cartridges run far higher[4][5][6][7][11][8]52–180 across brands; IEMAI 3D 52, YXPOLYER 80 at 500 g, Polymaker Fiberon 140, 3DXTech CarbonX 180[9][4][12][10]
Market availability1–5Available from several mainstream brands[4][5]Available from several mainstream brands[9][4]
Spool sizes & diameters1.75 and 2.85 mm; 0.5, 0.75 and 2 kg spools plus Stratasys-compatible cartridges[4][5]1.75 mm; 0.5, 0.75 and 2 kg spools[9][4]
Typical applicationsStiff tooling and fixtures that must survive above 100 °C[1]Stiff parts that must stay dimensionally stable in changing humidity — Polymaker sells this grade specifically on low moisture sensitivity[13][2]
Printing Parameters
Nozzle temperature°CNot documented260–290 (Extrudr DURAPRO PA12 CF)[14]
Bed temperature°CNot documented110 (Extrudr DURAPRO PA12 CF)[14]
Enclosure / chamber requirement1–5Enclosure recommended[15]Enclosure required (passive)[16][2]
Bed surface & adhesion aidClean the plate and apply glue; Simplify3D also lists Kapton tape and ABS slurry[15][17]PEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[18][16]
Maximum volumetric flow (mm³/s; see test conditions)mm³/sNot documented12 at Extrudr's 150 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[14][19]
Warping tendency1–5Moderate — needs adhesion aid or draught shield; the fibre reduces warping against unfilled ABS[15]Not documented
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[15]Needs a specific surface plus adhesive[18]
Stringing / oozing tendency1–5Slight — Polymaker advises 1–2 mm retraction at 20–30 mm/s[20]Moderate — retraction tuning needed[16]
Overall printing difficulty1–5Intermediate — dry filament and a tuned profile; hardened nozzle mandatory[15]Advanced — enclosure, hardware upgrades, tuning[16]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required[15]Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA12-CF10 and recommends hardened steel or ruby[2]
Abrasiveness1–5Highly abrasive — standard CF composite[15]Highly abrasive — standard CF composite; Polymaker puts brass nozzle life at roughly 9 h on PA12-CF10[2]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech specifies a hardened nozzle of 0.4 mm minimum and 0.25 mm layers or higher, and Prusa lists composites as a higher clogging risk[21][22][23]High — jams from moisture, heat creep or particles[24]
Heat-creep / jam sensitivity1–5Slightly sensitive[17]Moderate — good heatbreak cooling needed[18]
Hotend requirementNo special hot-end required[17]May require an all-metal hot end (Simplify3D)[18]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Moderate — the ABS matrix takes up 0.51–0.65 % saturated at 25 °C / 55 % RH and 3DXTech specifies a 80 °C, 4 h pre-dry[25][26][21]High (0.8–2 %) — 1.5 % equilibrium, the lowest of Polymaker's nylon composites and less than half its PA6-GF25[2][27]
Equilibrium moisture content at ~50 % RH%Not documented1.5 equilibrium water absorption (Polymaker Fiberon PA12-CF10)[2]
Drying temperature & timeNot documented80–100 °C; storage below 20 % RH[24][2]
Symptoms when wetBubbling and popping at the nozzle, stringing and a rough surface[24]Not documented
Effect of moisture on strengthPolymaker rates ABS moderate-sensitivity and publishes no dry-versus-conditioned figures; absorbed water flashes to steam in the hotend and shows as bubbling and poor layer adhesion[24]Polymaker's own dry/wet blocks for PA12-CF10 change little: at 2.92 % moisture tensile falls 77.4 → 71.7 MPa and modulus 3311 → 3132 MPa, against a halving for its PA6 grades[2][13]
Storage requirementSealed with desiccant; Polymaker rates ABS moderate-sensitivity[24]Sealed below 20 % RH with desiccant[24]
Hydrolysis at melt temperatureNot documentedPolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[28][29]
Mechanical Properties
Tensile strength (XY)MPa46 at break (printed XY, ISO 527)[1]77.4 ± 1.1 printed XY dry (Polymaker Fiberon), 71.7 ± 0.7 conditioned to 2.92 % moisture, ISO 527; 3DXTech quotes 72 at break. Stratasys FDM Nylon 12CF spans 76.5-124 at break printed XZ across five machine and tip combinations (ASTM D638)[2][3][30]
Young's modulusMPa5210 (printed XY, ISO 527) — more than double unfilled ABS[1]3311 ± 135 printed XY dry and 3132 ± 124 conditioned, ISO 527 (Polymaker Fiberon); 3DXTech quotes 8000. Stratasys FDM Nylon 12CF spans 7910-15400 printed XZ against 2130-3000 in ZX (ASTM D638)[2][3][30]
Elongation at break%2 at break (printed XY, ISO 527)[1]4.2 ± 0.4 printed XY dry and 5.3 ± 0.3 conditioned, ISO 527 (Polymaker Fiberon); 3DXTech quotes 2.1 at break[2][3]
Flexural strengthMPa76 (printed XY, ISO 178)[1]90 (printed XY, 3DXTech, ISO 178). Stratasys FDM Nylon 12CF spans 152-200 printed XZ against 61-73 in ZX (ASTM D790)[3][30]
Flexural modulusMPa5260 (printed XY, ISO 178)[1]7900 (printed XY, 3DXTech, ISO 178)[3]
Charpy impact, notchedkJ/m²Not documented9.9 ± 0.7 printed XY dry and 10.2 ± 0.8 conditioned, ISO 179 notched (Polymaker Fiberon)[2]
Other impact dataNot documentedIzod notched 102-138 J/m printed XZ against 22.4-45.5 J/m in ZX (Stratasys FDM Nylon 12CF, ASTM D256)[30]
Layer adhesion / Z tensileMPaNot documented52.2 ± 0.8 printed Z dry (Polymaker Fiberon) — 67 % of XY, unusually isotropic for a filled nylon; 42.1 ± 1.8 conditioned. Stratasys FDM Nylon 12CF gives 32.7-38.4 at break printed ZX (ASTM D638)[2][30]
Brittleness1–5Brittle — snaps with little warning; elongation at break 2 %[1]Moderate[2]
Hardness (scale-specific)Shore A / Shore D / RockwellNot documentedRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a carbon-fibre PA12 filament[31]
Creep resistance / sustained load1–5Good — no creep test found; chopped carbon fibre restrains matrix flow and modulus rises to 5210 MPa against 2200–2330 for unfilled ABS[1][25][26]Good. Ensinger rates its PA66-CF30 compound for sustained static and dynamic load at 110 °C continuous service; the PA12 matrix takes up 1.5 % equilibrium moisture against PA6's several per cent, so a PA12-CF part drifts less in service[32][2]
Fatigue / repeated-flex resistance1–5Below average — no S-N curve found; elongation at break falls to 2 % against 10.5 % for unfilled ABS[1][25]Good. Stratasys sells unfilled FDM Nylon 12 specifically for repetitive-flex parts on the strength of its fatigue properties, and Ensinger reports improved fatigue strength for carbon-filled nylon compounds[32]
Elasticity / flexibility1–5Rigid[1]Rigid[2]
Z strength as % of XY%Not documented31-50 (Stratasys FDM Nylon 12CF, ZX against XZ tensile at break, ASTM D638, five machine and tip combinations) against 67 (Polymaker Fiberon PA12-CF10, printed Z against XY)[2][30]
Thermal Properties
HDT at 0.45 MPa°CNot documented131 (ISO 75, 0.45 MPa, Polymaker Fiberon). Stratasys FDM Nylon 12CF gives 160 printed XY and 168 ZX, and 175 with unidirectional toolpaths (ASTM D648 at 66 psi)[2][30]
HDT at 1.8 MPa°CNot documented105 (ISO 75, 1.8 MPa, Polymaker Fiberon). Stratasys FDM Nylon 12CF gives 130 printed XY and 154 ZX (ASTM D648 at 264 psi)[2][30]
Glass transition (Tg)°C105 (DSC)[1]55 (DSC, Polymaker Fiberon)[2]
Melting point / Vicat°CNot documented171 melting (DSC); Vicat 170.2 (ISO 306)[2]
Thermal expansion (CTE)µm/m·K19–25 along the print bead and 80–84 in the build direction at 30 °C (20 wt% CF, large-format printed, TMA)[33]Stratasys FDM Nylon 12CF gives 116 on XY-built and 37 on ZX-built specimens over -50 to 20 °C, rising to 181 (XY) and 46 (ZX) above the 37.5 °C glass transition (ASTM E831); Extrudr quotes 100 for DURAPRO PA12 CF (ISO 11359-2)[14][30]
Flammability / UL 94Not documentedFlammable; no UL 94 rating published for the grades surveyed[28]
Environment & Chemical
UV resistance1–5Not documentedMonths outdoors before embrittlement — unstabilised polyamide yellows under UV[16]
Chemical resistanceGood against weak acids, weak alkalis, oils and grease; dissolved by acetone[34]Withstands oils, fuels and alkalis[16]
Water / humidity resistance in service1–5Not documentedGood — minor absorption; the most humidity-stable nylon composite here[13][2]
Food contactNot food safe — Polymaker cites potential chemical leaching[20]Not food-contact certified as filament[16]
Biodegradability / compostabilityNot biodegradable[20]Not biodegradable[16]
RecyclabilityMechanically recyclable but not accepted in household plastic collection[20]Not accepted in household plastic collection[16]
Electrical & ESD propertiesSurface resistance above 10⁹ ohm/sq — not static-dissipative (ASTM D257)[1]Surface resistivity above 10¹² ohm — insulating (Polymaker Fiberon, ANSI/ESD S11.11)[2]
Health & Safety
Fume toxicity1–5High — hazardous VOC such as styrene; enclosure and filtration needed[35][15]Moderate — measurable VOCs and UFPs, ventilation advised[35]
VOC emission rateµg/min12–113 styrene, the dominant VOC from every ABS and HIPS combination tested[35]Up to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[35]
Ultrafine-particle emission rateparticles/min2 × 10¹⁰ to 9 × 10¹⁰ median across all ABS printers, two orders of magnitude above PLA's ≈1 × 10⁸[35]≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[35]
Hazardous species emittedStyrene dominates. Bambu Lab states ABS and ASA release harmful gases such as styrene at printing temperature, which can be toxic and cause dizziness or nausea[35][15]Caprolactam, at up to 180 µg/min from nylon filament[35]
Ventilation / filtration requirement1–5Enclosure with carbon and HEPA filtration — an enclosure alone cut measured UFP by only about 35 %[35][15]Ventilated room or enclosure recommended[35]
Dust & fibre handling hazardCarbon fibre is bound in the matrix; sanding dust should not be inhaled[1]Fibre is bound in the matrix; sanding dust should not be inhaled[28]
Post-Processing
Sanding & machiningSands well and takes filler before painting[20]Sands poorly — gums rather than powders[18]
Painting & finishingPaints readily after light abrasion[20]Not documented
Gluing & solvent weldingNot documentedCyanoacrylate; no common solvent welds polyamide[18]
Vapour / chemical smoothingAcetone smoothing is blunted by the fibre — only the resin fraction dissolves[34]No practical vapour smoothing[18]
Support material pairingHIPS breaks away or dissolves in d-limonene; Bambu Lab sells a dedicated Support for ABS[36][15]Not documented
Dimensional accuracy & detailNot documentedPolymaker's own conditioning test found PA12-CF10 was the only nylon that did not grow past its original size after moisture conditioning[13]
Solvents & Solubility
Soluble inAcetone dissolves the resin and leaves the fibre as sludge; MEK, THF, ethyl acetate and chlorinated solvents do the same.[37][34]Formic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[38]
Softened or crazed byPetrol and perchloroethylene soften it and benzene attacks it; d-limonene disrupts layer adhesion in some ABS and ASA grades.[37][39]Zinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[38]
Solvent welding & smoothing agentAcetone vapour reaches only the resin fraction, so the fibre is left standing proud of the smoothed surface.[40][34]None — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[38]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. CarbonX Carbon Fiber ABS Technical Data Sheet 3DXTech · 2026-08 · tds
  2. Fiberon PA12-CF10 Technical Data Sheet V1.1 Polymaker · 2025-02 · tds
  3. CarbonX CF PA12 Technical Data Sheet v1 3DXTech · 2026-08 · tds
  4. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  5. Push Plastic product catalogue Push Plastic · 2026-08 · vendor
  6. IEMAI CF-ABS 3D Printing Filament product page IEMAI 3D · 2026-08 · vendor
  7. Siraya Tech Fibreheart ABS-CF Filament product page Siraya Tech · 2026-08 · vendor
  8. YXPOLYER ABS CF product page YXPOLYER · 2026-08 · vendor
  9. Polymaker product catalogue Polymaker · 2026-08 · vendor
  10. IEMAI 3D CF-PA12 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  11. Siraya Tech Fibreheart ABS-CF Core Filament product page Siraya Tech · 2026-08 · vendor
  12. YXPOLYER PA12 CF 500 g — product page YXPOLYER · 2026-08 · vendor
  13. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  14. Extrudr Product Catalogue (DURAPRO PA12 data block) Extrudr · 2025-03 · tds
  15. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  16. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  17. ABS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  18. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  19. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  20. ABS — material basics Polymaker Wiki · 2026-08 · doc
  21. CARBONX ABS+CF — product page (print recommendations) 3DXTech · 2026-08 · doc
  22. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  23. Carbon Fiber Filled — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  24. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  25. Bambu Filament Technical Data Sheet V3.0 — ABS Bambu Lab · 2026-08 · tds
  26. Polymaker ABS Pro Technical Data Sheet V1 (2026-05-29) Polymaker · 2026-05 · tds
  27. Fiberon PA6-GF25 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  28. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  29. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  30. FDM Nylon 12CF — Material Data Sheet Stratasys · 2025-09 · tds
  31. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  32. TECACOMP PA66 CF30 black — injection-moulding compound Ensinger · 2026-08 · tds
  33. Effects of Fiber Orientation on the Coefficient of Thermal Expansion of Fiber-Filled Polymer Systems in Large Format Polymer Extrusion-Based Additive Manufacturing Materials 15(8):2764 · 2022-04 · paper
  34. PolyLite ABS Technical Data Sheet (V5.5 served at this URL) Polymaker · 2024-11 · tds
  35. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  36. HIPS — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  37. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  38. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  39. HIPS — Knowledge Base Prusa Research · 2026-08 · doc
  40. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc