3D Printing Info

Filament comparison

PEEK vs PP-GF

Compare printing settings, strength, heat resistance, dated prices and sources.

PEEK guideGlass-fibre PP (PP-GF) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PEEK comparisonsMore PP-GF comparisons
PEEK vs PP-GF — documented properties and sources
PropertyPEEKHIGHTEMPGlass-fibre PP (PP-GF)POLYOLEFIN
Market snapshot
Listing priceUSD/kg; dated snapshots$531.87/kg median; $296.14–$770.00/kg across 5 dated product listings$49.09/kg median; $46.27–$86.01/kg across 3 dated product listings
Identity & Market
Base polymer / chemistryPolyether ether ketone — a semi-crystalline polyaryletherketone[1]Polypropylene reinforced with chopped glass fibre[2][3]
Densityg/cm³1.30 (ISO 1183)[1][4]1.12 (Prusament PP Glass Fiber, ISO 1183) — the glass lifts it above water[2]
Typical priceUSD/kg1 kg-equivalent spools span 296–770; the middle of the market is about 532[5][6][7]1 kg-equivalent spools cluster near 49[8][9][10]
Price range across brandsUSD/kg296-770 across brands and spool sizes; 3D4Makers recycled R-PEEK 296 at 750 g, IEMAI 3D 420 at 1 kg, LEHVOSS Luvocom 3F PEEK 9581 532 at 2 kg, 3DXTech ThermaX PEEK 770 at 500 g[5][6][7]46-86 across brands; BCN3D PP GF30 46 at 700 g, BASF Ultrafuse PP GF30 49 at 2.2 kg, Prusament PP Glass Fiber 86 at 850 g[8][9][10]
Market availability1–5Niche, a handful of specialist brands[5][6][4]Available from several mainstream brands[8][9][10]
Spool sizes & diameters1.75 and 2.85 mm; 200 g to 2 kg spools[5][6][4]1.75 and 2.85 mm; 700 g, 850 g and 2.2 kg spools[8][9][10]
Typical applicationsAerospace brackets, semiconductor handling, sterilisable medical tooling and downhole parts[1]Stiff, chemically resistant parts where PP-CF's cost or conductivity is unwanted[3]
Diameter tolerance± mmNot documented±0.04 (Prusament)[2]
Printing Parameters
Nozzle temperature°C380-400 (3DXTech printed-specimen conditions); Victrex quotes a 340-450 melt range for AM 450 FIL[1][4]245 ± 10 (Prusament) — 25 °C below the carbon-fibre grade[2][11]
Bed temperature°C130–140 (3DXTech)[1]95 ± 10 (Prusament)[2]
Enclosure / chamber requirement1–5Actively heated chamber required[12][13]Enclosure recommended — Simplify3D lists an enclosure as a hardware requirement and Polymaker advises one below 70 °C ambient to stop warping and cracking[14][15]
Recommended chamber temperature°CNot less than 150 for semi-crystalline printing (Victrex AM 450 FIL); bed above 150[4]Not documented
Part cooling fanNot documentedOff — Prusa runs 0 % except 100 % on bridges[2]
Maximum volumetric flow (mm³/s; see test conditions)mm³/sNot documented4 at Prusa's 50 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[2][16]
Warping tendency1–5Severe — heated chamber needed[12]High — enclosure needed for reliable large parts; Prusa recommends a brim[2]
Bed-adhesion difficulty1–5Very difficult — special plates or slurry required[12]Very difficult — special plates or slurry required[2]
Overall printing difficulty1–5Expert / industrial hardware only[12][13]Advanced — enclosure, hardware upgrades, tuning; hardened nozzle mandatory[2]
Extruder requirementAn all-metal hot end rated above 400 °C and a heated chamber; 3DXTech tests at 0.25 mm layer height on a 0.4 mm nozzle[1][12]Prusa states a hardened nozzle is necessary and recommends a brim[2]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely for unfilled grades, but brass softens near these nozzle temperatures — hardened or plated hot ends are the norm[12]Hardened steel required[2]
Abrasiveness1–5Non-abrasive when unfilled[1]Highly abrasive — standard GF composite[2]
Nozzle clog risk1–5Moderate — needs dry filament and a clean nozzle; 3DXTech lists no special nozzle concerns but a mandatory 120 °C pre-dry before every print[17]Moderate — needs dry filament and a clean nozzle; Prusa lists higher risk of nozzle clogging for glass-filled composites[18]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Not documentedLow (0.1–0.3 %) — 0.11 % at both 24 h and 7 days, higher than the carbon-fibre grade's 0.04 % but still very low[2][11]
Equilibrium moisture content at ~50 % RH%0.45 at saturation, 23 °C (ISO 62); 0.55 at 100 °C[4]0.11 after 24 h and 0.11 after 7 days at 24 °C / 22 % RH (Prusa Polymers)[2]
Drying temperature & time120 °C for 5 h, target below 0.020 % moisture (Victrex AM 450 FIL)[4]Not documented
Effect of moisture on strengthNo dry-versus-conditioned figures are published; 3DXTech mandates a 120 °C, 4 h pre-dry before every print because trapped water flashes to steam at these nozzle temperatures[17]Not applicable in practice at 0.11 % equilibrium uptake[2]
Storage requirementNot documentedNo special storage needed[2]
Mechanical Properties
Tensile strength (XY)MPa60-100 (printed XY): Victrex AM 450 FIL 60-80 at yield and 3DXTech 100, both ISO 527; 98 at yield injection-moulded[1][4]46.6 ± 1.3 filament tensile yield (Prusament, ISO 527) — more than double the carbon-fibre grade's 21[2][11]
Young's modulusMPa3000-4000 (printed XY, ISO 527, Victrex AM 450 FIL); 3720 (3DXTech); 4000 injection-moulded[1][4]Not documented
Elongation at break%28 (printed XY, ISO 527) — remarkably ductile for a high-temperature polymer[1]Not documented
Flexural strengthMPa130 (printed XY, ISO 178)[1]Not documented
Flexural modulusMPa2700 (printed XY, ISO 178)[1]Not documented
Charpy impact, notchedkJ/m²6.0 (injection-moulded, ISO 179/1eA); unnotched does not break[4]7.9 ± 0.4 printed horizontal and 9.9 ± 0.8 printed vertical XZ (ISO 179-1, notched)[2]
Other impact dataIzod notched 7.0 kJ/m2 injection-moulded (ISO 180/A). Printed anisotropy is extreme: VICTREX AM 200 on a Stratasys F900 gives Izod notched 1380-1530 J/m XZ against 30-62 J/m ZX (ASTM D256)[4][19]Not documented
Layer adhesion / Z tensileMPa20-85 at yield (printed ZX, ISO 527, Victrex AM 450 FIL); the spread is set by chamber temperature and weld quality[4]Not documented
Brittleness1–5Tough — absorbs impact, yields before breaking[1]Moderate[2]
Hardness (scale-specific)Shore A / Shore D / RockwellShore D 84.5 (injection-moulded, ISO 868); Rockwell M100 / R125 on extruded PEEK stock (ASTM D785)[4][20]Rockwell R102 (and M95) on extruded unfilled PP stock (ASTM D785); no figure is published for a glass-fibre PP filament[21]
Creep resistance / sustained load1–5Excellent — holds load for years. Victrex rates PEEK for long-term creep; injection-moulded flexural stress at 3.5 % strain falls only from 125 MPa at 23 °C to 85 MPa at 125 °C, and extruded stock is rated to 249 °C continuous[22][4][20]Not documented
Fatigue / repeated-flex resistance1–5Excellent — living hinges viable. Victrex rates PEEK for long-term fatigue as well as creep[22]Not documented
Elasticity / flexibility1–5Rigid[1]Rigid[2]
Z strength as % of XY%71-84 (VICTREX AM 200 LMPAEK printed on the Stratasys F900 and Fortus 450mc, ZX against XZ tensile yield, ASTM D638); unfilled PEEK's own ZX spread is wider[19]Not documented
Thermal Properties
HDT at 0.45 MPa°C140 (printed XY, ISO 75 at 0.45 MPa, 3DXTech)[1]138.3 (ISO 75, 0.45 MPa)[2]
HDT at 1.8 MPa°C152 (unannealed, ISO 75-2/Af, Victrex AM 450 FIL); 160 on extruded stock (ASTM D648 at 264 psi)[4][20]112.6 (ISO 75, 1.8 MPa)[2]
Glass transition (Tg)°C143 (DSC, 3DXTech); Victrex gives onset 143 and midpoint 150 (ISO 11357-2)[1][4]Not documented
Melting point / Vicat°C343 melting (ISO 11357-3, Victrex); VICTREX AM 200 LMPAEK melts at 303[4][19]Not documented
Continuous service temperature°C240 UL 746B relative thermal index, strength (RTI electrical 260, impact 180); Ensinger rates extruded PEEK stock at 249 long term[4][20]Not documented
Thermal expansion (CTE)µm/m·K37.8 (extruded PEEK stock, 23-60 °C, ASTM E831; source states 2.1e-5 in/in/°F), rising to 41.9 at 60-100 °C and 55.8 at 100-150 °C[20]Not documented
Flammability / UL 94UL 94 V-0 at 1.5 mm on the base resin; glow-wire flammability index 960 °C at 2.0 mm (IEC 60695-2-12)[1][4]Not documented
Environment & Chemical
Chemical resistanceOutstanding — resistant to almost all solvents and to steam sterilisation[1]Excellent against acids, alkalis and most solvents[15]
Water / humidity resistance in service1–5Excellent — essentially unaffected; 0.45 % water at saturation and resistant to steam sterilisation[4][1]Excellent — essentially unaffected[2]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised. None of these polymers was in the chamber study, and all are processed far above the temperatures it covered[23]Low hazard — minimal VOC and particle emission. Inferred: no polyolefin was among the nine filaments in the Azimi chamber study, so this is a family-level judgement rather than a measurement[23]
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[23]Open a window / occasional ventilation. Inferred — no polyolefin was measured in the chamber study[23]
Dust & fibre handling hazardNot documentedGlass fibre is bound in the matrix; avoid inhaling sanding dust[2]
Solvents & Solubility
Soluble in95–98 wt% sulphuric acid dissolves it — 10 g per 100 mL at 40–70 °C gives a dark red solution. Laboratory route only.[24][25]None at room temperature; chloroform dissolves the matrix at 60 °C and xylene at about 118 °C, leaving the fibre.[26][27]
Softened or crazed byConcentrated nitric, hydrofluoric, hydrobromic and hydriodic acids attack it; DCM, DMSO and THF swell thin-walled sections.[28][25]Xylene, decalin, CCl4 and chlorobenzene are heavily absorbed at 20 °C; oleum, chlorosulphonic acid and bromine destroy it.[26]
Solvent welding & smoothing agentNone — no solvent softens PEEK, so parts are joined thermally or mechanically, never chemically.[28][25]None — nothing softens PP at room temperature, so joints have to be welded thermally rather than chemically.[26]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. ThermaX PEEK Technical Data Sheet v3 3DXTech · 2026-08 · tds
  2. Prusament PP Glass Fiber Technical Datasheet v1.0 Prusa Polymers · 2024-11 · tds
  3. Prusament PP Glass Fiber — material page Prusa Polymers · 2026-08 · doc
  4. VICTREX AM 450 FIL — datasheet Victrex · 2025-12 · tds
  5. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  6. 3D4Makers product catalogue 3D4Makers · 2026-08 · vendor
  7. IEMAI 3D PEEK 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  8. BASF Ultrafuse PP GF30 Black 2.85 mm 2.200 g igo3d · 2026-08 · vendor
  9. BCN3D PP GF30 Black 2.85 mm 700 g igo3d · 2026-08 · vendor
  10. Prusa Prusament PP Glass Fiber Natural (NFC), 1.75 mm / 850 g 3DJAKE · 2026-08 · vendor
  11. Prusament PP Carbon Fiber Technical Datasheet v1.0 Prusa Polymers · 2024-11 · tds
  12. Prusament PEI 1010 Technical Datasheet v1.0 Prusa Polymers · 2024-09 · tds
  13. Prusament PEI 1010 — material page Prusa Polymers · 2026-08 · doc
  14. Polypropylene — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  15. PP — material basics Polymaker Wiki · 2026-08 · doc
  16. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  17. ThermaX PEEK — product page 3DXTech · 2026-08 · vendor
  18. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  19. VICTREX AM 200 — FDM Material Data Sheet Stratasys · 2024-04 · tds
  20. TECAPEEK natural (PEEK) — stock shape properties Ensinger · 2026-08 · tds
  21. TECAFINE PP natural — stock shape properties Ensinger · 2026-08 · tds
  22. PEEK polymers — product overview Victrex · 2026-08 · doc
  23. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  24. The Effects of Sulfonated Poly(ether ether ketone) Ion Exchange Preparation Conditions on Membrane Properties Yee, Zhang & Ladewig, Membranes 3(3) 182–195 · 2013-07 · paper
  25. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  26. Pro-fax and Moplen polypropylene — Chemical Resistance Guide (20, 60 and 100 °C) LyondellBasell · 2026-08 · tds
  27. US 5,278,282 Polymer recycling by selective dissolution — xylene dissolution temperatures Nauman & Lynch, Rensselaer Polytechnic Institute · 1994-01 · paper
  28. What solvents are not compatible with PEEK? — fluidics technical FAQ IDEX Health & Science · 2026-08 · doc