3D Printing Info

Filament comparison

PA6-CF vs PLA-PHA

Compare printing settings, strength, heat resistance, dated prices and sources.

Carbon-fibre PA6 (PA6-CF) guidePLA/PHA blend guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA6-CF comparisonsMore PLA-PHA comparisons
PA6-CF vs PLA-PHA — documented properties and sources
PropertyCarbon-fibre PA6 (PA6-CF)PAPLA/PHA blendPLA
Market snapshot
Listing priceUSD/kg; dated snapshots$62.48/kg median; $39.00–$133.32/kg across 6 dated product listings$76.40/kg median; $76.40–$76.40/kg across 1 dated product listings
Identity & Market
Base polymer / chemistryPA6 reinforced with chopped carbon fibre — Polymaker's grade is 20 wt%[1][2]PLA blended with polyhydroxyalkanoate, a bacterially fermented bio-polyester[3]
Densityg/cm³1.09 (Bambu Lab), 1.17 (Polymaker Fiberon and 3DXTech), ISO 1183[2][1][4]1.2 (ISO 1183)[3]
Typical priceUSD/kg1 kg-equivalent spools span 39–133; the middle of the market is about 80[2][5][6][7]Not documented
Price range across brandsUSD/kg39–133 across brands; IEMAI 3D 39, Bambu Lab 43, YXPOLYER 45, Polymaker Fiberon 80, 3DXTech CarbonX 83, Obsidian 133[2][5][8][9][6][7]Not documented
Market availability1–5Stocked by most mainstream brands[2][5][9][8][6][7]Niche, a handful of specialist brands[3][10]
Spool sizes & diameters1.75 and 2.85 mm; 0.5, 0.75, 1 and 2 kg spools[5][9][2]1.75 and 2.85 mm; 750 g and 2200 g spools[3]
Typical applicationsLoad-bearing brackets, tooling and drone frames that must hold strength above 150 °C[2][1]General-purpose printing where PLA's brittleness is the limiting factor[3]
Printing Parameters
Nozzle temperature°C260–290 (Bambu Lab); 280–300 (Polymaker Fiberon)[2][1]195–220 (colorFabb)[3]
Bed temperature°C40–50 (Polymaker Fiberon)[1]50–60 (colorFabb)[3]
Enclosure / chamber requirement1–5Enclosure required (passive) — Bambu Lab specifies a 45–60 °C chamber, Polymaker room temperature[2][1]Open frame is fine[3]
Recommended chamber temperature°C45–60 (Bambu Lab); room temperature (Polymaker Fiberon)[2][1]Not documented
Part cooling fanNot documented0–100 %; colorFabb states the blend runs on both heated and unheated beds[3][11]
Bed surface & adhesion aidEngineering or high-temperature plate with glue (Bambu Lab)[2]Not documented
Maximum volumetric flow (mm³/s; see test conditions)mm³/s8 at Bambu Lab's 100 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer; Polymaker rates its grade to 300 mm/s[2][1][12]3.2–8 at colorFabb's 40–100 mm/s, on a 0.4 mm nozzle at 0.2 mm layer[11][12]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[2]Not documented
Stringing / oozing tendency1–5Moderate — retraction tuning needed[13]Not documented
Overall printing difficulty1–5Expert / industrial hardware only — enclosure, hardened nozzle, an 80 °C dry and a printer that can hold the filament dry throughout[2][1][14]Beginner — prints on any machine out of the box[3]
Extruder requirement0.6 mm nozzle recommended by Bambu Lab; 0.4 and 0.8 also supported[2]Not documented
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA6-CF20 and recommends hardened steel or ruby[1]Brass fine indefinitely[3]
Abrasiveness1–5Highly abrasive — standard CF composite; Polymaker puts brass nozzle life at roughly 9 h[1]Non-abrasive[3]
Nozzle clog risk1–5Very high — frequent jams without careful setup; the combination of moisture and fibre is the worst case in the dataset[14][1]Very low — unfilled PLA blend; Prusa lists no drybox and no hardened nozzle for PLA[15]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[16]Not documented
Hotend requirementHardened steel or ruby nozzle plus an all-metal hot end rated to 300 °C[1][2]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5Very high (>2 %) — 2.35 % saturated at 25 °C / 55 % RH (Bambu Lab)[2]Moderate — the PLA matrix takes up 0.40–0.51 % saturated; colorFabb publishes no figure for the blend[17][18]
Equilibrium moisture content at ~50 % RH%2.35 saturated at 25 °C / 55 % RH (Bambu Lab)[2]Not documented
Drying temperature & time80 °C for 8–12 h (Bambu Lab); 100 °C for 10 h (Polymaker Fiberon)[2][1]Not documented
Symptoms when wetPopping and cracking during extrusion, then hard-to-diagnose defects[19]Not documented
Effect of moisture on strengthPolymaker publishes dry and wet printed blocks for PA6-CF20 itself: at 5.30 % moisture tensile falls 109.3 → 54.7 MPa and modulus 8636 → 2508 MPa, while notched Charpy rises 11.0 → 35.6 kJ/m². Fibre reinforcement reduces but does not remove the effect[1][19]Polymaker rates PLA low-sensitivity and publishes no dry-versus-conditioned figures for this grade; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[14]
Storage requirementSealed below 20 % RH with desiccant; often needs to stay in a dryer while printing[14]Not documented
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[1][20]Not documented
Mechanical Properties
Tensile strength (XY)MPa102 ± 7 (Bambu Lab) and 109.3 ± 2.4 (Polymaker Fiberon, dry/annealed) printed XY, ISO 527; the Fiberon grade falls to 54.7 ± 1.1 conditioned to 5.30 % moisture; 3DXTech quotes 63 at break[2][1][4]62–64 (ISO 527-1A, colorFabb; two grades quoted)[3]
Young's modulusMPa4430 ± 310 (Bambu Lab) and 8636 ± 211 (Polymaker Fiberon, dry/annealed) printed XY, ISO 527; Fiberon falls to 2508 ± 83 conditioned; 3DXTech quotes 3800[2][1][4]2960–3070 (ISO 527-1A, colorFabb)[3]
Elongation at break%5.8 ± 1.6 printed XY, ISO 527 (Bambu Lab); 3DXTech quotes 3 at break[2][4]4 and 11 (ISO 527-1A, colorFabb; two grades quoted)[3]
Flexural strengthMPa161.0 ± 3.9 printed XY dry, 64.9 ± 4.9 conditioned, ISO 178 (Polymaker Fiberon); 3DXTech quotes 84[1][4]Not documented
Flexural modulusMPa7038 ± 205 printed XY dry and 2286 ± 185 conditioned, ISO 178 (Polymaker Fiberon); 3DXTech quotes 3750[1][4]2500–3300 flexural modulus (ISO 178, colorFabb)[3]
Charpy impact, notchedkJ/m²11.0 ± 0.3 printed XY dry and 35.6 ± 1.2 conditioned, ISO 179 notched (Polymaker Fiberon)[1]2.8–3.7 (ISO 179, notched, colorFabb)[3]
Other impact dataCharpy unnotched 24.0 ± 1.0 printed XY dry and 73.0 ± 2.0 conditioned, 7.5 ± 2.7 printed Z dry (Polymaker Fiberon); Bambu Lab 40.3 ± 2.5 unnotched, 13.4 ± 1.7 notched[1][2]Not documented
Layer adhesion / Z tensileMPa48 ± 6 (Bambu Lab) and 54.0 ± 5.2 (Polymaker Fiberon, dry) printed Z, ISO 527; Fiberon falls to 25.5 ± 1.2 conditioned[2][1]Not documented
Brittleness1–5Moderate[2][1]Moderate — colorFabb positions the blend as tougher and less brittle than its generic PLA grades[3]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a carbon-fibre nylon filament[21]Not documented
Creep resistance / sustained load1–5Good. Ensinger rates its PA66-CF30 injection-moulding compound for exceptional performance under both static and dynamic loading with 110 °C continuous service; in a printed part the fibre restrains the matrix, but conditioning to equilibrium moisture still softens it[22][19]Poor — no PLA/PHA creep test; plain printed PLA sagged from 12 to 16.2–21.8 mm over 5 days at 1.25 kg[23][24][25]
Fatigue / repeated-flex resistance1–5Good. Ensinger states its PA66-CF30 compound has improved fatigue strength in tension, flexure and compression against unfilled and glass-filled PA66[22]Below average — no S-N curve for the blend; colorFabb positions it as tougher and less brittle than its generic PLA, which ran 38 000–49 000 cycles at 30 % of tensile strength[26][3]
Elasticity / flexibility1–5Rigid[2]Rigid[3]
Z strength as % of XY%47 (Bambu Lab) to 49 (Polymaker Fiberon), printed[2][1]Not documented
Thermal Properties
HDT at 0.45 MPa°C186 (Bambu Lab) and 215 (Polymaker Fiberon), ISO 75 at 0.45 MPa[2][1]Not documented
HDT at 1.8 MPa°C164 (Bambu Lab) and 173 (Polymaker Fiberon), ISO 75 at 1.8 MPa[2][1]Not documented
Glass transition (Tg)°C68 (Bambu Lab) to 74.2 (Polymaker Fiberon), DSC; 3DXTech quotes 70[2][1][4]Not documented
Melting point / Vicat°C223 melting (Bambu Lab, DSC); Vicat 212 (ISO 306)[2]Above 155 melting (ISO 3146-C)[3]
Continuous service temperature°CBounded by heat deflection of 164–173 °C at 1.8 MPa; no loaded-bar service figure is published[2][1]Not documented
Annealing response100 °C for 16 h (Polymaker Fiberon)[1]Not documented
Thermal expansion (CTE)µm/m·K94 in the XY direction and 180 in Z, measured on XY-built specimens (79 and 148 on XZ/ZX-built specimens), room temperature to 60 °C, ASTM E831. From Stratasys FDM Nylon-CF10, a blended-nylon matrix with 10 wt% carbon fibre — the closest published printed CTE for a carbon-fibre nylon[27]Not documented
Flammability / UL 94Flammable; no UL 94 rating published[1]Not documented
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows and chalks under UV[13]Degrades within weeks outdoors[28]
Chemical resistanceWithstands oils, fuels and alkalis[13]Not documented
Water / humidity resistance in service1–5Absorbs water, properties shift[19]Not documented
Food contactNot food-contact certified[13]Not documented
Biodegradability / compostabilityNot biodegradable[13]colorFabb states the PHA component is 100 % biodegradable[3]
RecyclabilityFibre-filled polyamide is not accepted in household plastic collection[13]Not documented
Electrical & ESD propertiesSurface resistance above 10⁹ ohm/sq — not static-dissipative (3DXTech, ASTM D257)[4]Not documented
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[29]Low hazard — minimal VOC and particle emission[29]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[29]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[29]Not documented
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[29]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[29]None needed in a normal room[29]
Dust & fibre handling hazardFibre is bound in the matrix; sanding dust should not be inhaled[1]Not documented
Post-Processing
Sanding & machiningSands to a matte finish; the fibre makes it cut more cleanly than unfilled nylon[16]Not documented
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[16]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[16]Not documented
Support material pairingPolyDissolve S1 (Polymaker Fiberon)[1]Not documented
Dimensional accuracy & detailConditioned parts grow; Polymaker declines to publish a standard dimensional allowance because it depends on geometry and infill[19]Not documented
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[30]Chloroform dissolves the PLA phase (10 % w/v, 2–4 h at 23 °C); THF and DMF need 65 °C. Laboratory reagents.[31]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[30]Acetone, ethyl acetate and toluene plasticise it but dissolve <1 % even at 65 °C; submersion in acetone crazes and destroys parts.[31][32]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[30]Chloroform vapour smooths and welds PLA at the cost of tensile strength; acetone does not smooth it at all.[33][32]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  2. Bambu Filament Technical Data Sheet — PA6-CF Bambu Lab · 2026-08 · tds
  3. PLA/PHA technical data sheet colorFabb · 2026-08 · tds
  4. CarbonX Carbon Fiber Nylon (Gen3) Technical Data Sheet v3.0 3DXTech · 2026-08 · tds
  5. Polymaker product catalogue Polymaker · 2026-08 · vendor
  6. YXPOLYER PA6 CF-Black 1 kg — product page YXPOLYER · 2026-08 · vendor
  7. IEMAI 3D CF-PA6 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  8. Printed Solid product catalogue Printed Solid · 2026-08 · vendor
  9. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  10. woodFill technical data sheet colorFabb · 2026-08 · tds
  11. glowFill technical data sheet colorFabb · 2026-08 · tds
  12. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  13. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  14. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  15. Filament Material Guide Prusa Knowledge Base · 2026-08 · doc
  16. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  17. Bambu Filament Technical Data Sheet V3.0 — PLA Basic Bambu Lab · 2026-08 · tds
  18. PolyLite PLA Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  19. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  20. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  21. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  22. TECACOMP PA66 CF30 black — injection-moulding compound Ensinger · 2026-08 · tds
  23. BambuLab PLA Basic vs PLA Tough vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  24. Polymaker PLA Pro vs PLA-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  25. Carbon Fiber PLA vs META-PLA vs PLA+ vs PLA by Sunlu — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  26. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  27. FDM Nylon-CF10 — Material Data Sheet (blended nylon, 10 wt% carbon fibre) Stratasys · 2026-08 · tds
  28. PLA — material guide Prusa Knowledge Base · 2026-08 · doc
  29. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  30. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  31. Solubility Study of Ingeo Biopolymer Grades in Common Organic Solvents (NWPD003) NatureWorks · 2019-10 · tds
  32. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc
  33. Effect of vapour smoothing in trichloromethane on 3D printed PLA — surface, mechanical and chemical structure Pitale, Keche & Chopra, Engineering Research Express 6(4) 045579 · 2024-12 · paper