3D Printing Info

Filament comparison

PP-GF vs TPU 85A

Compare printing settings, strength, heat resistance, dated prices and sources.

Glass-fibre PP (PP-GF) guideTPU 85A guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PP-GF comparisonsMore TPU 85A comparisons
PP-GF vs TPU 85A — documented properties and sources
PropertyGlass-fibre PP (PP-GF)POLYOLEFINTPU 85AFLEX
Market snapshot
Listing priceUSD/kg; dated snapshots$49.09/kg median; $46.27–$86.01/kg across 3 dated product listings$89.89/kg median; $31.99–$106.05/kg across 6 dated product listings
Identity & Market
Base polymer / chemistryPolypropylene reinforced with chopped glass fibre[1][2]Soft thermoplastic polyurethane at 82–85 Shore A[3][4][5]
Densityg/cm³1.12 (Prusament PP Glass Fiber, ISO 1183) — the glass lifts it above water[1]1.11 (BASF Ultrafuse 85A) to 1.19 (NinjaFlex 85A), ISO 1183 / ASTM D792[5][3]
Typical priceUSD/kg1 kg-equivalent spools cluster near 49[6][7][8]1 kg-equivalent spools span 32–106; the middle of the market is about 90[9][10][3]
Price range across brandsUSD/kg46-86 across brands; BCN3D PP GF30 46 at 700 g, BASF Ultrafuse PP GF30 49 at 2.2 kg, Prusament PP Glass Fiber 86 at 850 g[6][7][8]32–106 across brands; Siraya Tech Flex TPU 85A 32 at 1 kg, add:north TPU Pro Matte 85A 72, Recreus Filaflex 82A 90 at 500 g, Proto-pasta Clear Flexible TPU 90, 3DXTech 3DXFLEX 85A 96, NinjaTek NinjaFlex 106[11][9][10][12][3]
Market availability1–5Available from several mainstream brands[6][7][8]Available from several mainstream brands[9][11]
Spool sizes & diameters1.75 and 2.85 mm; 700 g, 850 g and 2.2 kg spools[6][7][8]1.75, 2.85 and 3 mm; 0.5, 1 and 2 kg spools[9][11][3]
Typical applicationsStiff, chemically resistant parts where PP-CF's cost or conductivity is unwanted[2]Soft-touch grips, seals, wearables and anything that must compress and rebound[3][4]
Diameter tolerance± mm±0.04 (Prusament)[1]Not documented
Printing Parameters
Nozzle temperature°C245 ± 10 (Prusament) — 25 °C below the carbon-fibre grade[1][13]200–220 (BASF Ultrafuse 85A, 210 typical)[5]
Bed temperature°C95 ± 10 (Prusament)[1]40 (BASF Ultrafuse 85A)[5]
Enclosure / chamber requirement1–5Enclosure recommended — Simplify3D lists an enclosure as a hardware requirement and Polymaker advises one below 70 °C ambient to stop warping and cracking[14][15]Open frame is fine[5]
Part cooling fanOff — Prusa runs 0 % except 100 % on bridges[1]Not documented
Bed surface & adhesion aidNot documentedPEI sheet or painter's tape; Polymaker warns TPU can over-stick and advises a glue stick as a release agent[16][17]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s4 at Prusa's 50 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[1][18]1.2–3.2 at the 15–40 mm/s BASF specifies on a 0.4 mm nozzle at 0.2 mm layer[5]
Warping tendency1–5High — enclosure needed for reliable large parts; Prusa recommends a brim[1]None[5]
Bed-adhesion difficulty1–5Very difficult — special plates or slurry required[1]Sticks to anything — Recreus states its 82A grade has excellent bed adhesion without a heated bed or additives[4]
Stringing / oozing tendency1–5Not documentedHigh — drying plus tuning needed[19][17]
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning; hardened nozzle mandatory[1]Advanced — enclosure, hardware upgrades, tuning; at this hardness the filament will not push through a Bowden tube[3][4]
Extruder requirementPrusa states a hardened nozzle is necessary and recommends a brim[1]Direct drive only. NinjaTek calls its 85A grade ideal for direct-drive extruders and Recreus specifies direct-drive printers for 82A; BASF caps print speed at 15–40 mm/s with a nozzle of 0.4 mm or larger[3][4][5]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required[1]Brass fine indefinitely[20]
Abrasiveness1–5Highly abrasive — standard GF composite[1]Non-abrasive[20]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; Prusa lists higher risk of nozzle clogging for glass-filled composites[21]High — jams from moisture, heat creep or particles[19][17]
Heat-creep / jam sensitivity1–5Not documentedVery high — softens in the cold zone readily; soft filament buckles between the drive gear and the melt zone[17][3]
Hotend requirementNot documentedNo special hot-end required, but a direct-drive extruder is (Simplify3D)[16]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Low (0.1–0.3 %) — 0.11 % at both 24 h and 7 days, higher than the carbon-fibre grade's 0.04 % but still very low[1][13]Moderate — NinjaTek measures 0.22 % in 24 h (ASTM D570) and BASF specifies a 70 °C dry for at least 5 h[3][5]
Equilibrium moisture content at ~50 % RH%0.11 after 24 h and 0.11 after 7 days at 24 °C / 22 % RH (Prusa Polymers)[1]0.22 after 24 h water immersion (NinjaFlex 85A, ASTM D570) — an immersion figure, not an equilibrium moisture content at 50 % RH[3]
Drying temperature & timeNot documented70 °C for at least 5 h in a hot-air dryer or vacuum oven (BASF)[5]
Symptoms when wetNot documentedBubbling and popping at the nozzle, stringing and a rough surface[19]
Effect of moisture on strengthNot applicable in practice at 0.11 % equilibrium uptake[1]Polymaker groups TPU with the highly hygroscopic materials; wet TPU prints with poor layer adhesion and weak, brittle layers[19]
Storage requirementNo special storage needed[1]Sealed with desiccant; often kept in a dryer during the print[19]
Mechanical Properties
Tensile strength (XY)MPa46.6 ± 1.3 filament tensile yield (Prusament, ISO 527) — more than double the carbon-fibre grade's 21[1][13]26 ultimate (NinjaFlex 85A, ASTM D638)[3]
Young's modulusMPaNot documented12 (NinjaFlex 85A, ASTM D638) — two orders of magnitude below any rigid filament; NinjaTek's 95A Cheetah reaches 26 by the same method[3][22]
Elongation at break%Not documented650 at break (Filaflex 82A) and 660 (NinjaFlex 85A); BASF measures 600 in XY and 320 in ZX[4][3][5]
Charpy impact, notchedkJ/m²7.9 ± 0.4 printed horizontal and 9.9 ± 0.8 printed vertical XZ (ISO 179-1, notched)[1]Not documented
Brittleness1–5Moderate[1]Very ductile — bends far before failing[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell R102 (and M95) on extruded unfilled PP stock (ASTM D785); no figure is published for a glass-fibre PP filament[23]29 Shore D / 85 Shore A (BASF Ultrafuse 85A, ISO 7619-1); 85 Shore A (NinjaFlex, ASTM D2240); 82 A nominal for Filaflex[3][5][4]
Creep resistance / sustained load1–5Not documentedPoor — no 85A creep test; a printed 95A TPU bar crept from 74.5 to 82.7 mm over 5 days at 1.25 kg, and softer grades creep more[24]
Fatigue / repeated-flex resistance1–5Not documentedExcellent — living hinges viable[17]
Elasticity / flexibility1–5Rigid[1]Rubbery / highly elastic[3][4]
Z strength as % of XY%Not documented53 — BASF measures 320 % elongation at break in ZX against 600 % in XY[5]
Wear resistance & frictionNot documentedAbrasion 0.08 g mass loss over 10 000 cycles (NinjaFlex, ASTM D4060); 82 mm³ (BASF, ISO 4649)[3][5]
Thermal Properties
HDT at 0.45 MPa°C138.3 (ISO 75, 0.45 MPa)[1]Not documented
HDT at 1.8 MPa°C112.6 (ISO 75, 1.8 MPa)[1]Not documented
Melting point / Vicat°CNot documented216 melting (NinjaFlex 85A, DSC)[3]
Environment & Chemical
UV resistance1–5Not documentedGood — years with some colour shift; Polymaker lists UV exposure among the conditions TPU withstands[17]
Chemical resistanceExcellent against acids, alkalis and most solvents[15]Withstands industrial solvents and UV exposure (Polymaker)[17]
Water / humidity resistance in service1–5Excellent — essentially unaffected[1]Not documented
Food contactNot documentedNot food safe without specific certification (Polymaker)[17]
Biodegradability / compostabilityNot documentedNot biodegradable[17]
RecyclabilityNot documentedNot accepted in household plastic collection[17]
Health & Safety
Fume toxicity1–5Low hazard — minimal VOC and particle emission. Inferred: no polyolefin was among the nine filaments in the Azimi chamber study, so this is a family-level judgement rather than a measurement[25]Low hazard — minimal VOC and particle emission; TPU was not among the nine filaments in the chamber study[25]
Ventilation / filtration requirement1–5Open a window / occasional ventilation. Inferred — no polyolefin was measured in the chamber study[25]Open a window / occasional ventilation[25]
Dust & fibre handling hazardGlass fibre is bound in the matrix; avoid inhaling sanding dust[1]Not documented
Post-Processing
Sanding & machiningNot documentedDifficult to sand or smooth; Polymaker limits post-processing to trimming or tumbling[17]
Gluing & solvent weldingNot documentedCyanoacrylate bonds TPU; no common solvent welds it[17]
Vapour / chemical smoothingNot documentedNo practical vapour smoothing[17]
Support material pairingNot documentedPolymaker warns TPU supports are often very difficult to remove[17]
Solvents & Solubility
Soluble inNone at room temperature; chloroform dissolves the matrix at 60 °C and xylene at about 118 °C, leaving the fibre.[26][27]DMF, DMSO, NMP and THF dissolve TPU; acetone, MEK and cyclohexanone are partial solvents. All laboratory reagents.[28]
Softened or crazed byXylene, decalin, CCl4 and chlorobenzene are heavily absorbed at 20 °C; oleum, chlorosulphonic acid and bromine destroy it.[26]Toluene and benzene swell it up to +50 % by weight at 23 °C; esters swell it severely; ethanol and IPA soften it.[28]
Solvent welding & smoothing agentNone — nothing softens PP at room temperature, so joints have to be welded thermally rather than chemically.[26]None practical — the true solvents (DMF, THF, NMP) are laboratory reagents and leave the joint swollen and weak.[28]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Prusament PP Glass Fiber Technical Datasheet v1.0 Prusa Polymers · 2024-11 · tds
  2. Prusament PP Glass Fiber — material page Prusa Polymers · 2026-08 · doc
  3. NinjaFlex 85A Technical Specifications NinjaTek · 2026-08 · tds
  4. Filaflex 82A product page (Shore hardness and elongation) Recreus · 2026-08 · vendor
  5. Ultrafuse TPU 85A Technical Data Sheet (Version 3.0) BASF Forward AM · 2022-08 · tds
  6. BASF Ultrafuse PP GF30 Black 2.85 mm 2.200 g igo3d · 2026-08 · vendor
  7. BCN3D PP GF30 Black 2.85 mm 700 g igo3d · 2026-08 · vendor
  8. Prusa Prusament PP Glass Fiber Natural (NFC), 1.75 mm / 850 g 3DJAKE · 2026-08 · vendor
  9. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  10. Siraya Tech Flex TPU 85A Filament — product page Siraya Tech · 2026-08 · vendor
  11. Proto-pasta product catalogue Proto-pasta · 2026-08 · vendor
  12. add:north TPU Pro Matte 85A product page add:north · 2026-08 · vendor
  13. Prusament PP Carbon Fiber Technical Datasheet v1.0 Prusa Polymers · 2024-11 · tds
  14. Polypropylene — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  15. PP — material basics Polymaker Wiki · 2026-08 · doc
  16. Flexible (TPE/TPU) — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  17. TPU — material basics Polymaker Wiki · 2026-08 · doc
  18. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  19. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  20. Extrudr Product Catalogue (DURAPRO PA12 data block) Extrudr · 2025-03 · tds
  21. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  22. NinjaTek technical specs comparison chart (Cheetah, NinjaFlex, Armadillo, Alloy 910, Nylon 645) NinjaTek · 2026-08 · tds
  23. TECAFINE PP natural — stock shape properties Ensinger · 2026-08 · tds
  24. BambuLab TPU 95A HF vs Qidi TPU 95A HF — results spreadsheet My Tech Fun (Igor Gaspar) · 2024-02 · test
  25. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  26. Pro-fax and Moplen polypropylene — Chemical Resistance Guide (20, 60 and 100 °C) LyondellBasell · 2026-08 · tds
  27. US 5,278,282 Polymer recycling by selective dissolution — xylene dissolution temperatures Nauman & Lynch, Rensselaer Polytechnic Institute · 1994-01 · paper
  28. Elastollan — Chemical properties: swelling and chemical resistance BASF · 2026-08 · tds