3D Printing Info

Filament comparison

PA-CF ESD vs PC-GF

Compare printing settings, strength, heat resistance, dated prices and sources.

ESD-safe CF nylon guideGlass-fibre PC (PC-GF) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA-CF ESD comparisonsMore PC-GF comparisons
PA-CF ESD vs PC-GF — documented properties and sources
PropertyESD-safe CF nylonPAGlass-fibre PC (PC-GF)PC
Market snapshot
Listing priceUSD/kg; dated snapshots$129.98/kg median; $129.98–$129.98/kg across 1 dated product listings$71.27/kg median; $71.27–$71.27/kg across 1 dated product listings
Identity & Market
Base polymer / chemistryCarbon-filled polyamide compounded to a static-dissipative resistivity — Polymaker's grade uses a PA612 matrix[1]Polycarbonate reinforced with 30 wt% short glass fibre[2]
Densityg/cm³1.10 (ISO 1183)[1]1.17 (measured on a 100 % infill printed part, ISO 1183-A)[2]
Typical priceUSD/kg1 kg-equivalent spools cluster near 130[3]1 kg spools cluster near 71[4]
Price range across brandsUSD/kg130 at Polymaker's 0.5 kg pricing[3]71 — BASF Ultrafuse PC GF30 at igo3d is the only priced listing found; Owens Corning sells XSTRAND GF30-PC in 500 g and 1 kg[4][2]
Market availability1–5Special order, 1–2 makers worldwide[3]Niche, a handful of specialist brands — neither Polymaker's nor 3DXTech's polycarbonate range contains a glass-fibre grade, but BASF Forward AM and Owens Corning both sell one through European retail[4][2][3][5]
Spool sizes & diameters1.75 mm; 0.5 kg spools[3]1.75 and 2.85 mm at +/- 0.05 mm; 500 g and 1 kg net spools[2]
Typical applicationsElectronics jigs and trays that also need nylon toughness and heat resistance[1]Functional prototyping for mechanical engineering, electronics and automotive[2]
Diameter tolerance± mmNot documented+/- 0.05 (Owens Corning XSTRAND)[2]
Printing Parameters
Nozzle temperature°CNot documented280-330 (Owens Corning XSTRAND GF30-PC)[2]
Bed temperature°CNot documented80-110 (Owens Corning XSTRAND GF30-PC)[2]
Enclosure / chamber requirement1–5Enclosure required (passive)[6]Enclosure required (passive) — as for unfilled PC[7][8]
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[9][6]Perforated plate, DimaFix or Magigoo PC glue (Owens Corning)[2]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[9]Not documented
Stringing / oozing tendency1–5Moderate — retraction tuning needed[6]Not documented
Overall printing difficulty1–5Expert / industrial hardware only[6][10]Not documented
Extruder requirementNot documentedOwens Corning specifies a nozzle above 0.4 mm and hardened steel nozzles and drive wheels[2]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA612-ESD and recommends hardened steel or ruby[1]Hardened steel required — Owens Corning states glass reinforcement shortens brass nozzle and drive-wheel life[2]
Abrasiveness1–5Highly abrasive — carbon-filled nylon composite; Polymaker puts brass nozzle life at roughly 9 h on PA612-ESD[1]Highly abrasive — 30 wt% glass fibre[2]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles[10]High — jams from moisture, heat creep or particles; PC already absorbs water from the air and Prusa lists glass-filled composites as a higher clogging risk[11][12]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[9]Not documented
Hotend requirementMay require an all-metal hot end (Simplify3D)[9]Not documented
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5High (0.8–2 %) — the PA612 matrix sits between PA6 and PA12[13][14]Negligible (<0.1 % EMC) — Owens Corning measures below 0.1 % at 23 °C and 50 % RH (ISO 62)[2]
Equilibrium moisture content at ~50 % RH%Not documentedBelow 0.1 at 23 °C and 50 % RH, and below 0.1 at saturation (ISO 62)[2]
Effect of moisture on strengthPolymaker publishes dry and wet printed blocks for PA612-ESD itself: at 4.64 % moisture tensile falls 84.3 → 73.6 MPa and modulus 4294 → 3731 MPa[1][14]No dry-versus-conditioned figures are published. Polymaker calls PC highly hygroscopic; absorbed water flashes to steam and shows as bubbling and poor layer adhesion[15][10]
Storage requirementSealed below 20 % RH with desiccant[10]Not documented
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[16][17]Not documented
Mechanical Properties
Tensile strength (XY)MPa84.3 ± 2.3 printed XY dry (annealed 100 °C/16 h), 73.6 ± 2.3 conditioned to 4.64 % moisture, ISO 527[1]65 at break (printed, ISO 527 at 1 mm/min)[2]
Young's modulusMPa4293.7 ± 116.4 printed XY dry and 3730.8 ± 156.2 conditioned, ISO 527[1]5400 (printed, ISO 527 at 1 mm/min)[2]
Elongation at break%3.0 ± 0.1 printed XY dry and 4.2 ± 0.4 conditioned, ISO 527[1]2.5 at break (printed, ISO 527 at 1 mm/min)[2]
Flexural strengthMPaNot documented113 at yield (printed, ISO 178 at 2 mm/min)[2]
Flexural modulusMPaNot documented5500 (printed, ISO 178 at 2 mm/min)[2]
Charpy impact, notchedkJ/m²5.9 ± 0.4 printed XY dry and 4.9 ± 0.3 conditioned, ISO 179 notched[1]Not documented
Other impact dataCharpy unnotched 24.1 ± 2.4 printed XY and 4.5 ± 0.2 printed Z (ISO 179)[1]Not documented
Layer adhesion / Z tensileMPa21.5 ± 2.7 printed Z dry — only a quarter of XY, the most anisotropic nylon composite here; 19.2 ± 1.6 conditioned[1]Not documented
Brittleness1–5Brittle — snaps with little warning; elongation 3.0 % in XY and 1.4 % in Z[1]Brittle — snaps with little warning; 2.5 % elongation at break[2]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a conductive carbon-filled nylon filament[18]Rockwell 70 (118) — the source does not name the scales and Shore D 79 on extruded unfilled PC stock (ASTM D785, D2240); no figure is published for a glass-fibre grade[19]
Creep resistance / sustained load1–5Good. Ensinger rates its PA66-CF30 compound for sustained static and dynamic load at 110 °C continuous service; the PA612 matrix here still takes up 4.64 % moisture at conditioning, which softens it[20][1]Excellent — holds load for years. Room-temperature tensile creep of moulded unfilled PC ran unbroken at 41 MPa until the test was stopped, and 30 wt% glass raises the tensile modulus from about 2.3 to 5.4 GPa[21][2]
Fatigue / repeated-flex resistance1–5Good. Ensinger states carbon-filled PA66 compounds have improved fatigue strength in tension, flexure and compression[20]Not documented
Elasticity / flexibility1–5Rigid[1]Rigid[2]
Z strength as % of XY%26 (printed Z against XY tensile)[1]Not documented
Thermal Properties
HDT at 0.45 MPa°C157.0 (ISO 75, 0.45 MPa)[1]Not documented
HDT at 1.8 MPa°C125.4 (ISO 75, 1.8 MPa)[1]137 (printed, ISO 75 Method A at 1.8 MPa)[2]
Glass transition (Tg)°C41.8 (DSC)[1]145 (DSC, ISO 11357)[2]
Melting point / Vicat°C187.3 melting (DSC); Vicat 190.0 (ISO 306)[1]270 stated as melting point (ISO 11357) — unusual for an amorphous polymer, but this is the published figure[2]
Thermal expansion (CTE)µm/m·KNot documented26.2 in XY and 77.4 in Z (printed, ISO 11359-2) — a threefold anisotropy, and the lowest in-plane expansion of any polycarbonate here[2]
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[16]UL 94 V-0 verified (Owens Corning)[2]
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows under UV[6]Good — years with some colour shift. Owens Corning lists UV resistance as a product benefit but publishes no exposure data[2]
Chemical resistanceWithstands oils, fuels and alkalis[6]Not documented
Water / humidity resistance in service1–5Not documentedExcellent — essentially unaffected; below 0.1 % water at saturation (ISO 62)[2]
Food contactNot food-contact certified as filament[6]Not documented
Biodegradability / compostabilityNot biodegradable[6]Not documented
RecyclabilityNot accepted in household plastic collection[6]Not documented
Electrical & ESD propertiesStatic-dissipative — the reason the grade exists; Polymaker's insulating nylon composites sit above 10¹² ohm by contrast[1][13]Electrically insulating (Owens Corning)[2]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[22]Moderate — measurable VOCs and UFPs, ventilation advised[22]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[22]Not documented
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[22]≈4 × 10¹⁰ median — the highest ultrafine-particle rate of the nine filaments in the chamber study, above every ABS tested[22]
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[22]Not documented
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[22]Ventilated room or enclosure recommended[22][8]
Dust & fibre handling hazardFibre is bound in the matrix; sanding dust should not be inhaled[16]Owens Corning warns that the glass reinforcement is abrasive when melted and advises sufficient ventilation and avoiding extrusion fumes[2]
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[9]Not documented
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[9]Not documented
Vapour / chemical smoothingNo practical vapour smoothing[9]Not documented
Dimensional accuracy & detailNot documentedHigh dimensional stability is the headline benefit; the 26.2 um/m*K in-plane CTE is a third of unfilled PC's[2]
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[23]Dichloromethane and chloroform dissolve the matrix and leave the fibre; DMF and dioxane do the same (Covestro).[24]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[23]Methanol, butyl acetate, ether, 1 % NaOH and phthalate plasticisers stress-crack it; acetone, MEK and xylene swell it.[24]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[23]Dichloromethane cement welds the resin, but the fibre keeps the joint from flowing closed. Controlled carcinogen.[25]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Fiberon PA612-ESD Technical Data Sheet V1.0 Polymaker · 2025-06 · tds
  2. XSTRAND GF30-PC Data Sheet Owens Corning · 2019-04 · tds
  3. Polymaker product catalogue Polymaker · 2026-08 · vendor
  4. BASF Ultrafuse PC GF30 Black 2.85 mm 1.000 g igo3d · 2026-08 · vendor
  5. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  6. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  7. PolyLite PC Technical Data Sheet V5.4 Polymaker · 2024-11 · tds
  8. ABS / ASA / PC Usage Guide Bambu Lab Wiki · 2026-08 · doc
  9. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  10. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  11. Composite materials filled with carbon, kevlar or glass Prusa Knowledge Base · 2026-08 · doc
  12. Polycarbonate — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  13. Fiberon PA612-CF15 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  14. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  15. PC — material basics Polymaker Wiki · 2026-08 · doc
  16. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  17. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  18. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  19. TECANAT natural (PC) — stock shape properties Ensinger · 2026-08 · tds
  20. TECACOMP PA66 CF30 black — injection-moulding compound Ensinger · 2026-08 · tds
  21. Experimental data for creep and dynamic mechanical properties of polycarbonate and polycarbonate/ABS Data in Brief 42:108264 · 2022-06 · paper
  22. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  23. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds
  24. Makrolon — The chemical resistance (Makrolon 2800, 6 days at 23 °C and 50 °C) Covestro · 2016-12 · tds
  25. Weld-On 3 Acrylic Plastic Cement — technical data sheet (shipped as dichloromethane) IPS Corporation · 2002-07 · tds