Filament comparison

PA6-CF vs Breakaway

Compare printing settings, strength, heat resistance, dated prices and sources.

Carbon-fibre PA6 (PA6-CF) guideBreak-away support guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA6-CF comparisonsMore Breakaway comparisons
PA6-CF vs Breakaway — documented properties and sources
PropertyCarbon-fibre PA6 (PA6-CF)PABreak-away supportSUPPORT
Market snapshot
Listing priceUSD/kg; dated snapshots$62.48/kg median; $39.00–$133.32/kg across 6 dated product listings$42.49/kg median; $26.00–$79.98/kg across 4 dated product listings
Identity & Market
Base polymer / chemistryPA6 reinforced with chopped carbon fibre — Polymaker's grade is 20 wt%[1][2]Break-away support compounds matched to a specific model material — Polymaker sells separate grades for PLA and for PA12[3][4]
Densityg/cm³1.09 (Bambu Lab), 1.17 (Polymaker Fiberon and 3DXTech), ISO 1183[2][1][5]1.22 (PolySupport for PLA) and 1.29 (PolySupport for PA12), ISO 1183[3][4]
Typical priceUSD/kg1 kg-equivalent spools span 39–133; the middle of the market is about 80[2][6][7][8]1 kg-equivalent spools span 26–80; the middle of the market is about 45[6][9][10]
Price range across brandsUSD/kg39–133 across brands; IEMAI 3D 39, Bambu Lab 43, YXPOLYER 45, Polymaker Fiberon 80, 3DXTech CarbonX 83, Obsidian 133[2][6][11][12][7][8]26–80 across brands and grades; IEMAI 3D E-REMOVE 26, Polymaker PolySupport for PLA 40 at 750 g, YXPOLYER 45, PolySupport for PA12 80 at 500 g[6][9][10]
Market availability1–5Stocked by most mainstream brands[2][6][12][11][7][8]Available from several mainstream brands[6][12]
Spool sizes & diameters1.75 and 2.85 mm; 0.5, 0.75, 1 and 2 kg spools[6][12][2]1.75 and 2.85 mm; 0.5 and 0.75 kg spools[6]
Typical applicationsLoad-bearing brackets, tooling and drone frames that must hold strength above 150 °C[2][1]Support that peels off by hand, avoiding the moisture handling and dissolution time that soluble supports demand[3]
Printing Parameters
Nozzle temperature°C260–290 (Bambu Lab); 280–300 (Polymaker Fiberon)[2][1]220–230 (PolySupport for PLA)[3]
Bed temperature°C40–50 (Polymaker Fiberon)[1]25–60 (PolySupport for PLA)[3]
Enclosure / chamber requirement1–5Enclosure required (passive) — Bambu Lab specifies a 45–60 °C chamber, Polymaker room temperature[2][1]Open frame is fine[3]
Recommended chamber temperature°C45–60 (Bambu Lab); room temperature (Polymaker Fiberon)[2][1]Not documented
Bed surface & adhesion aidEngineering or high-temperature plate with glue (Bambu Lab)[2]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s8 at Bambu Lab's 100 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer; Polymaker rates its grade to 300 mm/s[2][1][13]4–12 at Polymaker's 50–150 mm/s on a 0.4 mm nozzle at 0.2 mm layer[3]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[2]Not documented
Stringing / oozing tendency1–5Moderate — retraction tuning needed[14]Not documented
Overall printing difficulty1–5Expert / industrial hardware only — enclosure, hardened nozzle, an 80 °C dry and a printer that can hold the filament dry throughout[2][1][15]Easy — minor profile tuning[3]
Extruder requirement0.6 mm nozzle recommended by Bambu Lab; 0.4 and 0.8 also supported[2]A second extruder or a tool changer[3]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA6-CF20 and recommends hardened steel or ruby[1]Brass fine indefinitely[3]
Abrasiveness1–5Highly abrasive — standard CF composite; Polymaker puts brass nozzle life at roughly 9 h[1]Non-abrasive[3]
Nozzle clog risk1–5Very high — frequent jams without careful setup; the combination of moisture and fibre is the worst case in the dataset[15][1]Moderate — needs dry filament and a clean nozzle; Polymaker specifies a 55 °C dry for the PLA grade and warns brass nozzle life falls to about 9 h on the PA12 grade[3][4]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[16]Not documented
Hotend requirementHardened steel or ruby nozzle plus an all-metal hot end rated to 300 °C[1][2]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Very high (>2 %) — 2.35 % saturated at 25 °C / 55 % RH (Bambu Lab)[2]Moderate — 0.64 % equilibrium water absorption (PolySupport for PLA)[3]
Equilibrium moisture content at ~50 % RH%2.35 saturated at 25 °C / 55 % RH (Bambu Lab)[2]0.64 equilibrium water absorption (Polymaker PolySupport for PLA)[3]
Drying temperature & time80 °C for 8–12 h (Bambu Lab); 100 °C for 10 h (Polymaker Fiberon)[2][1]Not documented
Symptoms when wetPopping and cracking during extrusion, then hard-to-diagnose defects[17]Not documented
Effect of moisture on strengthPolymaker publishes dry and wet printed blocks for PA6-CF20 itself: at 5.30 % moisture tensile falls 109.3 → 54.7 MPa and modulus 8636 → 2508 MPa, while notched Charpy rises 11.0 → 35.6 kJ/m². Fibre reinforcement reduces but does not remove the effect[1][17]Not a structural material; no dry-versus-conditioned data is published[15]
Storage requirementSealed below 20 % RH with desiccant; often needs to stay in a dryer while printing[15]Not documented
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[1][18]Not documented
Mechanical Properties
Tensile strength (XY)MPa102 ± 7 (Bambu Lab) and 109.3 ± 2.4 (Polymaker Fiberon, dry/annealed) printed XY, ISO 527; the Fiberon grade falls to 54.7 ± 1.1 conditioned to 5.30 % moisture; 3DXTech quotes 63 at break[2][1][5]Not documented
Young's modulusMPa4430 ± 310 (Bambu Lab) and 8636 ± 211 (Polymaker Fiberon, dry/annealed) printed XY, ISO 527; Fiberon falls to 2508 ± 83 conditioned; 3DXTech quotes 3800[2][1][5]Not documented
Elongation at break%5.8 ± 1.6 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 3 at break[2][5]Not documented
Flexural strengthMPa161.0 ± 3.9 printed XY dry, 64.9 ± 4.9 conditioned, ISO 178 (Polymaker Fiberon); 3DXTech quotes 84[1][5]Not documented
Flexural modulusMPa7038 ± 205 printed XY dry and 2286 ± 185 conditioned, ISO 178 (Polymaker Fiberon); 3DXTech quotes 3750[1][5]Not documented
Charpy impact, notchedkJ/m²11.0 ± 0.3 printed XY dry and 35.6 ± 1.2 conditioned, ISO 179 notched (Polymaker Fiberon)[1]Not documented
Other impact dataCharpy unnotched 24.0 ± 1.0 printed XY dry and 73.0 ± 2.0 conditioned, 7.5 ± 2.7 printed Z dry (Polymaker Fiberon); Bambu Lab 40.3 ± 2.5 unnotched, 13.4 ± 1.7 notched[1][2]Not documented
Layer adhesion / Z tensileMPa48 ± 6 (Bambu Lab) and 54.0 ± 5.2 (Polymaker Fiberon, dry) printed Z, ISO 527; Fiberon falls to 25.5 ± 1.2 conditioned[2][1]Not documented
Brittleness1–5Moderate[2][1]Not documented
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a carbon-fibre nylon filament[19]Not documented
Creep resistance / sustained load1–5Good. Ensinger rates its PA66-CF30 injection-moulding compound for exceptional performance under both static and dynamic loading with 110 °C continuous service; in a printed part the fibre restrains the matrix, but conditioning to equilibrium moisture still softens it[20][17]Not documented
Fatigue / repeated-flex resistance1–5Good. Ensinger states its PA66-CF30 compound has improved fatigue strength in tension, flexure and compression against unfilled and glass-filled PA66[20]Not documented
Elasticity / flexibility1–5Rigid[2]Not documented
Z strength as % of XY%47 (Bambu Lab) to 49 (Polymaker Fiberon), printed[2][1]Not documented
Thermal Properties
HDT at 0.45 MPa°C186 (Bambu Lab) and 215 (Polymaker Fiberon), ISO 75 at 0.45 MPa[2][1]43 (ISO 75, 0.45 MPa, PolySupport for PA12). Polymaker's sheet prints a higher figure at the higher load, which is physically inverted; treat both HDT numbers as approximate[4]
HDT at 1.8 MPa°C164 (Bambu Lab) and 173 (Polymaker Fiberon), ISO 75 at 1.8 MPa[2][1]53 (ISO 75, 1.8 MPa, PolySupport for PA12) — printed above the 0.45 MPa figure on Polymaker's own sheet, which cannot be right; treat both as approximate[4]
Glass transition (Tg)°C68 (Bambu Lab) to 74.2 (Polymaker Fiberon), DSC; 3DXTech quotes 70[2][1][5]Not documented
Melting point / Vicat°C223 melting (Bambu Lab, DSC); Vicat 212 (ISO 306)[2]Vicat 171 (PolySupport for PA12, ISO 306)[4]
Continuous service temperature°CBounded by heat deflection of 164–173 °C at 1.8 MPa; no loaded-bar service figure is published[2][1]Not documented
Annealing response100 °C for 16 h (Polymaker Fiberon)[1]Not documented
Thermal expansion (CTE)µm/m·K94 in the XY direction and 180 in Z, measured on XY-built specimens (79 and 148 on XZ/ZX-built specimens), room temperature to 60 °C, ASTM E831. From Stratasys FDM Nylon-CF10, a blended-nylon matrix with 10 wt% carbon fibre — the closest published printed CTE for a carbon-fibre nylon[21]Not documented
Flammability / UL 94Flammable; no UL 94 rating published[1]Not documented
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows and chalks under UV[14]Not documented
Chemical resistanceWithstands oils, fuels and alkalis[14]Not documented
Water / humidity resistance in service1–5Absorbs water, properties shift[17]Not documented
Food contactNot food-contact certified[14]Not documented
Biodegradability / compostabilityNot biodegradable[14]Not documented
RecyclabilityFibre-filled polyamide is not accepted in household plastic collection[14]Not documented
Electrical & ESD propertiesSurface resistance above 10⁹ ohm/sq — not static-dissipative (3DXTech, ASTM D257)[5]Surface resistance above 10^13 ohm/sq (ASTM D257, THERMAX HTS2 and MTS1)[22][23]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[24]Low hazard — minimal VOC and particle emission; none of these materials was in the chamber study[24]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[24]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[24]Not documented
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[24]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[24]Open a window / occasional ventilation[24]
Dust & fibre handling hazardFibre is bound in the matrix; sanding dust should not be inhaled[1]Not documented
Post-Processing
Sanding & machiningSands to a matte finish; the fibre makes it cut more cleanly than unfilled nylon[16]Not documented
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[16]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[16]Not documented
Support material pairingPolyDissolve S1 (Polymaker Fiberon)[1]This is the support material. Polymaker publishes an adhesion matrix per model material, from very good to unusable, because break-away supports only work against the polymer they were matched to[3][4]
Dimensional accuracy & detailConditioned parts grow; Polymaker declines to publish a standard dimensional allowance because it depends on geometry and infill[17]Not documented
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[25]None — break-away support is removed mechanically; 3DXTech lists no water or solvent route for it.[26]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[25]Not documented
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[25]None — there is no solvent to weld or smooth with.[26]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  2. Bambu Filament Technical Data Sheet — PA6-CF Bambu Lab · 2026-08 · tds
  3. PolySupport Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  4. PolySupport for PA12 Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  5. CarbonX Carbon Fiber Nylon (Gen3) Technical Data Sheet v3.0 3DXTech · 2026-08 · tds
  6. Polymaker product catalogue Polymaker · 2026-08 · vendor
  7. YXPOLYER PA6 CF-Black 1 kg — product page YXPOLYER · 2026-08 · vendor
  8. IEMAI 3D CF-PA6 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  9. YXPOLYER Breakaway Support Filament 1 kg Black — product page YXPOLYER · 2026-08 · vendor
  10. IEMAI 3D E-REMOVE breakaway support filament — store page IEMAI 3D · 2026-08 · vendor
  11. Printed Solid product catalogue Printed Solid · 2026-08 · vendor
  12. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  13. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  14. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  15. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  16. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  17. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  18. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  19. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  20. TECACOMP PA66 CF30 black — injection-moulding compound Ensinger · 2026-08 · tds
  21. FDM Nylon-CF10 — Material Data Sheet (blended nylon, 10 wt% carbon fibre) Stratasys · 2026-08 · tds
  22. THERMAX HTS2 Break Away Support Technical Data Sheet v1.0 3DXTech · 2026-08 · tds
  23. THERMAX MTS1 Break Away Support Technical Data Sheet v1.0 3DXTech · 2026-08 · tds
  24. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  25. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  26. THERMAX HTS1 — product page 3DXTech · 2026-08 · vendor