3D Printing Info

Filament comparison

PA12 vs PETG-ESD

Compare printing settings, strength, heat resistance, dated prices and sources.

PA12 (Nylon 12) guideESD-safe PETG guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA12 comparisonsMore PETG-ESD comparisons
PA12 vs PETG-ESD — documented properties and sources
PropertyPA12 (Nylon 12)PAESD-safe PETGPETG
Market snapshot
Listing priceUSD/kg; dated snapshots$64.33/kg median; $36.00–$170.67/kg across 3 dated product listings$102.99/kg median; $65.98–$140.00/kg across 2 dated product listings
Identity & Market
Base polymer / chemistryPolyamide 12 — the longest-chain common nylon, with the fewest amide groups per unit mass and so the least moisture uptake[1][2]PETG compounded with a conductive filler to bring surface resistivity into the static-dissipative range[3][4]
Densityg/cm³1.01 specific gravity (Stratasys FDM Nylon 12, ASTM D792)[5]1.24 (Fiberon) and 1.28 (3DXTech), ISO 1183[3][4]
Typical priceUSD/kg1 kg-equivalent spools span 36–171; the middle of the market is about 64[6][7]1 kg-equivalent spools span 66–140; the middle of the market is about 103[8][9]
Price range across brandsUSD/kg36–171 across brands; IEMAI 3D 36, Fiberlogy 64 at 3DJake, 3DXTech AmideX Nylon 12 171[6][9][7]66–140 across brands; Fiberon PETG-ESD 66, 3DXSTAT ESD-PETG 140[8][9]
Market availability1–5Available from several mainstream brands[6][9]Niche, a handful of specialist brands[8][9]
Spool sizes & diameters1.75 and 2.85 mm; 750 g and 1 kg spools[9][6]1.75 mm; 0.5, 0.75, 1 and 3 kg spools[8][9]
Typical applicationsDimensionally stable functional parts, ducting and living hinges where PA6 would move too much with humidity[1][10]Electronics fixtures, trays and jigs handled around static-sensitive components[3][4]
Printing Parameters
Nozzle temperature°C260–290 (Extrudr DURAPRO PA12)[11]250–290 (Fiberon)[3]
Bed temperature°C110 (Extrudr DURAPRO PA12)[11]70–80 (Fiberon); 70 (3DXTech)[3][4]
Enclosure / chamber requirement1–5Enclosure required (passive)[1]Open frame is fine — Fiberon specifies room-temperature chamber[3]
Part cooling fanPart cooling fan not required (Simplify3D)[12]Not documented
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[12][1]Textured PEI, satin or powder-coated sheets; on smooth PEI a glue stick acts as a release agent[13][14]
Maximum volumetric flow (mm³/s; see test conditions)mm³/s12 at Extrudr's 150 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[11][15]Fiberon rates the material to 500 mm/s, equivalent to 40 on a 0.4 mm nozzle at 0.2 mm layer — a machine-limited headline rather than a measured melt rate[3][15]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[12][1]Needs the right surface or a thin adhesive — the problem is releasing the part, not sticking it[13][14]
Stringing / oozing tendency1–5Moderate — retraction tuning needed[1]Moderate — retraction tuning needed; Polymaker names stringing as PETG's common quirk[14]
Overall printing difficulty1–5Advanced — enclosure, hardware upgrades, tuning[1]Intermediate — dry filament and a tuned profile; resistivity depends on getting the nozzle temperature right[3]
Hardware Wear & Reliability
Nozzle hardness required1–4Brass fine indefinitely for unfilled grades[1]Hardened steel required[3]
Abrasiveness1–5Non-abrasive when unfilled[1]Moderately abrasive — conductive carbon filler[3]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles[10][16]Low — 3DXTech lists no special nozzle concerns and no minimum layer height for its ESD-PETG, only a 65 °C pre-dry[17]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[12]Slightly sensitive[18]
Hotend requirementMay require an all-metal hot end (Simplify3D)[12]No special hot-end required[18]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5High (0.8–2 %) — Polymaker's PA12-CF10 reaches 1.5 % equilibrium against 3.33 % for its PA6-GF25, and Polymaker developed the PA12 grade specifically for lower moisture sensitivity[2][10]Moderate (0.3–0.8 %) — the PETG matrix reaches 0.40 % saturated at 25 °C / 55 % RH and 3DXTech specifies a 65 °C, 4 h pre-dry[13][17]
Equilibrium moisture content at ~50 % RH%Not documented0.41 equilibrium water absorption (Fiberon PETG-ESD)[3]
Drying temperature & time60–80 °C for 8–12 h (Extrudr DURAPRO PA12); 100 °C for 8 h (Polymaker CoPA)[11][19]65 °C for 3 h (Fiberon)[3]
Symptoms when wetPopping and cracking during extrusion, then hard-to-diagnose defects[10]Bubbling and popping at the nozzle, stringing and a rough surface[16]
Effect of moisture on strengthPolymaker states its PA12 grade changes little between wet and dry, unlike its PA6-based materials; the CoPA dry-to-wet reference shows what the PA6-type response looks like[10][19]Polymaker groups PETG with nylon, PVA and TPU as highly hygroscopic; no dry-versus-conditioned strength figures are published for this grade and the loss shows as bubbling and poor layer adhesion[16]
Storage requirementSealed below 20 % RH with desiccant[16]Sealed with desiccant; Polymaker groups PETG with the highly hygroscopic materials[16][14]
Hydrolysis at melt temperaturePolymaker requires a 100 °C dry for 8 h and storage below 20 % RH; no molecular-weight loss figure is published, and the published wet data is conditioning rather than melt hydrolysis[19][20]Not documented
Mechanical Properties
Tensile strength (XY)MPa49.3 at yield and 33.4 at break printed XZ (Stratasys FDM Nylon 12, ASTM D638)[5]36.1 ± 0.9 printed XY, ISO 527 (Fiberon); 3DXTech quotes 50 at break[3][4]
Young's modulusMPa1510 printed XZ and 1250 ZX (Stratasys FDM Nylon 12, ASTM D638)[5]1983 ± 75 printed XY, ISO 527 (Fiberon)[3]
Elongation at break%30 at break printed XZ against 6.5 in ZX (Stratasys FDM Nylon 12, ASTM D638)[5]7.3 ± 0.7 printed XY, ISO 527 (Fiberon); 3DXTech quotes 13 at break[3][4]
Flexural strengthMPaNot documented54.0 ± 2.5 printed XY, ISO 178 (Fiberon)[3]
Flexural modulusMPaNot documented1651 ± 141 printed XY, ISO 178 (Fiberon)[3]
Charpy impact, notchedkJ/m²11 at +23 °C and 6.0 at -30 °C (Extrudr DuraPro PA12, ISO 179/1eA); unnotched does not break[11]5.7 ± 0.5 printed XY, ISO 179, notched (Fiberon)[3]
Other impact dataIzod notched 138 J/m printed XZ against 71.0 J/m in ZX (Stratasys FDM Nylon 12, ASTM D256)[5]Charpy unnotched 29.3 ± 2.2 printed XY (Fiberon, ISO 179)[3]
Layer adhesion / Z tensileMPa41.8 at yield and 41.2 at break printed ZX (Stratasys FDM Nylon 12, ASTM D638) — higher than the XZ break figure, because XZ specimens draw and neck first[5]20.7 ± 0.6 printed Z, ISO 527 (Fiberon)[3]
Brittleness1–5Tough — absorbs impact, yields before breaking[1]Moderate[3]
Creep resistance / sustained load1–5Moderate — the long-chain polyamides hold load better than PLA but below PC[1]Below average — no ESD-grade creep test; unfilled PETG sagged from 12 to 17.1–20.4 mm over 5 days at 1.25 kg[21][22][23][24]
Fatigue / repeated-flex resistance1–5Excellent — living hinges viable. Stratasys sells FDM Nylon 12 specifically for repetitive-flex parts such as snap-fit clips and press-fit inserts on the strength of its fatigue properties[1][5]Moderate — no ESD-grade S-N curve; unfilled printed PETG ran 79 000–193 000 cycles at 30 % of tensile strength[25]
Elasticity / flexibility1–5Semi-flexible[10]Slightly flexible in thin sections[3]
Z strength as % of XY%85 (Stratasys FDM Nylon 12, ZX against XZ tensile yield, ASTM D638) — one of the least anisotropic unfilled filaments measured[5]57 (Fiberon, printed Z against XY tensile)[3]
Thermal Properties
HDT at 0.45 MPa°C94.7 printed XY and 91.9 in XZ/ZX (Stratasys FDM Nylon 12, ASTM D648 at 66 psi)[5]76 (ISO 75, 0.45 MPa, Fiberon)[3]
HDT at 1.8 MPa°C84.3 printed XY and 75.3 in XZ/ZX (Stratasys FDM Nylon 12, ASTM D648 at 264 psi)[5]72 (ISO 75, 1.8 MPa, Fiberon)[3]
Glass transition (Tg)°C34.0 (Stratasys FDM Nylon 12, ASTM D7426 inflection point)[5]77 (Fiberon) and 80 (3DXTech), DSC[3][4]
Melting point / Vicat°CVicat A 142 (Extrudr DURAPRO PA12, ISO 306)[11]Amorphous — no melting point; Vicat 86 (Fiberon, ISO 306)[3]
Continuous service temperature°CBounded by a Vicat softening point of 142 °C (Extrudr DURAPRO PA12); no loaded-bar service figure is published[11]Not documented
Thermal expansion (CTE)µm/m·K84-103 printed (Stratasys FDM Nylon 12, ASTM E831: 84.4 in XY and 85.6 in XZ/ZX over -50 to 10 °C, 89.1 over 10-45 °C, 98.2 over 45-70 °C); Extrudr quotes 100 for DURAPRO PA12 (ISO 11359-2)[11][5]Not documented
Flammability / UL 94Flammable; no UL 94 rating published for the unfilled grades surveyed[11]Flammable; no UL 94 rating published for standard grades[26]
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement[1]Not documented
Chemical resistanceWithstands oils, fuels and alkalis[1]Withstands acids, alkalis, oils and UV exposure[14]
Water / humidity resistance in service1–5Good — minor absorption; the least moisture-sensitive of the common nylons[10]Not documented
Food contactNot food-contact certified as filament[1]Not certified for food contact as filament[14]
Biodegradability / compostabilityNot biodegradable[1]Not biodegradable[14]
RecyclabilityMechanically recyclable but not accepted in household plastic collection[1]Not accepted in household plastic collection[14]
Electrical & ESD propertiesNot documentedSurface resistivity falls with nozzle temperature: 7.0×10⁶–1.6×10⁷ ohm at 250 °C, 3.2×10⁵–4.7×10⁵ at 270 °C and below 1×10⁴ at 290 °C (Fiberon); 3DXTech quotes 10⁷–10⁹ ohm/sq[3][4]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[27]Moderate — measurable VOCs and UFPs, ventilation advised[27]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon; total VOC reached nearly 200 µg/min, the highest of the nine filaments tested[27]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median — low for ultrafine particles despite the highest VOC mass of any filament tested[27]Not documented
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament — the largest single-VOC emission rate measured in the study[27]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[27]Open a window / occasional ventilation[27]
Dust & fibre handling hazardNot documentedConductive carbon filler is bound in the matrix; avoid inhaling sanding dust[3]
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[12]Sands poorly — the material is tough and gums rather than powders[18]
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[12]Cyanoacrylate; no common solvent welds PETG cleanly[18]
Vapour / chemical smoothingNo practical vapour smoothing[12]No practical vapour smoothing[18]
Support material pairingPolymaker sells a break-away PolySupport matched to PA12[12]Prints its own supports; Polymaker rates PolyDissolve S1 for PETG[18]
Dimensional accuracy & detailHolds dimensions better than PA6 after conditioning — Polymaker singles its PA12 grade out on exactly this point[10]Nozzle temperature has to be held steady — it moves surface resistivity by three orders of magnitude[3]
Solvents & Solubility
Soluble inDissolved at 23 °C by formic acid, phenol, m-cresol, 96 % sulphuric acid or hexafluoroisopropanol — all laboratory reagents.[28][29]No common workshop solvent; 1,2-dichloroethane destroys it inside a week and dichloromethane — a carcinogen — dissolves the surface.[30][31]
Softened or crazed byNot resistant to 10 % formic acid, phenol, chloroform or dichloromethane (Ensinger); zinc chloride stress-cracks nylon.[29][28]Acetone (+16 % weight over 1 year at 23 °C), ethyl acetate, toluene and DMF swell and soften it; methanol crazes it.[30]
Solvent welding & smoothing agentNone — nylon's only solvents are formic acid, phenol and HFIP, all of which degrade the part they wet.[28]Dichloromethane brushed on is the only agent that smooths PETG — a controlled carcinogen, not workshop stock.[31]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  2. Fiberon PA612-CF15 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  3. Fiberon PETG-ESD Technical Data Sheet V1.1 Polymaker · 2026-08 · tds
  4. 3DXSTAT ESD-PETG Technical Data Sheet 3DXTech · 2026-08 · tds
  5. FDM Nylon 12 — Material Data Sheet Stratasys · 2021-09 · tds
  6. Nylon PA12 — product listing 3DJake International · 2026-08 · vendor
  7. IEMAI 3D PA12 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  8. Polymaker product catalogue Polymaker · 2026-08 · vendor
  9. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  10. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  11. Extrudr Product Catalogue (DURAPRO PA12 data block) Extrudr · 2025-03 · tds
  12. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  13. Prusament PETG Technical Datasheet v1.1 Prusa Polymers · 2022-02 · tds
  14. PETG — material basics Polymaker Wiki · 2026-08 · doc
  15. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  16. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  17. 3DXSTAT ESD-PETG — product page (print recommendations) 3DXTech · 2026-08 · doc
  18. PET and PETG — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  19. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  20. PolyMide CoPA — Technical Data Sheet page Polymaker Wiki · 2026-08 · tds
  21. PCTG vs PETG comparison — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  22. Extrudr PETG vs PCTG vs XPETG-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  23. Prusament PETG-CF vs PETG V0 vs PETG — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  24. BambuLab PETG Basic vs Translucent vs PETG-CF — results spreadsheet My Tech Fun (Igor Gaspar) · 2026-08 · test
  25. Mechanical Properties of Additively Manufactured Polymeric Materials — PLA and PETG — For Biomechanical Applications Polymers 16(13):1868 · 2024-06 · paper
  26. Prusament PETG V0 Technical Datasheet Prusa Polymers · 2026-08 · tds
  27. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  28. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  29. Chemical resistance — resistance of Ensinger plastics to chemicals (DIN 50 014, 23/50) Ensinger · 2026-08 · tds
  30. Eastman Spectar copolyester — Chemical resistance (unstressed bars, 1 year at 23 °C) Eastman Chemical Company · 2026-08 · tds
  31. Improve your 3D prints with chemical smoothing Prusa Research · 2026-08 · doc