PA-CF ESD vs PA12-CF

Compare printing settings, strength, heat resistance, dated prices and sources.

ESD-safe CF nylon guideCarbon-fibre PA12 (PA12-CF) guide

2 selected · all documented properties

Open these two in the interactive comparisonMore PA-CF ESD comparisonsMore PA12-CF comparisons
PA-CF ESD vs PA12-CF — documented properties and sources
PropertyESD-safe CF nylonPACarbon-fibre PA12 (PA12-CF)PA
Market snapshot
Listing priceUSD/kg; dated snapshots$129.98/kg median; $129.98–$129.98/kg across 1 dated product listings$109.98/kg median; $52.00–$180.00/kg across 4 dated product listings
Identity & Market
Base polymer / chemistryCarbon-filled polyamide compounded to a static-dissipative resistivity — Polymaker's grade uses a PA612 matrix[1]PA12 reinforced with chopped carbon fibre — Polymaker's grade is 10 wt%[2][3]
Densityg/cm³1.10 (ISO 1183)[1]1.06 (Polymaker Fiberon) and 1.16 (3DXTech), ISO 1183[2][3]
Typical priceUSD/kg1 kg-equivalent spools cluster near 130[4]1 kg-equivalent spools span 52–180; the middle of the market is about 110[4][5][6]
Price range across brandsUSD/kg130 at Polymaker's 0.5 kg pricing[4]52–180 across brands; IEMAI 3D 52, YXPOLYER 80 at 500 g, Polymaker Fiberon 140, 3DXTech CarbonX 180[4][5][7][6]
Market availability1–5Special order, 1–2 makers worldwide[4]Available from several mainstream brands[4][5]
Spool sizes & diameters1.75 mm; 0.5 kg spools[4]1.75 mm; 0.5, 0.75 and 2 kg spools[4][5]
Typical applicationsElectronics jigs and trays that also need nylon toughness and heat resistance[1]Stiff parts that must stay dimensionally stable in changing humidity — Polymaker sells this grade specifically on low moisture sensitivity[8][2]
Printing Parameters
Nozzle temperature°CNot documented260–290 (Extrudr DURAPRO PA12 CF)[9]
Bed temperature°CNot documented110 (Extrudr DURAPRO PA12 CF)[9]
Enclosure / chamber requirement1–5Enclosure required (passive)[10]Enclosure required (passive)[10][2]
Bed surface & adhesion aidPEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[11][10]PEI sheet with a glue stick, or a dedicated adhesive such as Magigoo[11][10]
Maximum volumetric flow (mm³/s; see test conditions)mm³/sNot documented12 at Extrudr's 150 mm/s cap on a 0.4 mm nozzle at 0.2 mm layer[9][12]
Bed-adhesion difficulty1–5Needs a specific surface plus adhesive[11]Needs a specific surface plus adhesive[11]
Stringing / oozing tendency1–5Moderate — retraction tuning needed[10]Moderate — retraction tuning needed[10]
Overall printing difficulty1–5Expert / industrial hardware only[10][13]Advanced — enclosure, hardware upgrades, tuning[10]
Hardware Wear & Reliability
Nozzle hardness required1–4Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA612-ESD and recommends hardened steel or ruby[1]Hardened steel required — Polymaker measures brass nozzle life at about 9 h on PA12-CF10 and recommends hardened steel or ruby[2]
Abrasiveness1–5Highly abrasive — carbon-filled nylon composite; Polymaker puts brass nozzle life at roughly 9 h on PA612-ESD[1]Highly abrasive — standard CF composite; Polymaker puts brass nozzle life at roughly 9 h on PA12-CF10[2]
Nozzle clog risk1–5High — jams from moisture, heat creep or particles[13]High — jams from moisture, heat creep or particles[13]
Heat-creep / jam sensitivity1–5Moderate — good heatbreak cooling needed[11]Moderate — good heatbreak cooling needed[11]
Hotend requirementMay require an all-metal hot end (Simplify3D)[11]May require an all-metal hot end (Simplify3D)[11]
Moisture Behaviour
Moisture absorption (hygroscopicity)1–5High (0.8–2 %) — the PA612 matrix sits between PA6 and PA12[14][8]High (0.8–2 %) — 1.5 % equilibrium, the lowest of Polymaker's nylon composites and less than half its PA6-GF25[2][15]
Equilibrium moisture content at ~50 % RH%Not documented1.5 equilibrium water absorption (Polymaker Fiberon PA12-CF10)[2]
Drying temperature & timeNot documented80–100 °C; storage below 20 % RH[13][2]
Effect of moisture on strengthPolymaker publishes dry and wet printed blocks for PA612-ESD itself: at 4.64 % moisture tensile falls 84.3 → 73.6 MPa and modulus 4294 → 3731 MPa[1][8]Polymaker's own dry/wet blocks for PA12-CF10 change little: at 2.92 % moisture tensile falls 77.4 → 71.7 MPa and modulus 3311 → 3132 MPa, against a halving for its PA6 grades[2][8]
Storage requirementSealed below 20 % RH with desiccant[13]Sealed below 20 % RH with desiccant[13]
Hydrolysis at melt temperaturePolymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[16][17]Polymaker specifies an 80–100 °C dry and storage below 20 % RH; no molecular-weight loss figure is published, and the wet data it does publish is conditioning rather than melt hydrolysis[16][17]
Mechanical Properties
Tensile strength (XY)MPa84.3 ± 2.3 printed XY dry (annealed 100 °C/16 h), 73.6 ± 2.3 conditioned to 4.64 % moisture, ISO 527[1]77.4 ± 1.1 printed XY dry (Polymaker Fiberon), 71.7 ± 0.7 conditioned to 2.92 % moisture, ISO 527; 3DXTech quotes 72 at break. Stratasys FDM Nylon 12CF spans 76.5-124 at break printed XZ across five machine and tip combinations (ASTM D638)[2][3][18]
Young's modulusMPa4293.7 ± 116.4 printed XY dry and 3730.8 ± 156.2 conditioned, ISO 527[1]3311 ± 135 printed XY dry and 3132 ± 124 conditioned, ISO 527 (Polymaker Fiberon); 3DXTech quotes 8000. Stratasys FDM Nylon 12CF spans 7910-15400 printed XZ against 2130-3000 in ZX (ASTM D638)[2][3][18]
Elongation at break%3.0 ± 0.1 printed XY dry and 4.2 ± 0.4 conditioned, ISO 527[1]4.2 ± 0.4 printed XY dry and 5.3 ± 0.3 conditioned, ISO 527 (Polymaker Fiberon); 3DXTech quotes 2.1 at break[2][3]
Flexural strengthMPaNot documented90 (printed XY, 3DXTech, ISO 178). Stratasys FDM Nylon 12CF spans 152-200 printed XZ against 61-73 in ZX (ASTM D790)[3][18]
Flexural modulusMPaNot documented7900 (printed XY, 3DXTech, ISO 178)[3]
Charpy impact, notchedkJ/m²5.9 ± 0.4 printed XY dry and 4.9 ± 0.3 conditioned, ISO 179 notched[1]9.9 ± 0.7 printed XY dry and 10.2 ± 0.8 conditioned, ISO 179 notched (Polymaker Fiberon)[2]
Other impact dataCharpy unnotched 24.1 ± 2.4 printed XY and 4.5 ± 0.2 printed Z (ISO 179)[1]Izod notched 102-138 J/m printed XZ against 22.4-45.5 J/m in ZX (Stratasys FDM Nylon 12CF, ASTM D256)[18]
Layer adhesion / Z tensileMPa21.5 ± 2.7 printed Z dry — only a quarter of XY, the most anisotropic nylon composite here; 19.2 ± 1.6 conditioned[1]52.2 ± 0.8 printed Z dry (Polymaker Fiberon) — 67 % of XY, unusually isotropic for a filled nylon; 42.1 ± 1.8 conditioned. Stratasys FDM Nylon 12CF gives 32.7-38.4 at break printed ZX (ASTM D638)[2][18]
Brittleness1–5Brittle — snaps with little warning; elongation 3.0 % in XY and 1.4 % in Z[1]Moderate[2]
Hardness (scale-specific)Shore A / Shore D / RockwellRockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a conductive carbon-filled nylon filament[19]Rockwell M88 / R117 on extruded PA66-GF30 stock (ASTM D785); no figure is published for a carbon-fibre PA12 filament[19]
Creep resistance / sustained load1–5Good. Ensinger rates its PA66-CF30 compound for sustained static and dynamic load at 110 °C continuous service; the PA612 matrix here still takes up 4.64 % moisture at conditioning, which softens it[20][1]Good. Ensinger rates its PA66-CF30 compound for sustained static and dynamic load at 110 °C continuous service; the PA12 matrix takes up 1.5 % equilibrium moisture against PA6's several per cent, so a PA12-CF part drifts less in service[20][2]
Fatigue / repeated-flex resistance1–5Good. Ensinger states carbon-filled PA66 compounds have improved fatigue strength in tension, flexure and compression[20]Good. Stratasys sells unfilled FDM Nylon 12 specifically for repetitive-flex parts on the strength of its fatigue properties, and Ensinger reports improved fatigue strength for carbon-filled nylon compounds[20]
Elasticity / flexibility1–5Rigid[1]Rigid[2]
Z strength as % of XY%26 (printed Z against XY tensile)[1]31-50 (Stratasys FDM Nylon 12CF, ZX against XZ tensile at break, ASTM D638, five machine and tip combinations) against 67 (Polymaker Fiberon PA12-CF10, printed Z against XY)[2][18]
Thermal Properties
HDT at 0.45 MPa°C157.0 (ISO 75, 0.45 MPa)[1]131 (ISO 75, 0.45 MPa, Polymaker Fiberon). Stratasys FDM Nylon 12CF gives 160 printed XY and 168 ZX, and 175 with unidirectional toolpaths (ASTM D648 at 66 psi)[2][18]
HDT at 1.8 MPa°C125.4 (ISO 75, 1.8 MPa)[1]105 (ISO 75, 1.8 MPa, Polymaker Fiberon). Stratasys FDM Nylon 12CF gives 130 printed XY and 154 ZX (ASTM D648 at 264 psi)[2][18]
Glass transition (Tg)°C41.8 (DSC)[1]55 (DSC, Polymaker Fiberon)[2]
Melting point / Vicat°C187.3 melting (DSC); Vicat 190.0 (ISO 306)[1]171 melting (DSC); Vicat 170.2 (ISO 306)[2]
Thermal expansion (CTE)µm/m·KNot documentedStratasys FDM Nylon 12CF gives 116 on XY-built and 37 on ZX-built specimens over -50 to 20 °C, rising to 181 (XY) and 46 (ZX) above the 37.5 °C glass transition (ASTM E831); Extrudr quotes 100 for DURAPRO PA12 CF (ISO 11359-2)[9][18]
Flammability / UL 94Flammable; no UL 94 rating published for the grades surveyed[16]Flammable; no UL 94 rating published for the grades surveyed[16]
Environment & Chemical
UV resistance1–5Months outdoors before embrittlement — unstabilised polyamide yellows under UV[10]Months outdoors before embrittlement — unstabilised polyamide yellows under UV[10]
Chemical resistanceWithstands oils, fuels and alkalis[10]Withstands oils, fuels and alkalis[10]
Water / humidity resistance in service1–5Not documentedGood — minor absorption; the most humidity-stable nylon composite here[8][2]
Food contactNot food-contact certified as filament[10]Not food-contact certified as filament[10]
Biodegradability / compostabilityNot biodegradable[10]Not biodegradable[10]
RecyclabilityNot accepted in household plastic collection[10]Not accepted in household plastic collection[10]
Electrical & ESD propertiesStatic-dissipative — the reason the grade exists; Polymaker's insulating nylon composites sit above 10¹² ohm by contrast[1][14]Surface resistivity above 10¹² ohm — insulating (Polymaker Fiberon, ANSI/ESD S11.11)[2]
Health & Safety
Fume toxicity1–5Moderate — measurable VOCs and UFPs, ventilation advised[21]Moderate — measurable VOCs and UFPs, ventilation advised[21]
VOC emission rateµg/minUp to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[21]Up to 180 caprolactam, the dominant VOC from nylon and the largest single-VOC rate in the study[21]
Ultrafine-particle emission rateparticles/min≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[21]≈2 × 10⁸ median for nylon — low for particles despite the highest VOC mass measured[21]
Hazardous species emittedCaprolactam, at up to 180 µg/min from nylon filament[21]Caprolactam, at up to 180 µg/min from nylon filament[21]
Ventilation / filtration requirement1–5Ventilated room or enclosure recommended[21]Ventilated room or enclosure recommended[21]
Dust & fibre handling hazardFibre is bound in the matrix; sanding dust should not be inhaled[16]Fibre is bound in the matrix; sanding dust should not be inhaled[16]
Post-Processing
Sanding & machiningSands poorly — gums rather than powders[11]Sands poorly — gums rather than powders[11]
Gluing & solvent weldingCyanoacrylate; no common solvent welds polyamide[11]Cyanoacrylate; no common solvent welds polyamide[11]
Vapour / chemical smoothingNo practical vapour smoothing[11]No practical vapour smoothing[11]
Dimensional accuracy & detailNot documentedPolymaker's own conditioning test found PA12-CF10 was the only nylon that did not grow past its original size after moisture conditioning[8]
Solvents & Solubility
Soluble inFormic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[22]Formic acid, phenol, m-cresol and hexafluoroisopropanol dissolve the matrix at 23 °C, leaving the fibre; laboratory reagents.[22]
Softened or crazed byZinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[22]Zinc chloride solutions stress-crack the nylon matrix, alcoholic calcium chloride dissolves it, mineral acids attack it.[22]
Solvent welding & smoothing agentNone — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[22]None — nylon's only solvents (formic acid, phenol, HFIP) degrade the part, and the fibre blocks surface flow anyway.[22]

Material entries describe families or representative grades, not an interchangeable specification for every spool. Test methods, orientations and conditions may differ. Unknown values are marked “Not documented”. Prices and source dates remain historical snapshots; check the linked guide for product details. Differences highlight text, not a universal winner.

Sources for this comparison

  1. Fiberon PA612-ESD Technical Data Sheet V1.0 Polymaker · 2025-06 · tds
  2. Fiberon PA12-CF10 Technical Data Sheet V1.1 Polymaker · 2025-02 · tds
  3. CarbonX CF PA12 Technical Data Sheet v1 3DXTech · 2026-08 · tds
  4. Polymaker product catalogue Polymaker · 2026-08 · vendor
  5. 3DXTech product catalogue 3DXTech · 2026-08 · vendor
  6. IEMAI 3D CF-PA12 3D Printing Filament — store page IEMAI 3D · 2026-08 · vendor
  7. YXPOLYER PA12 CF 500 g — product page YXPOLYER · 2026-08 · vendor
  8. Moisture Conditioning — effect on printed nylon properties Polymaker Wiki · 2026-08 · doc
  9. Extrudr Product Catalogue (DURAPRO PA12 data block) Extrudr · 2025-03 · tds
  10. PA (Nylon) — material basics Polymaker Wiki · 2026-08 · doc
  11. Nylon — Ultimate 3D Printing Materials Guide Simplify3D · 2026-08 · doc
  12. Max volumetric speed Prusa Knowledge Base · 2026-08 · doc
  13. Wet Filament — signs, causes and drying Polymaker Wiki · 2026-08 · doc
  14. Fiberon PA612-CF15 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  15. Fiberon PA6-GF25 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  16. Fiberon PA6-CF20 Technical Data Sheet V1.1 Polymaker · 2024-12 · tds
  17. PolyMide CoPA Technical Data Sheet V5.4 (dry and wet status blocks) Polymaker · 2024-11 · tds
  18. FDM Nylon 12CF — Material Data Sheet Stratasys · 2025-09 · tds
  19. TECAMID 66 GF30 black (PA66-GF30) — stock shape properties Ensinger · 2026-08 · tds
  20. TECACOMP PA66 CF30 black — injection-moulding compound Ensinger · 2026-08 · tds
  21. Emissions of Ultrafine Particles and Volatile Organic Compounds from Commercially Available Desktop Three-Dimensional Printers with Multiple Filaments (Azimi et al.) Environmental Science & Technology 50(3) 1260-1268 · 2016-01 · paper
  22. Ultramid Nylon Chemical Resistance guide (unmodified PA6 B27E and PA66 A27E) BASF · 2026-08 · tds